Nano-TiO<sub>2</sub> Doped Chitosan Scaffold for the Bone Tissue Engineering Applications

Kumar, Pawan

doi:https://doi.org/10.1155/2018/6576157

International Journal of Biomaterials

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion Data Availability Conflicts of Interest References Copyright Related Articles

Research Article | Open Access

Volume 2018 | Article ID 6576157 | https://doi.org/10.1155/2018/6576157

Nano-TiO₂ Doped Chitosan Scaffold for the Bone Tissue Engineering Applications

Pawan Kumar¹

Academic Editor: Carlo Galli

Received30 May 2018

Accepted18 Aug 2018

Published03 Sept 2018

Abstract

The present focus is on the synthesis of highly effective, porous, biocompatible, and inert scaffold by using ceramic nanoparticles and natural polymer for the application in tissue engineering. Freeze-drying method was used to fabricate nano-TiO₂ doped chitosan sample scaffold. Nano-TiO₂/chitosan scaffold can considered as an effective solution for damaged tissue regeneration. The interaction between chitosan (polysaccharide) and nano-TiO₂ makes it highly porous and brittle that could be an effective substitute for bone tissue engineering. The TiO₂ nanoparticles have a great surface area and inert properties while chitosan is highly biocompatible and antibacterial. The physiochemical properties of TiO₂ nanoparticles and scaffold are evaluated by XRD and FTIR. The nanoparticles doped scaffold has given improved density (1.2870g/cm³) that is comparatively relevant to the dry bone (0.8 - 1.2 gm/cm³). The open and closed porosity of sample scaffold were measured by using Brunauer–Emmett–Teller analyzer (BET) and scanning electron microscopy (SEM). The mechanical properties are examined by stable microsystem (Texture Analyzer). The in vitro degradation of scaffold is calculated in PBS containing lysozyme at pH 7.4. Electron and fluorescence microscopy are used to study morphological characteristics of the scaffolds and TiO₂ nanoparticles. The growth factor and drug-loaded composites can improve osteogenesis and vascularization.

1. Introduction

In the human body, bone is an extremely dynamic and diverse tissue (structurally and functionally). The human skeletal system is a collection of long to short, flat, and irregular bones. The average pore sizes of bone are 100-300 μm. The active diffusion of nutrients occurs within 150-200 μm pore sizes from blood supply. The nonmineralized (type-1 collagen) and mineralized phases (plate like apatite) are main composition of bone extracellular matrix [1–3]. Trauma, injury, infections, and bone extracellular matrix (ECM) loss are among the most human health threatening problems. Bone tissue engineering easily eliminates the issues of surgical treatments including donor site morbidity, inadequate availability, immune response of the body, and infections. The different substitutes including hydroxyapatite, different composition of bioactive glass, a number of synthetic and natural polymers, and their composites were fabricated for the bone tissue engineering. Still, none of the above materials could meet all the characteristics of bone graft substitutes [4, 5]. The three major approaches of tissue engineering include isolated bone cells (osteogenic) transplantation or injection to the desired injured site, application of isolated tissue inducing molecules, or growth factors to the defected site and designing of 3D scaffolds [6]. Chitosan (natural polysaccharide) is the derivative of chitin (most abundant in nature after cellulose), used as graft material in tissue restoration because of its high biocompatibility and rapid degradation without toxicity. The well-designed 3D scaffold having the capability to mimic the extracellular matrix of bone promotes cell adhesion and cell proliferation without producing toxicity and helps in the promotion of new tissue [7, 8]. The progress of any scaffold depends on its porosity and biomechanical and physical properties that allows fast vascularization without producing cytotoxicity. The chitosan scaffold exhibits cationic nature, which is liable for exchange of negatively, charged molecules like proteoglycans, glycosaminoglycan (GAG), and other nutrients [9]. GAG is the chief constituent of ECMs that allow cell accumulation or adhesion and proliferation on the surface of scaffold. Many studies stated that the porous structure [10] gels [11], thin films [12], membranes [13], and fibres [14] favour more bone cell growth with chitosan. However, chitosan has numerous shortcomings such as lack of mechanical strength, fast degradation, and missing of cell signaling molecules that are most important for growth of damaged tissue [15, 16]. Titanium oxide (TiO₂) is available in the form of nanocrystals having a high surface area. Some researcher [17] observed the antiseptic and antibacterial activity of titanium oxide. Some researcher also proposed that TiO₂ can be used as good filler materials in biodegradable polymers because the presence of titanium oxide enhances cell attachment and cell proliferation [18]. Due to its inert property, it has medical and health applications. Both chitosan and TiO₂ nanoparticles are biocompatible, inert, and chemically stable so that they can be useful for hard tissue engineering also. They support cell adhesion and proliferation without producing toxicity. A lightweight and cost-effective TiO₂/chitosan scaffold can be fabricated by freeze-drying method that fulfills many biomechanical requirements of a hard tissue graft. The present work includes TiO₂ nanoparticles doped chitosan for scaffold synthesis.

