Behavior of PMMA Denture Base Materials Containing Titanium Dioxide Nanoparticles: A Literature Review

Gad, Mohammed M.; Abualsaud, Reem

doi:https://doi.org/10.1155/2019/6190610

International Journal of Biomaterials

On this page

Abstract Introduction Conclusion Conflicts of Interest References Copyright Related Articles

Review Article | Open Access

Volume 2019 | Article ID 6190610 | https://doi.org/10.1155/2019/6190610

Behavior of PMMA Denture Base Materials Containing Titanium Dioxide Nanoparticles: A Literature Review

Mohammed M. Gad¹and Reem Abualsaud²

Academic Editor: Wen-Cheng Chen

Received14 Nov 2018

Revised22 Dec 2018

Accepted02 Jan 2019

Published17 Jan 2019

Abstract

Titanium dioxide nanoparticles (TiO₂NP) have gained interest in the dental field because of their multiple uses in addition to their antimicrobial effect. One of the applications in dentistry involves the incorporation into poly methyl methacrylate (PMMA) resin. However, there is a lack of evidence on their effects on the behavior of the resulting nanocomposite. Therefore, the present review aims to screen literatures for data related to PMMA/TiO₂ nanocomposite to figure out the properties of TiO₂ nanoparticles, methods of addition, interaction with PMMA resin matrix, and finally the addition effects on the properties of introduced nanocomposite and evidence on its clinical performance. Regardless of the latest research progress of PMMA/TiO₂ nanocomposite, the questionable properties of final nanocomposite and the lack of long-term clinical evidence addressing their performance restrict their wide clinical use. A conclusive connection between nanoparticle size or addition method and nanocomposite properties could not be established.

1. Introduction

The numerous advantages of poly methyl methacrylate (PMMA) make it the most dominant polymer used as denture base material. The ease of processing, low cost, light weight, stability in the oral cavity, and aesthetic properties are of these advantages [1]. However, this material is not ideal in every aspect. PMMA resin denture base material has poor surface properties and weak mechanical properties including impact and flexural strengths [2]. Therefore, resins should be reinforced using different materials to enhance their properties. Recently, nanotechnology invaded the dental field and initiated investigative research projects to explore the possible applications and expected benefits within dentistry. It is of paramount importance to know the science behind this nanotechnology to know how to utilize it to our advantage. Polymeric nanocomposites are made of polymer matrix and filler at the nanoscale [3]. Literature shows that nanoscale reinforcing agents produce new mechanical and physical properties, which create a new class of nanocomposites [4]. In dentistry, many attempts have been made to create an improved version of PMMA with the addition of different nanosized fillers [5]. The properties of the new composite material depend on the nature of the added nanoparticles, their size, and morphology [6].

The science and applications of nanotechnology are constantly evolving as we witness new products being introduced into the market. This comes with great responsibility to insure the safety, efficiency, and applicability of such new technologies. Although nanomaterials generally offer superior properties, their mechanical properties fall short in comparison to pure materials. Lately, worldwide research showed several advancements in the nanocomposite field after the extensive research on mechanical and physical properties of these nanocomposites [7]. Different nanoparticles have been incorporated into the polymer matrix. Among these is TiO₂NP with its unique properties [7, 8]. The literature investigated the effect of TiO₂NP on some properties of PMMA. But a comprehensive study on the overall performance of PMMA nanocomposite was not observed. In addition to that, the relation between final properties of the composite and the actual structure is not available. One of the goals of the present study is to review the effectiveness of TiO₂NP addition to PMMA for dental applications. It also seems necessary to determine the best percentage of filler required to improve the properties as well as the method of reinforcement to control future applications.

