Optical Microstructure, FESEM, Microtensile, and Microhardness Properties of LM 25-B4Cnp-Grnp Hybrid Composites Manufactured by Selective Laser Melting
Table 2
Research studies on LM 25- B4Cnp-Grnp hybrid composites.
| Metal matrix composite | Hardness | Tensile | Composite preparation | Reference |
| AleMgeSi-T6/fly ash/boron carbide | 62 RHN | 180 MPa | Stir casting process | Saravana kumar et al., [12] | AA7075/B4C/ZrC hybrid nanocomposite | 132 HV | 469 MPa | Powder metallurgy techniques | Manohar.G et al., [11] | Al7010/B4C/BN | 170 HV | 227.089 MPa | Ultrasonic assisted stir casting technique | Gopichand dirisenapu et al., [13] | Al6063 alloy composites/B4C | 84 BHN | 143 MPa | Ultrasonic assisted stir-casting process | B. Byra reddy, and T. P. Bharathesh [9] | Al2218 alloy and its nano-B4C composites | 85.66 BHN | 229 MPa | Stir casting process | Vidyadhar pujar et al., [34] | Nanographite and ZrO2-reinforced Al7075 alloy | 75 BHN | 260 Mpa | Stir casting method | Raj kumar et al., [15] | Al12Si + 10%TiN | 156 HV | 347 Mpa | Selective laser melting | Xaiopeng Li et al., (2022) [35] | A356/B4C composite | 77 BHN | 271 Mpa | Electromagnetic stir casting process with vacuum | Shyam lal et al., (2020) [36] | Al6061-SiC-graphite hybrid surface composite | 1.2 Gpa | 82 Gpa | Friction stir processing | Abhishek sharma [16] | Nano- and micro-Gr/aluminium 6061 alloy | 63 HRC | 165 MPa | Two step stir castingtwo step stir casting | Rajkumar and santosh [17] |
|
|