Optical Microstructure, FESEM, Microtensile, and Microhardness Properties of LM 25-B<sub>4</sub>Cnp-Grnp Hybrid Composites Manufactured by Selective Laser Melting

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr class="thead"><td class="align_left" colspan="2">Ultimate strength value (MPa)</td></tr><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td class="align_left">LM 25-5% B<sub>4</sub>Cnp-5% Grnp</td><td class="align_left"><b>668.93</b></td></tr><tr><td class="align_left">LM 25-10% B<sub>4</sub>Cnp-10% Grnp</td><td class="align_left"><b>739.16</b></td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Ultimate strength value (N/mm<sup>2</sup>).</div>

Advances in Materials Science and Engineering

tab3

Table 3

Table 3: Optical Microstructure, FESEM, Microtensile, and Microhardness Properties of LM 25-B<sub>4</sub>Cnp-Grnp Hybrid Composites Manufactured by Selective Laser Melting 

Table 3 | Optical Microstructure, FESEM, Microtensile, and Microhardness Properties of LM 25-B4Cnp-Grnp Hybrid Composites Manufactured by Selective Laser Melting 