Up to November of 2018, database search on Google scholar, PubMed, and Scopus was conducted using the key words “Denture base; Polymethylmethacrylate (PMMA); TiO₂ nanoparticles; Physical properties”. Forty-eight articles were found (Figure 1). Only 21 articles written in English language were included, where the titanium nanoparticles were incorporated into PMMA denture base material. The twenty-seven excluded articles did not fulfill the inclusion criteria. Few of the excluded articles were investigating the effect of surface coating with titania layer on physical properties (6 articles) and three others used microsized titania particles. Other excluded articles were investigating: a mixture of two nanofillers (ZrO₂/TiO₂), (Fe₂O₃/TiO₂) (2 articles), the addition of barium titanate as a filler (3 articles), the addition of titania nanotubes (1 article), mica or zirconia/ABW (Aluminum borate whiskers) reinforced denture base acrylic (2 article), gallates modified titanium nanoparticles (1 article), and PMMA not used for denture bases (3 articles). Two excluded papers lacked full experimental data, three papers were reviews, and one paper was not in English language. The selected articles were reviewed to extract all data related to PMMA/TiO₂ nanocomposite and to figure out the properties of TiO₂NP, method of addition, interaction with PMMA resin matrix, effects on the properties of newly introduced nanocomposite, and finally evidence on their clinical performance.

1.1. Properties of NP

TiO₂NP has proved to have antimicrobial properties. Moreover, it is a cheap biocompatible material, chemically stable, free of toxicity, resistant to corrosion with high strength, and high refractive index [8, 18, 23, 30]. Furthermore, the literature showed that even the slight addition of TiO₂NP reinforcing agent to a polymeric material affects the electrical, optical, chemical, and physical properties of the resulting hybrid material [9, 31].

Its photocatalytic ability promoted it to be known as an antimicrobial agent encouraging its addition to biomaterials [11, 12, 20, 23, 25]. TiO₂NP have been found effective against a wide range of microorganisms including gram-positive and gram-negative bacteria, fungi, and viruses [11, 23, 25]. The antimicrobial effect could be attributed to the surface properties and structure of the nanoparticles, including; nanocrystalline TiO₂, hydrophilic surface effect, infrared reflectivity, and noncontact antimicrobial activity. Therefore, TiO₂NP have been recommended as filler in polymeric materials [24].

1.2. Methods of PMMA/ Nanocomposite Preparation

Resulting properties of the hybrid material (PMMA/TiO₂NP) will depend on the dispersion of the nanoparticles within the matrix, which is directly related to the added amount [9]. To achieve good dispersion of nanoparticles within polymers, different methods of TiO₂NP addition were suggested. It is either added to acrylic powder or monomer. The addition of TiO₂NP to acrylic powder was suggested where the required percentages were weighed and thoroughly mixed with acrylic powder. To attain a uniform mixture and homogenous distribution of TiO₂NP, ultrasonic mixer, mortar, and pestle, high-energy ball milling and silanization of particles were all employed in which ball milling seemed to be the most effective method [16, 19, 21–23]. In another method, TiO₂ nanoparticles were mixed with the acrylic powder up to 20 min in an amalgamator to obtain a homogenous mix [15, 21]. Others mixed the nanoparticles with resin powder by hand to create the desired filler/powder ratio [13, 14].

Addition of TiO₂NP to liquid monomer is another method of filler incorporation within acrylic resin [22]. Investigators added nanoparticles to acrylic monomer to prepare monomer/TiO₂NP in different concentrations. To insure uniformity, ultrasonic dispersion was done [10, 24]. The monomer containing NP was sonicated for 60 min before mixing with PMMA powder [32]. Others were sonicated using a probe at 120 W and 60 KHz for 3 min to prevent nanoparticles agglomeration and insure homogeneity of the mixture [18, 25].

An additional method called twin-screw extraction process was developed to disperse the particles into the PMMA [9, 33, 34]. TiO₂NP was mixed with the acrylic and extruded using ZSK-25 twin-screw extruder at 210°C and screw speed of 250 rpm. Nanocomposite granules were then dried at 80°C for 2 h using dryer unit of injection molding machine [34].

