Nanofibrous Chitosan-Polyethylene Oxide Engineered Scaffolds: A Comparative Study between Simulated Structural Characteristics and Cells Viability

Table 1

A summary of electrospinning setup and the corresponding processing parameters for each sample scaffold.

Sample code	Deposition time (h)	Feed rate (mL·h^−1)	Applied voltage (kv)	Distance (cm)
Variation on time
1	1	0.27	8	13
2	2	0.27	8	13
3*	3	0.27	8	13
4	4	0.27	8	13
Variation on feed rate
5	3	0.17	8	13
6	3	0.37	8	13
Variation on voltage
7	3	0.27	10	13
8	3	0.27	13	13
9	3	0.27	15	13
Variation on distance
10	3	0.27	8	10
11	3	0.27	8	15

∗Control sample was electrospun with constant processing parameters; deposition time is 3 h, feed rate is 0.27 mL·h⁻¹, applied voltage is 8 kv, and tip to collector distance is 13 cm.