Research Letters in Physical Chemistry
Volume 2008, Article ID 342976, 4 pages
http://dx.doi.org/10.1155/2008/342976
Research Letter

Ultrasoft and High Magnetic Moment CoFe Films Directly Electrodeposited from a B-Reducer Contained Solution

Data Storage Institute, A-Star, 5 Engineering Drive 1, National University of Singapore (NUS), Singapore 117608

Received 13 March 2008; Accepted 20 May 2008

Academic Editor: Eli Ruckenstein

Copyright © 2008 Baoyu Zong et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. S. R. Brankovic, X. Yang, T. J. Klemmer, and M. Seigler, “Pulse electrodeposition of 2.4 T Co37Fe63 alloys at nanoscale for magnetic recording application,” IEEE Transactions on Magnetics, vol. 42, no. 2, pp. 132–139, 2006. View at Publisher · View at Google Scholar
  2. P. C. Andricacos and N. Robertson, “Future directions in electroplated materials for thin-film recording heads,” IBM Journal of Research and Development, vol. 42, no. 5, pp. 671–680, 1998. View at Google Scholar
  3. T. Osaka, M. Takai, K. Hayashi, K. Ohashi, M. Saito, and K. Yamada, “A soft magnetic CoNiFe film with high saturation magnetic flux density and low coercivity,” Nature, vol. 392, no. 6678, pp. 796–798, 1998. View at Publisher · View at Google Scholar
  4. Ultra-soft magnetic films for high-frequency inductors (GWN.4561), http://www.stw.nl/Projecten/G/gwn/gwn4561.htm.
  5. S. X. Wang, N. X. Sun, M. Yamaguchi, and S. Yabukami, “Sandwich films: properties of a new soft magnetic material,” Nature, vol. 407, no. 6801, pp. 150–151, 2000. View at Publisher · View at Google Scholar
  6. W. Yu, J. A. Bain, Y. Peng, and D. E. Laughlin, “Magnetization reduction due to oxygen contamination of bias sputtered Fe35Co65 thin films,” IEEE Transactions on Magnetics, vol. 38, no. 5, pp. 3030–3032, 2002. View at Publisher · View at Google Scholar
  7. E. I. Cooper, C. Bonhôte, J. Heidmann et al., “Recent developments in high-moment electroplated materials for recording heads,” IBM Journal of Research and Development, vol. 49, no. 1, pp. 103–126, 2005. View at Google Scholar
  8. B. Zong, Y. Wu, G. Han et al., “Synthesis of iron oxide nanostructures by annealing electrodeposited Fe-based films,” Chemistry of Materials, vol. 17, no. 6, pp. 1515–1520, 2005. View at Publisher · View at Google Scholar
  9. M. Kawasaki and Y. Kanada, “Soft magnetic film having high saturation magnetic flux density, thin-film magnetic head using the same, and manufacturing method of the same,” US patent no. 6765757, August 2002.
  10. G. Herzer, “Soft magnetic nanocrystalline materials,” Scripta Metallurgica et Materialia, vol. 33, no. 10-11, pp. 1741–1756, 1995. View at Publisher · View at Google Scholar
  11. Q. Zeng, I. Baker, V. McCreary, and Z. Yan, “Soft ferromagnetism in nanostructured mechanical alloying FeCo-based powders,” Journal of Magnetism and Magnetic Materials, vol. 318, no. 1-2, pp. 28–38, 2007. View at Publisher · View at Google Scholar
  12. F. Lallemand, L. Ricq, E. Deschaseaux, L. De Vettor, and P. Berçot, “Electrodeposition of cobalt-iron alloys in pulsed current from electrolytes containing organic additives,” Surface & Coatings Technology, vol. 197, no. 1, pp. 10–17, 2005. View at Publisher · View at Google Scholar