Research Article
Carmellose Mucoadhesive Oral Films Containing Vermiculite/Chlorhexidine Nanocomposites as Innovative Biomaterials for Treatment of Oral Infections
Table 4
Mechanical properties of prepared mucoadhesive oral films.
| Sample | Tensile testing | Puncture testing | Tensile strength (N) | Tensile work (mJ) | Elongation (mm) | Puncture strength (N) | Puncture work (mJ) | Deformation (mm) |
| C | 24.31 ± 0.60 | 325.00 ± 30.62 | 28.27 ± 3.49 | 15.40 ± 1.11 | 29.02 ± 2.90 | 4.92 ± 0.17 | C-T | 33.79 ± 0.57 | 176.70 ± 1.67 | 5.30 ± 0.05 | 23.52 ± 0.62 | 28.64 ± 1.15 | 2.79 ± 0.12 | 10CHDAC | 27.63 ± 3.31 | 317.71 ± 39.35 | 19.19 ± 1.52 | 15.29 ± 0.96 | 22.58 ± 1.36 | 3.60 ± 0.04 | 10CHDAC-T | 40.14 ± 1.42 | 156.28 ± 15.31 | 4.66 ± 0.04 | 22.65 ± 1.14 | 28.44 ± 1.58 | 2.20 ± 0.12 | 20CHDAC | 32.34 ± 2.25 | 332.64 ± 34.28 | 15.47 ± 0.79 | 14.34 ± 0.64 | 19.96 ± 0.91 | 2.72 ± 0.04 | 20CHDAC-T | 42.39 ± 1.23 | 116.14 ± 13.59 | 3.20 ± 0.02 | 21.08 ± 0.59 | 33.42 ± 0.65 | 1.76 ± 0.03 | 10CHDG | 24.40 ± 1.61 | 299.96 ± 10.18 | 21.39 ± 0.37 | 13.98 ± 1.70 | 22.35 ± 3.20 | 3.65 ± 0.23 | 10CHDG-T | 38.09 ± 0.37 | 167.28 ± 31.11 | 4.80 ± 0.23 | 23.29 ± 1.07 | 28.84 ± 2.55 | 2.45 ± 0.02 | 20CHDG | 21.98 ± 2.72 | 227.15 ± 46.96 | 14.65 ± 2.27 | 12.41 ± 0.48 | 18.88 ± 1.22 | 2.77 ± 0.11 | 20CHDG-T | 38.06 ± 1.44 | 136.70 ± 20.64 | 3.97 ± 0.51 | 18.67 ± 1.52 | 28.76 ± 1.42 | 1.89 ± 0.01 |
|
|