Carmellose Mucoadhesive Oral Films Containing Vermiculite/Chlorhexidine Nanocomposites as Innovative Biomaterials for Treatment of Oral Infections
Table 3
Physical properties of prepared mucoadhesive oral films.
| Sample | Weight (mg) | Thickness (µm) | Surface pH | Residence time (min) |
| C | 64.67 ± 3.97 | 256.25 ± 12.26 | 6.58 ± 0.01 | 25.58 ± 5.31 | C-T | 75.89 ± 8.80 | 344.36 ± 17.75 | 4.74 ± 0.01 | 82.33 ± 4.87 | 10CHDAC | 95.11 ± 8.11 | 383.12 ± 1.96 | 7.66 ± 0.07 | 69.44 ± 2.63 | 10CHDAC-T | 107.97 ± 6.11 | 436.39 ± 19.33 | 5.32 ± 0.07 | 96.46 ± 3.60 | 20CHDAC | 130.60 ± 5.21 | 522.53 ± 12.29 | 7.94 ± 0.04 | 75.03 ± 11.43 | 20CHDAC-T | 140.80 ± 6.16 | 662.09 ± 26.27 | 6.43 ± 0.07 | 84.95 ± 12.77 | 10CHDG | 96.43 ± 10.68 | 372.21 ± 4.23 | 7.46 ± 0.07 | 58.83 ± 13.29 | 10CHDG-T | 110.01 ± 5.12 | 474.32 ± 22.56 | 4.86 ± 0.11 | 84.11 ± 6.81 | 20CHDG | 131.42 ± 8.29 | 522.11 ± 15.69 | 7.76 ± 0.10 | 60.01 ± 11.82 | 20CHDG-T | 144.96 ± 10.08 | 679.53 ± 25.34 | 5.11 ± 0.05 | 97.36 ± 9.54 |
|
|