Abstract

Objective. To evaluate shear bond strength (SBS) values of a methacrylate (FZ 250) and a silorane-based (FS) resin composite to various underlying materials. Materials and Methods. A total of 80 samples were prepared with four different underlying materials; a flowable (FLC) and a bulk-fill flowable composite (BFC), and a conventional (CGIC) and resin modified glass-ionomer cement (RMGIC). These underlying materials were laminated plus to methacrylate or silorane-based resin composites . To evaluate the specimens SBS values were evaluated with a universal testing machine (cross-head speed; 1.0 mm/min). Statistical comparisons were carried out using two-way ANOVA and Tukey’s post hoc test with a significance level of . Results. SBS values for FZ250 were significantly higher than for FS for all of the underlying materials tested . SBS values of FZ250 to BFC were significantly higher than to all other materials , whereas SBS values of FS did not vary significantly according to underlying material . Conclusion. The use of FS in conjunction with any of the tested materials showed lower SBS than the FZ 250. Also, new low elastic modulus liner BFC presented slightly good interfacial adhesion so, the usage of BFC as an underlying material may be preferable for FZ 250.

1. Introduction

Composite resins are the most common tooth-colored restorative materials used for aesthetic purposes [1]. However, their polymerization shrinkage remains a major drawback to their clinical success as dental restorative materials [2, 3]. Numerous clinical strategies have been suggested and technologies developed with the aim of reducing polymerization shrinkage. Clinical approaches have focused on the modification of curing light source and irradiation sequence and incremental placement of resin composite in posterior teeth [46]. Also layering techniques for resin composites that contain the use of low elastic modulus liners under the resin composite [710] such as flowable composites and glass ionomer cements have been found to be of great interest [11]. Technological approaches have focused on amounts and types of matrix monomer and filler, initiator level, and the addition of nonbonding microparticles [12].

Recently, dental composites have been developed based on silorane chemistry [13]. These composites contain oxirane and siloxane molecules that are polymerized through a ring-opening mechanism that results in a lower level of polymerization shrinkage relative to other polymerization mechanisms [14, 15]. In addition, their hydrophobicity of siloxane helps to reduce polymerization shrinkage [16]. However, while the low levels of polymerization shrinkage of silorane-based composite have been noted, other issues have been raised, namely, problems in cavity wall adaptation and curing in deep cavities [17]. These limitations suggest that, in clinical situations, the use of some type of material beneath the silorane composite may be beneficial [14, 18]. In the dental industry’s ongoing search for materials with improved properties, a new generation of flowable composites, known as “bulk-fill flowable composites,” has been introduced to the dental market. These new products have higher filler contents and are said to have better mechanical properties than earlier composites and are thus recommended for large posterior restorations [19]. By promoting light transmittance, bulk-fill flowable composites have been reported to enable a depth of cure in excess of 4 mm, thereby reducing polymerization shrinkage of laminated composite materials [20], simplifying the filling procedure, and saving precious chair time [2123].

Generally posterior composite resin restorations placed without a liner show good longevity [24, 25]. However, in terms of clinical practice, dentists may choose layering techniques that combine positive properties of several restorative materials. For the success of layering technique there should be a reasonable bond between two materials [26]. But there is limited knowledge about the bonding properties of combining different materials, especially with regard to silorane-based resin composites and bulk-fill flowable composites. Therefore, this study aimed to evaluate SBS values of a silorane-based resin composite (Filtek Silorane, FS) and a methacrylate-based resin composite (Filtek Z250, FZ250) to a bulk-flowable composite, a regular flowable composite, a conventional glass ionomer cement, and a resin modified glass ionomer cement. The null hypotheses tested were as follows. (1) The bonding performance of a silorane-based resin composite does not differ from that of a methacrylate-based resin composite. (2) The SBS values of resin composites are not affected by the type of underlying material used.

2. Materials and Methods

2.1. Test Materials

The materials used in the study (including lot numbers and manufacturers’ information) are listed in Table 1. Composite materials included a methacrylate-based composite (FZ250, Filtek Z250) and a silorane-based composite (FS, Filtek Silorane), and underlying materials included a regular flowable composite (FLC, ÆliteFlo), a bulk-fill flowable composite (BFC, SDR flow), a conventional glass ionomer cement (CGIC, Riva self-cure), and a resin modified glass ionomer cement (RMGIC, Fuji II LC).

2.2. Preparation of Specimens

Underlying material specimens were prepared using plastic molds drilled with holes  mm in diameter and  mm in depth. For each underlying material, 20 specimens were prepared, for a total of 80 specimens. During setting, tops and bottoms of the molds were covered with cellulose acetate strips and glass microscope slides, and hand pressure was applied to produce a smooth surface. For the CGIC specimens, the assembly was held in place for 10 min. For the light-cured test materials, the filled molds were cured on both sides and in different positions for a total of 40 seconds using an LED curing unit (Elipar Free Light II, 3M/ESPE, St. Paul, MN, USA; light intensity: 1000 mV/cm2). Following polymerization, specimens were removed from molds, and any excess material was removed by gentle grinding on both sides with 600-grit silicon carbide paper (Phoenix Beta, Buehler, Germany) until flat and equal surfaces were obtained. Debris was removed with a dust blower.

Prior to placement of composites, Clearfil SE bond was used with FZ250, and the Filtek Silorane system adhesive bond was applied with the silorane composite, as recommended by the manufacturer.