Hence, the properties of nanocomposites depend on the interactions between the polymer matrix and the filler, suggesting the importance of functionalized TiO₂NP [35, 36]. As revealed by a previous study, PMMA nanocomposite based on functionalized TiO₂NP demonstrated better mechanical and physical properties [30]. One reported method of silanization used 100 ml of ethanol solution (70 vol%) with adjusted pH of 4.5 through titrating with 99.9% acetic acid. Following that, silane-coupling agent (TMSPM) was added to ethanol solution and mixed. A hundred grams of TiO₂NP were added to TMSPM-ethanol solution and mixed for 20 minutes followed by probe sonication for 30 minutes. The mixture was then left to dry for 14 days and the resulting powder was a silanized TiO₂NP [18, 37]. Others modified the titania nanoparticles using methacrylic acid (MA) by dispersing 10 g of nanoparticles into 250 ml iso-propanol and 125 ml of MA into 80°C ultrasonic bath for 8h. The resulting compound was dried at 85°C after infiltration and washing [14].

1.3. Behavior of NP toward PMMA

In addition to NP size and shape, its interaction with PMMA matrix is considered a main factor of reinforcement effectiveness, which depends on the surface characterization of the NP. Chatterjee (2010) studied the interaction between PMMA and TiO₂NP and found that they interact chemically and physically [9]. The TiO₂NP can react with -COOR group of PMMA polymer in two different ways. One way is the formation of H-bond between carbonyl group (-C=O) and surface hydroxyl group (-OH) of TiO₂NP. The other way is the binding of TiO₂NP with two oxygen atoms of -COOR by a bidentate coordination to Ti⁴⁺ cation [9]. When TiO₂NP come to the surface, they form crosslinks with PMMA [9]. As the amount of TiO₂NP loading within the PMMA increases, this bonding also increases. All this is possible because of the hydroxyl group on the surface of TiO₂NP and the -C=O (Carbonyl), -OH (Hydroxyl), -COOH (Carboxyl), and -COOR (Ester) groups in the polymer matrix. The cross linking has been confirmed by Fourier-transform infrared spectroscopy (FTIR) [22, 33].

The dispersion of the TiO₂NP within the matrix hinders polymer chain movements due to the strong adhesion between the TiO₂NP and PMMA. As a result, better modulus is seen with TiO₂NP-PMMA composite materials [9]. Other investigators reported increased stiffness of the composite material and decreased PMMA mobility [19]. This may be due to the large interface of TiO₂NP when wrapped in PMMA, which possesses a smaller dielectric coefficient. There will be a strong electric interaction between them resulting in an electric dipole layer at the nanoparticle surface. In terms of the atomic bonding, the origin of the nonlinear refractive index may be due to the hyperpolarizability of Ti-O pairs [21, 38]. Moreover, the addition of spherical nanoscale particles is capable of filling the interpolymeric spaces, which was found to enhance the polishability of the material [15].

1.4. Properties of PMMA/ Nanocomposite

As mentioned earlier, PMMA is the most predominant polymer-based material for dentures. However, its mechanical and surface properties are low [39]. The addition of any material to improve the antimicrobial properties of the PMMA should not have an adverse effect on the mechanical properties. In reverse, it is highly preferred to add a material that will improve both biological and mechanical properties [34]. TiO₂NP is commonly used as a coloring agent and filler. It is capable of increasing the toughness of polymers producing a composite material with superior properties [40]. With the added antimicrobial property, it is incorporation into PMMA resins is extensively used in oral removable appliances [41]. Therefore, the properties of the nanocomposite were screened in this review to evaluate the reliability of TiO₂NP as an additive to improve the performance of PMMA/TiO₂ nanocomposite denture base material.

