Research Article
Interrelationships of Pressure-Dependent Hole Fraction and Elongational Viscosity in Polymer Melts
Table 3
Values of parameters of (
7) evaluated for
at different elongational rates.
| Polymer | (sā1) | | | | | | R2 |
| LDPE60 | 60 90 120 | 7.14 7.08 7.12 | 72.63 72.01 68.95 | 0.142 0.141 0.135 | 0.0031 0.0033 0.0032 | 1.18 1.32 1.33 | 0.99981 0.99975 0.99977 |
| LDPE65 | 30 60 90 107 | 8.05 8.61 8.97 9.10 | 67.69 46.81 31.02 24.13 | 0.134 0.0927 0.0615 0.048 | 0.0012 0.00070 0.00049 0.00043 | 1.23 1.07 0.43 0.55 | 0.99977 0.99986 0.99997 0.99995 |
| LLDPE | 60 90 120 | 9.13 9.01 8.89 | 8.47 7.44 7.06 | 0.0227 0.0199 0.0189 | 0.00042 0.00048 0.00054 | 0.64 0.64 0.60 | 0.99993 0.99993 0.99994 |
| HDPE | 60 90 107 120 148 | 9.26 9.06 8.98 8.92 8.83 | 35.23 35.15 34.86 34.58 33.89 | 0.0575 0.0574 0.0569 0.0564 0.0553 | 0.00043 0.00053 0.00057 0.00060 0.00067 | 0.34 0.25 0.23 0.24 0.31 | 0.99998 0.99999 0.99999 0.99999 0.99999 |
| PMMA | 60 90 120 | 3.33 3.31 3.44 | 452.45 440.95 423.15 | 0.6740 0.6569 0.6304 | 0.2028 0.2066 0.1804 | 0.81 0.91 1.00 | 0.99991 0.99988 0.99985 |
| PC | 60 90 120 | 3.97 3.71 3.53 | 359.15 374.00 384.53 | 3.820 3.98 4.090 | 0.0954 0.1225 0.1466 | 2.44 1.99 1.73 | 0.99906 0.99941 0.99954 |
| PP | 90 107 120 | 7.20 7.14 7.09 | 86.30 84.30 83.91 | 0.0813 0.0794 0.0790 | 0.0029 0.0031 0.0033 | 1.04 0.82 0.73 | 0.99986 0.99991 0.99993 |
| PS | 30 60 90 120 | 3.74 3.71 3.70 3.63 | 313.11 303.36 297.94 296.65 | 0.1990 0.1928 0.1893 0.1886 | 0.1060 0.1091 0.1105 0.1178 | 1.42 1.11 1.25 1.48 | 0.99970 0.99981 0.99977 0.99959 |
|
|