2. Materials and Methods

2.1. Materials

Analytical grade low molecular weight chitosan (75-85% deacetylated), titanium tetra isopropoxide (TTIP, 97% assay), sodium borohydride, glutaraldehyde (25% in H₂O), acetic acid, and NaOH were purchased Sigma-Aldrich. Lysozyme was procured from Thermo Fisher Scientific.

2.2. Synthesis of TiO₂ Nanoparticles

The hydrothermal method is used for the TiO₂ nanoparticles synthesis. Firstly, 1M titanium tetra isopropoxide (TTIP) is used to make colloidal solution by hydrolysis, mixed with acetic acid (4M), and allowed for one hour of stirring. After an aging period of 24 hours, 25 ml of this solution transferred to Teflon lined tube of stainless steel autoclave and placed in oven at 180°C for 12 hours. After that, precipitates were washed three times with distilled water. The mixture solution was filtered and placed in oven for drying at 100°C to get TiO₂ crystal [19].

2.3. Scaffold Synthesis

For the synthesis of chitosan/TiO₂ sample scaffold, firstly make 2% (w/v) solution of chitosan by the addition of 1% (w/v) acetic acid solution with 6 h stirring. The calculated amount (1g) of titanium oxide nanoparticles is mixed with 100 ml distilled water to make slurry. Add this slurry in viscus solution of chitosan with continuous stirring for 12 h at room temperature. 1 M solution of NaOH is used dropwise to adjust pH 10 of the mixture. 0.5 ml solution of glutaraldehyde (0.25% v/v) is used to make cross-linking between chitosan and TiO₂. After 15 hours of stirring, degas the suspension centrifugally and dispense it into Petri plates. These Petri plates are placed at - 80°C in an ultralow temperature freezer (LFZ-86L series, LABFREEZ) for 72 hours. After 72 hours, these frozen samples were transferred to the chamber of lyophilizer (ALLID FROST, Macflow Engg. Pvt. Ltd.), where the ice was removed by direct sublimation and the unfrozen water removed by desorption in a secondary drying process [20]. The freeze-dried sample neutralized with distilled water to remove acetate residue. The free glutaraldehyde (uncross-linked) was removed by using 5% sodium borohydride (reducing agent) solution and then washed with distilled water. After that, lyophilize these samples again for 48 h and collect pale yellow color scaffolds as shown in Figure 1.

2.4. XRD Analysis

The graphical X-ray powder diffraction patterns of the TiO₂ and chitosan/TiO₂ samples were noted down by Rigaku Ultima IV X-Ray diffractometer, using Cu-Ka (1.5406 Å) radiation at room temperature in the range of 10° to 60° at 2 theta degree scale.

2.5. FTIR Analysis

The Fourier transform infrared (FTIR) spectra (from 4000 cm⁻¹ to 400 cm⁻¹) of the hydrothermally synthesized TiO₂ nanoparticles and chitosan/TiO₂ scaffold were recorded in Perkin Elmer Spectrum RX1 spectrometer. FTIR gives the information related to the presence of different chemical or functional groups in the samples.

2.6. SEM Observation

Scanning electron microscope (SEM, JEOL) has given the information about the surface and the fracture section of scaffold. For the SEM analysis, thin section of sample scaffold was used with gold prior coating.