1.4.1. Antimicrobial Activities

TiO₂NP were found to have an intrinsic antimicrobial property due the production of cytotoxic oxygen radicles [26]. TiO₂NP are ideal additives because of their nontoxicity and chemical stability. However, under certain conditions they have an antimicrobial ability [41]. When they are exposed to UV-light in the presence of oxygen and water, they decompose and oxidize other compounds; organic and inorganic. Therefore, they can be considered as antimicrobial additive [41]. Furthermore, TiO₂NP had the ability to inhibit the adherence of cariogenic bacteria in planktonic phase as well as in later phases of biofilm formation. The addition of TiO₂NP to PMMA resin used for dentures or other oral appliances will have a positive effect against microbial colonization [42].

Anehosur et al. (2012) found that the addition of 3 wt% TiO₂NP to PMMA produced a positive antimicrobial effect. It had the ability to reduce microbial number, which prevents quorum sensing thereby halts plaque formation on PMMA/TiO₂ nanocomposite surface [11]. Due to the photocatalytic property against microorganisms, patients will be able to maintain the hygiene of their dentures easily by exposing them to solar energy/light sources to activate the TiO₂NP [11]. On the same way, Alrahlah et al. (2018) reported a 50% and 90% decrease in bacterial cell attachment of E. faecalis and P. aeruginosa, respectively, with the mere addition of 3% TiO₂NP [43]. Likewise, Totu et al. (2017) investigated the effect of incorporating TiO₂NP into a 3D-printed PMMA denture in an attempt to improve denture antimicrobial characteristics and found that even the small addition of 0.4% of TiO₂NP to PMMA resulted in a nanocomposite that prevented the colonization of microorganisms and further formation of biofilm [24]. As a result, TiO₂NP could be incorporated into denture PMMA resin to successfully fabricate antimicrobial dentures [24]. The large active surface area of the nanoparticles compared to their small size makes them highly effective in low percentages of addition. It was found that as low as 0.4%, 1% and 2.5% TiO₂NP inhibited the growth of Candida. As reported in the literature, TiO₂NP caused a halt in the cellular enzymes and increased cell wall permeability causing cell death [44].

Few studies reported that the addition of as much as 5wt% TiO₂NP to the PMMA is needed to achieve the antimicrobial effect [45]. However, with this addition, structural decomposition and material weakening may occur [26].

1.4.2. Surface Properties

Surface microtopography of the denture is a very important feature in microbial adhesion and plaque formation and subsequently denture stomatitis.

(1) Surface Roughness. Denture wearers have high prevalence of poor oral health. This is mostly caused by the surface contours of the dentures and the irregularities of the oral mucosa [45]. Many factors were found to have an effect on the surface roughness () of denture bases, one of which is the reinforcing material of the acrylic resin [46]. Alwan and Alameer (2015) found an increase in surface roughness with the addition of 3wt% of TiO₂NP to PMMA denture base material and attributed this increase to the presence of nanoparticles on the surface of specimens [18].

To establish a relation between contact angle (wetting) and the amount of TiO₂NP filler in the PMMA resin, Hashem et al. (2017) found that it is dependent on filler amount. The addition of 1wt% TiO₂NP led to a reduction in surface wetting while the addition of more filler improved wetting. This finding confirms the effect of fillers on the surface of composite material compared to the pure counterpart [22].

While few investigations were made on surface roughness of PMMA/TiO₂ nanocomposite, a significant increase was reported compared to pure PMMA [18]. As the surface gets rougher and values increase, the surface area increases, meaning more sites are available for microbial adhesion and colonization. One of the most common organisms to be harbored on the surface of acrylic denture bases is C. Albicans [47]. Studies have reported that the surface roughness of a denture should not exceed 0.2 μm [45]. Although there is a direct relation between surface roughness and candida adhesion (increased roughness increases candida adhesion), the reduction in candida count confirms the antifungal properties of TiO₂NP.