Following initial preparations, specimens of each group of underlying material were divided into 2 subgroups according to the composite to be used in lamination. A 2 mm high cylindrical polyethylene tube with an internal diameter of approximately 8 mm was placed on the surface of each underlying specimen, the tube was filled with composite (either FZ250 or FS), and all samples (except the self-cure samples) were polymerized for 20 s using an LED curing unit, with all procedures carried out at room temperature. Light-cured samples were then stored in an incubator at 37°C and 100% humidity for 24 h. The self-cure CGIC specimens were stored at 37°C for 1 h before being immersed in distilled water at 37°C for the next 23 hours [27]. All specimens were then thermocycled between 5°C and 55°C for 500 cycles using a dwell time of 10 s and a transfer time of 30 s between each bath.

2.3. Shear Bond Strength Testing

Specimens were subjected to shear bond strength (SBS) testing by placing them in a universal testing machine (LRX Lloyd Instruments, Ametek Inc., Leicester, UK) and removing the tubes with a sharp blade at a crosshead speed of 1.0 mm/min. Load at debonding was recorded in Newtons, and MPa was calculated by dividing this value by the bonded area (mm2).

Debonded specimens were examined under a stereomicroscope (Nikon SMZ 1500, Tokyo, Japan) at ×25 magnification, and failure modes were classified as either cohesive failure (fracture inside the composite resin or underlying material), adhesive failure (fracture within the bonding interface), or mixed failure (a combination of cohesive and adhesive failures) [28].

2.4. Scanning Electron Microscopy (SEM)

Specimens were gold-sputtered under a high vacuum and examined by SEM at ×25 and ×100 magnification (JEOL, JSM-6400, Tokyo, Japan).

2.5. Statistical Analysis

SBS values were expressed as mean ± standard deviation. Statistical analysis was performed using SPSS for Windows, Version 12.0.1 (SPSS Inc., Chicago, IL, USA). Normal distribution of variables was determined by Levene’s test, and SBS values were analyzed using two-way ANOVA. Multiple comparisons were performed using Tukey’s post hoc test, with a significance level of .

3. Results

SBS values are given in Table 2. SBS values of FZ250 were significantly higher than SBS values of FS for all underlying test materials (). Among FZ250 specimens, the SBS value for BFC was significantly higher than all other underlying materials (), whereas no other significant differences were found (). Among the FS specimens, CGIC had the highest SBS value of all the underlying materials tested; however, none of the differences in SBS values for any of the underlying materials were statistically significant ().

Fracture analysis results are given in Table 2. Mixed and cohesive failures were the most common failure modes for the FZ250 group, whereas adhesive failure was most common for the FS group. SEM views of different groups were shown in Figures 1(a)1(d).

4. Discussion

Although resin composites have shown great improvement, the clinicians still prefer to apply layering techniques that aimed to combine the favorable properties of different materials in a single restoration [11, 29]. Thus, by decreasing the bulk amount, of resin used, this technique can also reduce the detrimental effect of polymerization shrinkage, which may result in microleakage and marginal gap [30]. In addition, it acts as stress absorbing layer between the shrinking composite and dentine [31]. If the quality of interfacial adaptation between two materials could be improved it was assumed that the durability of layered resin restorations may be increased [32].

This study showed that the SBS values of FS to underlying materials were lower than those of FZ250 , with adhesive failure, the most common failure mode for FS. The lower bonding performance of FS could be attributed to its low reactivity and to low surface wettability of the intermediate resin adhesive. The silorane adhesive system is based on methacrylate chemistry (technical information from 3M-ESPE) [33, 34], which allows conventional methacrylate-based composites to bond to dentin, and it utilizes a self-etching primer with a pH of 2.7, which can be classified as “ultra-mild” [35]. There is currently no consensus about the bonding performance of the silorane adhesive system. Some studies found that silorane adhesive system showed equal performance with conventional methacrylate-based adhesives [3638]. However our study is in line with the others that found lower bond efficiency [18, 39].

This study also found that, with the exception of FZ250-BFC, SBS values of laminated composites were not affected by the type of underlying material. Thus, the second null hypothesis tested was partially rejected. This is supported by the fact that adhesive failure was the most common failure type among FS specimens. Successful adhesion between dental materials is related to the chemical composition of their surfaces [35, 40]. The use of bulk-fill flowable composites is highly desired in routine restorative practice, as they can overcome the negative effects of polymerization shrinkage and can be placed and cured in a single layer of up to 4 mm in thickness [15]. While covering bulk-fill flowable composite material with a 2 mm layer of conventional composite resin has been recommended [23], there is limited knowledge regarding laminated usage of bulk-fill flowable composites. To our knowledge, this is the first study to compare the bond strengths of two different resin composites to a bulk-fill flowable composite and conventional underlying materials.

In line with previous studies [4143], this study found the mean SBS value of FZ250 to RMGIC to be higher than that of FZ250 to CGIC, although the difference was not significant (). Some studies have suggested that the presence of HEMA and the formation of resin tags in RMGIC may be responsible for stronger bonding when compared to CGIC, regardless of the adhesive system used [44].

Failure analysis is a recommended method for assessing bonding of dental materials [45]. Cohesive failure is an indication that a strong bond has been formed at the interface of materials. In this study, not only was the bonding performance of FZ250 to BFC found to be better than to other underlying materials, cohesive failure was the main failure mode among FZ250-BFC specimens.

5. Conclusions

Within the limitations of this study, the following can be concluded.(1)SBS values of FS are lower than SBS values of FZ250. For this reason, in cases with deep cavities or where there is questionable adaptation of resin composite to the cavity wall, incremental usage of FZ250 is preferable to FS.(2)Bulk-fill composite resin appears to be a suitable alternative for use as a base under methacrylate-based composite resins.

Conflict of Interests

All authors declare that there is no conflict of interests.