2.7. TEM Observation

Transmission Electron Microscope produces high-resolution images by the transmission of high-energy electron through the specimen. Structure, composition, and size of nanoparticles were analyzed by TEM (Hitachi H 7500) results. These nanoparticles were used for doping with chitosan to make scaffold.

2.8. Bulk Structure Analysis

Fluorescence Microscope (Leica DM 250) studied the surface topography and distribution of TiO₂ nanoparticles in chitosan gel. The chitosan/TiO₂ gel was used to understand the connectivity and branched structure existing between chitosan and TiO₂.

2.9. Porosity Measurement

The pore volume, micropore radius, and pore specific surface area of the sample were examined by BET (Quantachrome® Nova Station). The small sized pieces of sample scaffold were loaded in the sample tube and set measurement conditions. These results are mostly concentration- and viscosity-dependent.

2.10. Mechanical Properties

The sample size of 2.5×4×4 mm³ was cut down for the fracture strength measurement. The values of results can be uttered as the mean ± standard error. The force versus time graph is used to explain the hardness of the chitosan/TiO₂ scaffold.

2.11. Density

Density measurement is important for physical property evaluation. Equation (1) was used to measure the density of scaffold that give the calculated ratio of the mass by volume of sample [21].where D is the diameter, is density, H is the thickness, and W is the weight of the sample, respectively.

2.12. Swelling Behavior

PBS solution was used to check the swelling or water retention capability of the sample scaffold. The swelling capacity depends on the porosity of the sample and nature of materials. The swelling capacity of the sample was calculated by the following [21]:where is initial weight and is the weight of the sample after swelling.

2.13. Biodegradation

The measurement of in vitro weight degradation of the chitosan/TiO₂ scaffold was required to estimate the bioavailability of materials. The pieces of the sample were incubated in the PBS solution (pH 7.4) containing 1 × 10⁴ U/ml of lysozyme at room temperature for 14 days. After the interval of 7 and 14 days, degradation of the sample was recorded by using the following [21]:where W₀ is initial weight and W_f is the final weight after degradation sample.

2.14. Cytotoxicity

To check the cytotoxicity and biocompatibility of chitosan/TiO₂ scaffolds, fibroblast cell lines were maintained in the cell culture facility in MEM with 10% FBS and 100 U/ml penicillin–streptomycin. Before cell seeding, all the sample scaffolds were sterilized and placed in an incubator with cell culture for 2 hours with 5% CO₂ and 85% humidity. The detached cells (1×10⁵ cells/100 μl) were seeded dropwise on the surface of scaffolds for the investigation of cytocompatibility. The cell seeded scaffolds were placed in a humidified incubator at 37°C for 4 h for the cell attachment [22].

3. Results and Discussion

The formation of nano-TiO₂ was confirmed in XRD spectra (Figure 2). The particle size (4.48 nm) of TiO₂ was determined by using Scherrer equation. The chitosan/TiO₂ scaffold has shown a crystalline nature. The XRD of chitosan/TiO₂ scaffold and TiO₂ nanoparticles showed peaks at 25.7°, 35.8°, 36.9°, 40.2°, 46.6°, and 53.0° corresponding to TiO₂ (crystalline) and broad phase from 18 to 21° corresponding to chitosan (slightly amorphous). The FTIR spectrum has confirmed the presence of relevant functional groups in the sample (Figure 3). There is a band present from 2800 to 3400 cm⁻¹ in the sample due to OH stretching vibrations. The band present from 600 to 711 cm⁻¹ represents Ti–O–Ti stretching bonding [23]. The peak present in the sample near 1630 cm⁻¹ shows Ti-OH bending vibrations of adsorbed H₂O molecules and peak at 1380cm⁻¹ indicating Ti-O [24]. The presence of C-H, C=O, and CH-OH groups was confirmed at 2924, 1656, and 1422 cm⁻¹, respectively [25].