(2) Hardness. Reports have confirmed that TiO₂NP improved the hardness of heat cure PMMA [10, 18]. Xia et al. (2008) attributed the increase in surface hardness to two factors: proper filler content and use of silane-coupling agent which increases the bonding between filler and resin matrix [48]. The effect on surface hardness was detected with additions of TiO₂NP as low as 1% [21]. In another study investigating the addition of 0.5%, 1%, and 2%, hardness values were found to increase with the addition and the highest values were seen with 2wt% TiO₂. Mosalman et al. (2017) related this to increased number of bonds between matrix and fillers, which requires more energy to break these bonds [49]. Hashem et al. (2017) reported an increase in hardness values that reached 20%, 30%, and 34% more than pure PMMA with 1%, 2%, and 3% TiO₂NP, respectively. This was explained by the increase in material stiffness due to presence of rigid particles within the matrix in addition to reduction of matrix mobility [22].

Alwan and Alameer (2015) concluded that 3% addition of TiO₂ caused a significant increase in surface hardness compared to pure PMMA [18] while Ahmed et al. (2016) suggested the need of adding 5% TiO₂NP to increase surface hardness of conventional and high impact heat cure acrylic resin to remarkable values [19]. More recently, Alrahlah et al. (2018) confirmed the increase in surface hardness of up to 35% with 3% TiO₂NP addition. The values of the hardness measurements were higher at the surface of the composite resin and decreased as we move inward toward the core of the material, suggesting higher crosslinking at the surface [43]. Regarding selection of the most appropriate concentration of filler for inclusion within denture resin, results of multicriteria decision making (MCDM) method suggested that a filler content in the range of 2wt% would create a composite material with improved mechanical properties including surface hardness [34].

1.4.3. Mechanical Properties

(1) Flexural Properties. During function, oral appliances including dentures are exposed to a magnitude of deforming stresses and any factor that increases the deformation of the denture base may lead to fracture [17]. One of the factors that may change the amount of denture deformation is the additive into the PMMA resin. The effect of TiO2NP addition on flexural strength of PMMA is partially dependent on the type of acrylics and the concentration of nanoparticles [19]. In 2013, Sodagar et al. investigated the effect of adding 0.5% and 1% TiO2NP into PMMA and reported a decrease in flexural strength. PMMA containing 0.5wt% showed the lowest values. It was concluded that there is an inverse relation between the concentration of the filler and the flexural strength of reinforced PMMA [12]. Han et al. (2008) reached the same conclusion and related the results to agglomeration of particles within the matrix, which makes them stress concentrations areas [50]. Other studies also reported a reduction in flexural strength [13, 19, 32] and modulus of elasticity [51] with the addition of TiO₂NP. Hamouda et al. (2014) found that TiO₂NP caused a reduction in flexural strength with no change in flexural modulus [13]. In the same token, Nazirkar et al. in (2014) were exploring the effect of adding TiO₂NP into heat cure acrylic resin on antimicrobial properties and reported an adverse effect on flexural strength of the final product [32].

In contrast to previous studies, superior flexural properties were reported with different concentrations of TiO₂NP added to PMMA than those of normal PMMA [10, 18, 21, 52]. This improvement may be attributed to the effect of silanization of TiO₂NP [18] or the good dispersion of fillers within the matrix, which improves modulus, transverse strength, and ductility [18, 52]. Hashem et al. (2017) found that, with 0.5–3wt% TiO₂NP addition, flexural strength and modulus increased. Moreover, they suggested that reinforced PMMA could offer superior chemical and mechanical properties making it a better option for dentures than pure PMMA resin [22]. On the same way, Rashahmadi et al. (2017) found that the mere addition of 0.5% TiO₂NP improved the flexural strength and Young’s modulus by 4%. Based on MCDM results, TiO₂NP addition to PMMA is an excellent option for improving properties of PMMA for dental applications especially in 2wt% concentration [34]. In a recent study by Karci et al. (2018), [16] different types (heat- auto-, and microwave polymerized) of acrylic mixed with 1%, 3%, and 5% nanotio2 were used to test the flexural strength of the resulting composite. That study came to a conclusion that the addition of 1% TiO₂NP to heat- and autopolymerized acrylic could improve the flexural strength while it remained unchanged with 3% TiO₂NP and decreased with 5% for all types of acrylic. This was explained by the increase in agglomeration of nanoparticles at higher addition percentages.

