<table class="table-group" width="800px"><tr class="fig-image" id="a"><td><img alt="685648.fig.004a" src="https://static.hindawi.com/articles/at/volume-2009/685648/figures/685648.fig.004a.jpg"/></td></tr><tr class="fig-caption"><td align="center"><table><tr><td><b>(a) </b>8 hours</td></tr></table></td></tr><tr class="fig-image" id="b"><td><img alt="685648.fig.004b" src="https://static.hindawi.com/articles/at/volume-2009/685648/figures/685648.fig.004b.jpg"/></td></tr><tr class="fig-caption"><td align="center"><table><tr><td><b>(b) </b>16 hours</td></tr></table></td></tr></table>

<table>Worn surface morphology after impact-corrosion wear for 8 hours and 16 hours at the impact energy of 1.2 J. </table>