The hydrothermally synthesized nano-TiO₂ is examined by TEM as shown in Figure 4. The TEM image of TiO₂ is shown around 2 nm sized particles with irregular shape. TiO₂ slurry does an interfacial interaction between chitosan and nanoparticles, which causes a nanoscale dispersion of TiO₂ in the matrix. The interaction between TiO₂ nanoparticles and chitosan depends on the charge state of the interface. Cationic chitosan is adsorbed on the surface of TiO₂, driven by electrostatic interactions and steric effects; adsorption is strictly pH-dependent and creation of stable TiO₂–chitosan composite [26]. Glass transition temperature (Tg) of chitosan (dry state) was found to be 118C confirmed by conventional DSC. The polymer-nanoparticles interactions play a key role in controlling the local dynamics of matrix and glass transition value of sample. The uniform dispersion of TiO₂ in chitosan matrix improved the glass transition temperature (Tg) chitosan/TiO₂ sample [27]. The well-interconnected, heterogeneous pore microstructures in sample scaffold are shown in Figure 5. Stretched pores were generated in the scaffold during lyophilization whose formation might be due to hydrogen bonding formation between polymer and nanoparticles and parallel ice crystal growth. SEM images of scaffold revealed mixed size of pores from 8.24 to 38.43μm were found in the chitosan/TiO₂ scaffold which are more relevant for tissue engineering because the pore sizes of bone, muscle, and skin vary from 20 to 300 μm [20]. The pore size lower than 300μm helps to proliferate osteoblast cell easily through the scaffold [28]. Porosity of scaffold examined by BET revealed a specific surface area (2.7752 m²g⁻¹), pore specific surface area (3.8751 m²g⁻¹), pore volume (0.0030 cm³g⁻¹), and pore diameter 2.86 nm. Previously examined chitosan and chitosan-gelatin scaffolds [20] show less porosity than chitosan/TiO₂ scaffold. The addition of TiO₂ nanoparticles increased porosity of scaffold. The addition of nano-f-CNT in chitosan increased porosity [29], while the addition of nanosilica reduces the porosity [30]. The sample of chitosan/TiO₂ as observed by fluorescence microscopy (Figure 6) revealed a low surface density of biomolecules and interconnected branched structure clearly shown in the image. The experimental density of chitosan/TiO₂ scaffold found 1.2870g/cm³, which is more than chitosan and chitosan/gelatin scaffolds [20] and comparatively nearby the normal dry bone density (0.8 - 1.2 g/cm³). The density of TiO₂ is 4.23 g/cm³ which is less than stainless steel 316L (7.9g/cm³), tantalum (16.6), and gold (19.3g/cm³); however, it is better than fat (0.94g/cm³), soft tissues (1.01-1.06g/cm³), glass (2.4-2.8g/cm³), bone (1-2 g /cm³), and aluminum oxide (3.98g/cm³). The density of chitosan is very low (0.15-0.30 g/cm³) so TiO₂ is selected as a dopant to increase the density of scaffolds. The addition of nanobioglass and nanosilica enhanced the density of scaffolds [22, 30] but in this work we found that nano-TiO₂ reduces the density of scaffold. The change in density of a scaffold depends upon the concentration of chitosan in a composition. The force-time graph shows the fracture strength with respect to breaking time of sample as shown in Figure 7. The doping of titanium oxide makes effective improvements in the strength of scaffold without producing toxicity, proved by International Agency for Research on Cancer (IARC). The force bearing capacity of the sample was 1347.5 N/m² and breaking time was 0.58 sec that is better than chitosan scaffold, i.e., as previously described in [20], but less than CS/Alg, CS/Alg/nSiO₂, chitosan/CNT, chitosan-PPy-Alg, and chitosan-gelatin scaffolds [20, 29–32]. Hence, the scaffold can be used for preparing implants of bioinert and lightweight, which makes brittle composite with low density. The physical and mechanical characteristics of scaffold depend on the viscosity, ingredient concentration, pH of matrix, temperature, and lyophilization. At room temperature, the observed water retention capacity of chitosan-TiO₂ scaffold is found to be 24%, which is less than chitosan, chitosan-gelatin [20], chitosan-PPy-Alg [31], chitosan-alginate, chitosan-silica, [32], and chitosan-bioglass [22] scaffolds. The retention is also depending upon the porosity and nature of materials contained by the scaffolds. The percentage degradation of chitosan/TiO₂ scaffold was very slow compared to other chitosan based scaffolds [20, 29–32], 12.24% after 7 days and 14.80% after 14 days. The degree of crystallinity is the major factor, which controls the hydrolysis rate. However, TiO₂ supports apatite formation when it is encountered with Simulated Body Fluid [33]. TiO₂ nanoparticles have shown similarity with nanostructured nature of microenvironment. They have ability to pass the biological barriers, enter into the cell nuclei, and affect the cell functions such as proliferation and differentiation. From results, we found that the incorporation of TiO₂ in chitosan did not show any influence on fibroblast proliferation. Cytotoxicity and cell attachment studies showed the nanocomposites are nontoxic to an array of fibroblast cell line. The incorporation of TiO₂ into biodegradable scaffolds may enhance cell seeding and hence the subsequent tissue growth [34]. After preselected time intervals (7 and 14 days), the number of cells increased as shown in Figures 8 and 9. Fibroblast cells were successfully grown on the surface of chitosan/TiO₂ scaffolds.

