Repair of Cranial Bone Defects Using rhBMP2 and Submicron Particle of Biphasic Calcium Phosphate Ceramics with Through-Hole

<div>Morphology of the donut shape of microporous biphasic calcium phosphate ceramics (d-BCP) in the presence or absence of rhBMP2 (recombinant human bone morphogenetic proteins 2) was analyzed with SEM. d-BCP (10 mg) was soaked into rhBMP2 solution (5 <i>μ</i>g/mL) and then freeze-dried. (a, b) d-BCP, (c, d) rhBMP2/d-BCP, and (b, d) high magnification image of the d-BCP with and without rhBMP2.</div>