Delocalized Photomechanical Effects of UV ns Laser Ablation on Polymer Substrates Captured by Optical Holography Workstation: An Overview on Experimental Result

Figure 5

Defect formation versus number of pulses of 50 : 50 polymer blends at 193 nm with different MW.