Mechanical Properties and Biological Behavior of 3D Matrices Produced by Electrospinning from Protein-Enriched Polyurethane
Table 3
Mechanical characteristics of untreated and GA-treated matrices after incubation in PBS.
| Matrix | Mechanical characteristics of matrix | Incubation in phosphate buffer for | Control | 7 days | 21 days |
| Untreated | 3% Tec-80A + 10% GL | Tensile strength | 14.9 ± 1.6 | 15.7 ± 0.5 | 16.8 ± 0.9 | Elongation at break | 398 ± 20 | 296 ± 38 | 298 ± 25 | 3% Tec-80A + 15% GL | Tensile strength | 15.6 ± 0.8 | 20.4 ± 1.7 | 17.0 ± 1.2 | Elongation at break | 392 ± 51 | 293 ± 24 | 383 ± 47 | 5% Tec-80A + 15% GL | Tensile strength | 10.8 ± 0.3 | 14.2 ± 1.3 | 13.8 ± 1.2 | Elongation at break | 376 ± 54 | 379 ± 37 | 527 ± 42 |
| GA-treated | 3% Tec-80A + 10% GL | Tensile strength | 15.1 ± 1.8 | 17.3 ± 2.8 | 18.1 ± 0.8 | Elongation at break | 298 ± 31 | 323 ± 24 | 304 ± 41 | 3% Tec-80A + 15% GL | Tensile strength | 9.2 ± 0.5 | 7.7 ± 1.2 | 9.9 ± 0.8 | Elongation at break | 346 ± 27 | 477 ± 39 | 472 ± 64 | 5% Tec-80A + 15% GL | Tensile strength | 9.5 ± 1.6 | 11.0 ± 2.1 | 12.0 ± 1.1 | Elongation at break | 287 ± 39 | 343 ± 51 | 530 ± 67 |
|
|
: tensile strength, MPa; elongation at break, %. |