PMMA Third-Body Wear after Unicondylar Knee Arthroplasty Decuples the UHMWPE Wear Particle Generation In Vitro
Table 2
Median size and morphology parameters of all analyzed particles.
| | Area (µm2) | Roundness | AR | ECD (µm) | FF | Mean diameter (µm) |
| Bone particles | 0.013* (0.003–8.978) | 0.674* (0.084–1.176) | 1.337* (1.000–5.931) | 0.129* (0.062–3.381) | 0.680* (0.067–0.903) | 0.144* (0.057–5.383) | PMMA particles | 0.011* (0.003–8.401) | 0.516* (0.067–1.176) | 1.509* (1.000–11.862) | 0.118* (0.062–3.271) | 0.606* (0.035–0.887) | 0.130* (0.057–5.742) | Control | 0.012* (0.003–6.690) | 0.578* (0.062–1.176) | 1.509* (1.000–9.897) | 0.124* (0.062–2.919) | 0.629* (0.033–0.902) | 0.130* (0.057–4.995) |
|
|
; in brackets: min.–max.
|