In a study by Mosalman et al. (2017), various percentages of TiO₂NP (0.5, 1, and 2wt %) were added to pure PMMA and found that the flexural strength of all groups stayed unchanged. Samples with 0.5wt% TiO₂NP showed only 3.75% improvement in flexural strength compared to pure PMMA. Young’s modulus for all groups was improved with the highest value seen in samples containing 2wt% TiO₂NP [49].

(2) Impact Strength. With regard to impact strength, the addition of TiO₂NP to heat cured acrylic resin resulted in a positive effect compared to pure PMMA [18]. Studies have confirmed this finding with different concentrations of TiO₂NP, including 1% [19, 23], 2wt%[34, 49], and 3wt% [25]. The same finding was reported after the addition of silanized TiO₂NP [53]. The detected increase in impact strength was justified by good bonding between PMMA matrix and TiO₂ nanofillers. These fillers reside in small voids between polymer chains and result in slow segmental motion. Also, they provide large surface area due to their small size, which helps in energy dissipation [25]. Others suggested that the nanofillers in the acrylic resin tolerate most of the applied load while the resin matrix helps in structural integrity and load distribution, which eventually inhibits crack propagation [23].

(3) Tensile Strength. Shirkavand and Moslehifard (2014) investigated the effect of 0.5wt%, 1wt%, and 2wt% TiO₂NP on tensile strength of PMMA base resins and found that the tensile strength of nanocomposite was the highest with 1wt% TiO₂NP and the improvement was 35% more compared to pure PMMA. However, further increase in TiO₂NP content led to an adverse effect [15] due to clustering of TiO₂NP. The fillers work as impurities and act as defects and stress concentration centers [15, 49]. The same results were also reported by Ghaheremani et al. (2017) [23]. The increase in tensile strength is probably attributed to the fact that, following the incorporation of nanoparticles into acrylic powder, the applied load is mainly tolerated by these nanoparticles.

Contrary to previous studies, Chatterjee in 2010 found that nanocomposite with filler content as high as 5wt% and 15wt% had a 59% and 95% increase in tensile modulus, respectively, compared to that of pure PMMA [9]. This was caused by the strong adhesion between TiO₂NP and PMMA. The applied load is transferred through these interfacial surfaces to the strongest material that is the nanoparticles [9].

1.4.4. Color Stability

It is noteworthy that the reinforcing filler material should ideally improve the mechanical properties without causing an adverse reaction to the aesthetics [25, 41]. TiO₂NP have whitish color; therefore, the appropriate percentage of this additive that fulfills the aforementioned requirement should be considered. An objective evaluation of the color change is usually done using a spectrophotometer where the difference between light absorption between different samples is calculated [28]. Aziz in 2018 evaluated the color change after adding 3wt% of TiO₂NP and found that the amount of light absorbed increased making the reinforced specimens more opaque compared to pure PMMA. This change was due to the presence of TiO₂NP within the matrix, which absorbs more light than polymer matrix due high atomic number [25]. Further studies are required to determine the proper TiO₂NP percentage needed to attain a PMMA/TiO₂ nanocomposite with superior properties and acceptable aesthetics.

1.4.5. Water Sorption, Solubility, and Porosity

Conventional acrylic resins have voids and porosities that allow water molecules exchange which could be the leading cause for water sorption and solubility [18]. The nature of denture resin material allows it to absorb water, which acts as a plasticizer and affects the material dimensional stability and denture durability [41]. The water molecules force themselves between polymer chains, move them apart, create internal stresses, and result in crack formation [29]. As reported by Alwan and Alameer [18], the addition of TiO₂NP to heat cure acrylic resin decreases water sorption and solubility significantly compared to pure PMMA. Torres et al. (2011) concluded that PMMA-TiO₂-Fe₂O₃ nanocomposites had lower sorption and porosity values compared to pure PMMA but similar solubility levels. However, the solubility levels were originally low, which is important to prevent the adverse effects on oral structures or polymer functions [41]. Also, as the material gets more homogenous, it becomes less soluble with lower water sorption levels [29].