4. Conclusion

The lyophilized sample of the scaffold was pale yellow in color, brittle, and inelastic. The scaffold fabricated using the freeze-drying technique exhibited high porosity and relatively low density with good mechanical properties. The remarkable adsorption or water retention capacity of TiO₂ doped chitosan scaffold was noticed during investigation. The addition of TiO₂ reduces the fast degradation of scaffold. The nanoparticles restricted the formation of the strong bond during sample preparation. Hence, it can be concluded that nanoparticles doped scaffolds can be used for preparing a biocompatible implant with lighter weight. The natural origin and biocompatible nature of chitosan support bone cells attachment, proliferation, and mineralization. Titanium oxide is inert in nature, so the combination of chitosan/TiO₂ can be a good substitute for tissue engineering. Still a lot of research needs to be conducted for optimizing different parameters of scaffolds without compromising biodegradability and toxicity. Multidisciplinary approach for fabrication of new scaffolds with improved properties is highly desired.

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The author declare that they have no conflicts of interest.

References

F. Anagnostou, R. Bizios, and H. Petite, “Engineering bone: challenges and obstacles,” Journal of Cellular and Molecular Medicine, vol. 9, no. 1, pp. 72–84, 2005.
View at: Publisher Site | Google Scholar
J. Zeltinger, J. K. Sherwood, D. A. Graham, R. Müeller, and L. G. Griffith, “Effect of pore size and void fraction on cellular adhesion, proliferation, and matrix deposition,” Tissue Engineering Part A, vol. 7, no. 5, pp. 557–572, 2001.
View at: Publisher Site | Google Scholar
D. W. Hutmacher, “Scaffold design and fabrication technologies for engineering tissues—state of the art and future perspectives,” Journal of Biomaterials Science, Polymer Edition, vol. 12, no. 1, pp. 107–124, 2001.
View at: Publisher Site | Google Scholar
R. J. O'Keefe and J. Mao, “Bone tissue engineering and regeneration: from discovery to the clinic-an overview,” Tissue Engineering—Part B: Reviews, vol. 17, no. 6, pp. 389–392, 2011.
View at: Publisher Site | Google Scholar
C. Wang, H. Shen, Y. Tian et al., “Bioactive Nanoparticle–Gelatin Composite Scaffold with Mechanical Performance Comparable to Cancellous Bones,” ACS Applied Materials & Interfaces, vol. 6, no. 15, pp. 13061–13068, 2014.
View at: Publisher Site | Google Scholar
H. Chen, R. Truckenmüller, C. Van Blitterswijk, and L. Moroni, “Fabrication of nanofibrous scaffolds for tissue engineering applications BT-Nanomaterials in Tissue Engineering,” in Woodhead Publishing Series in Biomaterials, pp. 158–183, Woodhead Publishing, 2013.
View at: Publisher Site | Google Scholar
W. W. Thein-Han, J. Saikhun, C. Pholpramoo, R. D. K. Misra, and Y. Kitiyanant, “Chitosan-gelatin scaffolds for tissue engineering: physico-chemical properties and biological response of buffalo embryonic stem cells and transfectant of GFP-buffalo embryonic stem cells,” Acta Biomaterialia, vol. 5, no. 9, pp. 3453–3466, 2009.
View at: Publisher Site | Google Scholar
A. M. Martins, C. M. Alves, F. Kurtis Kasper, A. G. Mikos, and R. L. Reis, “Responsive and in situ-forming chitosan scaffolds for bone tissue engineering applications: an overview of the last decade,” J. Mater. Chem., vol. 20, no. 9, pp. 1638–1645, 2010.
