Effect of the Fabrication Technique on Compressive Properties of Cu-PTFE Composites
Table 2
Average mechanical parameters of Cu-PTFE composites.
| Specimens | Elastic modulus (MPa) | Yield strength (MPa) | Hardening modulus (MPa) | Ultimate strength (MPa) | Failure strain |
| A1 | 161 | 10.5 | 18.8 | 26.3 | 2.79 | A2 | 157 | 10.9 | 20.4 | 28.9 | 2.60 | A3 | 169 | 10.2 | 21.1 | 31.1 | 2.74 | A4 | 163 | 11.6 | 26.7 | 35.2 | 2.18 | B1 | 62 | 11.6 | 19.4 | 23.6 | 2.57 | B2 | 80 | 12.9 | 22.4 | 26.6 | 2.89 | B3 | 76 | 12.6 | 21.4 | 25.3 | 2.79 | B4 | 77 | 13.3 | 21.1 | 24.4 | 2.50 |
|
|