| Sample | Specific activity* (U/g) | Thermal stability*, a (%) | Aymard-Belarbi parameters | Half-life (h) | Amount of ABTS oxidized in 24 h under denaturing conditions (mmol/U) | C | α | β | |
| CLEA-0.2-200 | 298 ± 44 | 7.9 ± 1.2 | 0,71 | 0,15 | 1,78 | 2.36 | 0.305 | CLEA-0.2-400 | 65.3 ± 1.9 | 13.5 ± 0.4 | 0,12 | −0,01 | 0,19 | 5.79 | 0.135 | CLEA-0.2-600 | 42.9 ± 3.5 | 17.7 ± 1.4 | 0,38 | 0,04 | 0,77 | 2.79 | 0.101 | CLEA-0.6-200 | 18.6 ± 3.5 | 81.5 ± 15.3 | 0,79 | 0,006 | 183166 | 44.2 | 0.178 | CLEA-0.6-400 | 103 ± 21 | 31.4 ± 6.4 | 0,74 | 0,025 | 49,72 | 0.84 | 0.094 | CLEA-0.6-600 | 133 ± 29 | 34.4 ± 7.5 | 1,04 | 0,04 | 7,65 | 18.7 | 0.172 | CLEA-1.0-200 | 77.1 ± 0.3 | 47.6 ± 0.2 | 19,3 | 0,34 | 0,34 | 20.8 | 0.159 | CLEA-1.0-400 | 14.7 ± 3.2 | 68.6 ± 14.9 | 1,32 | 0,13 | 0,125 | 62.3 | 0.301 | CLEA-1.0-600 | 24.4 ± 0.2 | 22.3 ± 0.2 | 0,76 | 0,027 | 41,2 | 16.5 | 0.123 | CLEA-0.5-1 | 35.6 ± 4.1 | 13.6 ± 7.9 | 0,32 | 0,03 | 1,27 | 1.51 | 0.379 | CLEA-0.5-100 | 156 ± 6 | 38.5 ± 4.6 | 0,76 | 0,026 | 56,8 | 5.84 | 0.334 | CLEA-1.5-1 | 69 ± 14 | 82.9 ± 17.3 | 0,80 | 0,006 | 34,8 | 7.00 | 0.259 | CLEA-1.5-100 | 39.5 ± 1.9 | 118.5 ± 1.8 | 1,58 | 0,03 | 0,03 | 78.48 | 1.103 | CLEA1.0-0.05 | 21.2 ± 6.6 | 85.5 ± 28.6 | 13,4 | 0,025 | 0,025 | 2.77 | ND | CLEA-1.0-50.5 | 78.8 ± 9.9 | 60.0 ± 4.8 | 0,51 | 0,027 | 15048 | 7.54 | 0.565 | CLEA-1.0-136 | 737 ± 24 | 68.8 ± 2.7 | 0,465 | 0,024 | 2,62 | 1.29 | 0.539 | CLEA-0.134-50.5 | 186 ± 10 | 37.2 ± 3.2 | 0,413 | 0,005 | 0,117 | 11.9 | ND | CLEA-1.867-50.5 | 16.0 ± 2.9 | 91.8 ± 2.5 | 1,58 | 0,0264 | 0,0259 | 81.1 | 1.094 | Free laccase | 284 ± 33 | 21.3 ± 2.5 | 0,433 | 0,0189 | 0,0997 | 19.7 | 0.787 |
|
|