Therefore, the addition of TiO₂NP fills the microvoids and polymer interstitial spaces decreasing the ability of composite material to absorb water. In addition to that TiO₂NP are insoluble in water and these particles partly replace the hydrophilic matrix, which decreases water uptake. The use of silane-coupling agent in silanization process of TiO₂NP could lead to a reduction in the amount of water that reaches the inner layers of polymer matrix [18].

1.4.6. Thermal Properties

The addition of 3% TiO₂NP to PMMA had no effect on thermal conductivity [25]. The glass transition temperature () test is done to understand the thermal stability and determine the temperature at which the material starts to degrade. As the percentage of TiO₂NP increases, the of nanocomposite increases linearly up to 7.5wt% TiO₂. Pure PMMA is stable up to 134°C (1% weight loss) while PMMA/2wt%TiO₂ and PMMA/5wt%TiO₂ are stable up to 154°C and 180°C, respectively. was improved by 15%–34% with 2%–5% addition of TiO₂NP, respectively. However, further addition of TiO₂NP caused a decrease in thermal stability [33]. Another study by Safi (2014) reported the positive effect of TiO₂NP addition on the temperature of acrylic resin [51]. In a recent study [43], authors evaluated the effect of adding 1%, 2%, and 3% TiO₂NP to PMMA on thermal behavior and found a slight effect on , degradation temperature, and rate.

Chatterjee (2010) in another study reported that the addition of 5wt% TiO₂NP caused a 23% increase in and this improvement reached only 3% when the amount of TiO₂NP was increased to 15% [9]. Also, pure PMMA showed 5% weight loss at 217°C while a higher temperature (310°C) was needed to create the same effect in the PMMA/5wt%TiO₂ [9]. Recently, Totu et al. (2018) [14] confirmed the increase in decomposition temperature for PMMA/TiO₂NP composite suggesting an improved thermal stability. This may be explained by the reduced intercrystalline distance, interaction, and bond formation between nanoparticles and polymer chains or the absorption of some energy by the titania particles increasing the thermal stability. Final decomposition of the PMMA/TiO₂NP composite happened at temperatures 620-700°C with decreasing pattern of the total mass loss as the amount of nanoparticles increased.

The thermal stability of TiO₂NP added to PMMA inhibits the degradation of the resin and improves the thermal stability of the composite material [33]. Another explanation for thermal stability is the migration of TiO₂NP with low surface energy to the surface of the PMMA resin to form a heat resistant layer [9]. The decrease in thermal stability with higher amount of nanofiller may be attributed to the agglomeration of filler particles rather than forming a filler-to-matrix interaction. This agglomeration reduces the effect of heat retardation associated with TiO₂NP [33]. TiO₂NP crystalline phase has free electrons that can be associated with surface reactions. Oxygen that diffused in the nanocomposite samples was absorbed on the surface of TiO₂NP. Hence, diffused oxygen amount in the PMMA matrix was lower than in pure PMMA, which led to the slower thermooxidative degradation of the PMMA matrix [9, 33].

It is knows that PMMA shrinks upon polymerization causing dimensional changes in the final product. Dimensional stability is also affected by coefficient of thermal expansion. The result of a study by Hashem et al. (2017)[22] showed that pure PMMA and PMMA/3%TiO₂ started to disintegrate and lose weight at 200°C with 90% weight loss happening at 400°C for both materials, suggesting no significant effect of TiO₂NP on the melting temperature of the composite material. This might be explained by the minimal amount of filler addition or the presence of large number of decomposition sites within the material [22].