View at: Publisher Site | Google Scholar
A. di Martino, M. Sittinger, and M. V. Risbud, “Chitosan: a versatile biopolymer for orthopaedic tissue-engineering,” Biomaterials, vol. 26, no. 30, pp. 5983–5990, 2005.
View at: Publisher Site | Google Scholar
T. Jiang, C. M. Pilane, and C. T. Laurencin, “Fabrication of Novel Porous Chitosan Matrices as Scaffolds for Bone Tissue Engineering,” Materials Research Society - Proceedings, vol. 845, 2004.
View at: Publisher Site | Google Scholar
M. Yamamoto, Y. Takahashi, and Y. Tabata, “Controlled release by biodegradable hydrogels enhances the ectopic bone formation of bone morphogenetic protein,” Biomaterials, vol. 24, no. 24, pp. 4375–4383, 2003.
View at: Publisher Site | Google Scholar
N. Sultana, “Study of in vitro degradation of biodegradable polymer based thin films and tissue engineering scaffolds,” African Journal of Biotechnology, vol. 10, pp. 18709–18715, 2011.
View at: Publisher Site | Google Scholar
C. E. Orrego and J. S. Valencia, “Preparation and characterization of chitosan membranes by using a combined freeze gelation and mild crosslinking method,” Bioprocess and Biosystems Engineering, vol. 32, no. 2, pp. 197–206, 2009.
View at: Publisher Site | Google Scholar
F. Pati, H. Kalita, B. Adhikari, and S. Dhara, “Osteoblastic cellular responses on ionically crosslinked chitosan-tripolyphosphate fibrous 3-D mesh scaffolds,” Journal of Biomedical Materials Research Part A, vol. 101, no. 9, pp. 2526–2537, 2013.
View at: Publisher Site | Google Scholar
M. Okada and T. Furuzono, “Hydroxylapatite nanoparticles: fabrication methods and medical applications,” Science and Technology of Advanced Materials, vol. 13, no. 6, p. 064103, 2012.
View at: Publisher Site | Google Scholar
J. R. Porter, T. T. Ruckh, and K. C. Popat, “Bone tissue engineering: a review in bone biomimetics and drug delivery strategies,” Biotechnology Progress, vol. 25, no. 6, pp. 1539–1560, 2009.
View at: Publisher Site | Google Scholar
S. M. Gupta and M. Tripathi, “A review of TiO₂ nanoparticles,” Chinese Science Bulletin, vol. 56, no. 16, pp. 1639–1657, 2011.
View at: Publisher Site | Google Scholar
J. K. Savaiano and T. J. Webster, “Altered responses of chondrocytes to nanophase PLGA/nanophase titania composites,” Biomaterials, vol. 25, no. 7-8, pp. 1205–1213, 2004.
View at: Publisher Site | Google Scholar
R. Vijayalakshmi and V. Rajendran, “Synthesis and characterization of nano-TiO₂ via different methods,” Scholars Research Library, vol. 4, pp. 1183–1190, 2012.
View at: Publisher Site | Google Scholar
P. Kumar, B. S. Dehiya, and A. Sindhu, “Comparative study of chitosan and chitosan–gelatin scaffold for tissue engineering,” International Nano Letters, vol. 7, no. 4, pp. 285–290, 2017.
View at: Publisher Site | Google Scholar
J. S. Mao, L. G. Zhao, Y. J. Yin, and K. D. Yao, “Structure and properties of bilayer chitosan-gelatin scaffolds,” Biomaterials, vol. 24, no. 6, pp. 1067–1074, 2003.
View at: Publisher Site | Google Scholar
M. Peter, N. S. Binulal, S. V. Nair, N. Selvamurugan, H. Tamura, and R. Jayakumar, “Novel biodegradable chitosan-gelatin/nano-bioactive glass ceramic composite scaffolds for alveolar bone tissue engineering,” Chemical Engineering Journal, vol. 158, no. 2, pp. 353–361, 2010.
