Intrinsic Osteoinductivity of Porous Titanium Scaffold for Bone Tissue Engineering

Table 4

Mechanical properties of porous Ti scaffold and its mechanical fixation in Sawbones. Data are expressed as mean ± standard deviation; shows significant difference at .

Mechanical characteristics
Compressive strength	35 MPa
Compressive modulus	73 MPa
Young’s modulus	0.55 MPa
Mechanical stability in vitro
Push-in depth	5.8 mm
Push-in strength	5.67 MPa
Push-out strength	1.44 MPa
Interfacial shear strength	0.81 MPa (±0.36)