View at: Publisher Site | Google Scholar
H. Pan, X. Wang, S. Xiao, L. Yu, and Z. Zhang, “Preparation and characterization of TiO2 nanoparticles surface-modified by octadecyltrimethoxysilane,” Indian J. Eng. Mater. Sci, vol. 20, pp. 561–567, 2013.
View at: Google Scholar
A. León, P. Reuquen, C. Garín et al., “FTIR and Raman Characterization of TiO2 Nanoparticles Coated with Polyethylene Glycol as Carrier for 2-Methoxyestradiol,” Applied Sciences, vol. 7, no. 1, p. 49, 2017.
View at: Publisher Site | Google Scholar
S. Yasmeen, M. Kabiraz, B. Saha, M. Qadir, M. Gafur, and S. Masum, “Chromium (VI) Ions Removal from Tannery Effluent using Chitosan-Microcrystalline Cellulose Composite as Adsorbent,” International Research Journal of Pure and Applied Chemistry, vol. 10, no. 4, pp. 1–14, 2016.
View at: Publisher Site | Google Scholar
A. E. Wiącek, A. Gozdecka, and M. Jurak, “Physicochemical Characteristics of Chitosan–TiO,” Industrial & Engineering Chemistry Research, vol. 57, no. 6, pp. 1859–1870, 2018.
View at: Publisher Site | Google Scholar
F. A. Al-Sagheer and S. Merchant, “Visco-elastic properties of chitosan-titania nano-composites,” Carbohydrate Polymers, vol. 85, no. 2, pp. 356–362, 2011.
View at: Publisher Site | Google Scholar
M. C. Nerantzaki, I. G. Koliakou, M. G. Kaloyianni et al., “New N-(2-carboxybenzyl)chitosan composite scaffolds containing nanoTiO2 or bioactive glass with enhanced cell proliferation for bone-tissue engineering applications,” International Journal of Polymeric Materials and Polymeric Biomaterials, vol. 66, no. 2, pp. 71–81, 2017.
View at: Publisher Site | Google Scholar
J. Venkatesan, B. Ryu, P. N. Sudha, and S.-K. Kim, “Preparation and characterization of chitosan-carbon nanotube scaffolds for bone tissue engineering,” International Journal of Biological Macromolecules, vol. 50, no. 2, pp. 393–402, 2012.
View at: Publisher Site | Google Scholar
K. C. Kavya, R. Jayakumar, S. Nair, and K. P. Chennazhi, “Fabrication and characterization of chitosan/gelatin/nSiO₂ composite scaffold for bone tissue engineering,” International Journal of Biological Macromolecules, vol. 59, pp. 255–263, 2013.
View at: Publisher Site | Google Scholar
K. M. Sajesh, R. Jayakumar, S. V. Nair, and K. P. Chennazhi, “Biocompatible conducting chitosan/polypyrrole-alginate composite scaffold for bone tissue engineering,” International Journal of Biological Macromolecules, vol. 62, pp. 465–471, 2013.
View at: Publisher Site | Google Scholar
J. A. Sowjanya, J. Singh, T. Mohita et al., “Biocomposite scaffolds containing chitosan/alginate/nano-silica for bone tissue engineering,” Colloids and Surfaces B: Biointerfaces, vol. 109, pp. 294–300, 2013.
View at: Publisher Site | Google Scholar
T. Kasuga, H. Kondo, and M. Nogami, “Apatite formation on TiO2 in simulated body fluid,” Journal of Crystal Growth, vol. 235, no. 1-4, pp. 235–240, 2002.
View at: Publisher Site | Google Scholar
R. Jayakumar, R. Ramachandran, V. V. Divyarani, K. P. Chennazhi, H. Tamura, and S. V. Nair, “Fabrication of chitin-chitosan/nano TiO2-composite scaffolds for tissue engineering applications,” International Journal of Biological Macromolecules, vol. 48, no. 2, pp. 336–344, 2011.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2018 Pawan Kumar. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

3251

Downloads

1756

Citations