1.4.7. Viscoelastic Behavior

Little work has been done on the effects of TiO₂NP on the viscoelastic behavior (creep-recovery and relaxation) behavior of PMMA matrix. Recently, in a study by Alrahlah done to investigate viscoelastic properties of TiO₂NP-modified PMMA denture base composite, it was found that the creep-recovery and relaxation behaviors of PMMA were significantly improved due to the addition of TiO₂NP. Also, the improvement further increased as the concentration of the nanofiller changed from 1% to 3%. This improvement in the behavior indicates the role of the nanoparticles in increasing the stiffness of the PMMA matrix owing to the reduction in its molecular mobility and free volume [43].

1.4.8. Electrical Behavior

It is imperative to avoid prolonged contact between oral mucosa and materials with high electrical conductivity. Metallic particles present in restorative materials my produce a galvanic effect in the highly conductive oral environment causing oral discomfort, changes in cell proliferation, and immune markers [27, 54]. Totu and colleagues (2018) [55] studied the effect of adding different percentages of TiO₂NP (0% (control), 0.2%, 0.4%, 0.6%, 1.0%, 2.0%, 2.5%, and 5%) to PMMA used for 3D printing on the electrical properties of the resulting nanocomposite. They reported a decrease in material resistance with the additions of ≥1% TiO₂NP. Also, an increase in electrical conductivity was noted with the addition of 5% TiO₂NP. However, the composite material still maintained its insulating property.

2. Overall Performance and Clinical Significance

It is well understood that advancements in biomaterial science affect the progression of technologies in any field including dental prostheses. The introduction of nanomaterials had significantly changed the clinical and technological aspects of dentistry. In this paper, the latest research progress on the applications of TiO₂NP in prosthodontics was reviewed. It clearly shows varying responses of physical and mechanical properties of the modified materials where a number of properties improved, others deteriorated, and few did not change. Their level of effectiveness as shown in the literature is diverse, being more or less effective than pure materials. Therefore, to attain removable prostheses with improved properties and acceptable clinical performance, the material of manufacture (acrylic resin) can be enhanced by adding proper percentage of nanofiller, initial surface treatment of the nanoparticles, and appropriate selection of addition method. Authors hope that this review article would provide some valuable elicitation for future scientific and technological innovations in the related field.

Based on this review, TiO₂NP were found to be enhancers in some aspects, modifiers in some, and insignificant in others. The effect depends mainly on NP size, addition method, surface treatment, and loading percentage. Although the size of NP ranged between 5 nm and 350 nm, the results of the studies were not justified based on the nanofiller size, and a clear link between size and effect was not established. For that, further investigations to relate the resulting properties to nanoparticle size are required.

Variations in the results were mainly related to filler mode of addition. The addition of nanoparticles to acrylic monomer was considered more effective owing to better dispersion of NP within the monomer. In this method, the dominant improvement was noticed in mechanical properties while physical properties were slightly affected. It is worth noting that with this technique the polymer: monomer ratio may be affected. Therefore, mixing the nanofiller with acrylic powder has been suggested and studied. Till now, no study can be found that compares between the effects of different modes of addition (nanofillers addition to powder or monomer). Based on this review, further investigations of the above-mentioned point are necessary as well as the proper way to establish the proportion of polymer/monomer ratio for each method; hence nanofiller addition interferes with the manufacture’s recommended ratios.

The percentage of addition also plays a role in resulting properties. While the range of addition was very broad (0.5–30wt%), low percentages resulted in improved properties compared to higher percentages. Simple addition of 1–2wt% ratios exhibited improved properties, while increasing the filler content more than 5wt% significantly weakened the final nanocomposites. In fact, the bonding between TiO₂NP and resin matrix is a critical factor to achieve the desired properties of nanocomposite. As showed in Table 1, the treatment of NP with saline coupling agents improved the properties in comparison to untreated particles. Therefore, NP surface treatment is recommended.

According to Table 1, inconsistencies in prepared specimen sizes for the same test were seen, which may have contributed to variations in the results between studies experimenting with the same filler percentage. This reflects a major error in the methodologies of the studies where the test should have been done according to standardized specimens’ dimensions and testing procedures. Testing should follow an internationally accepted standardization protocol like the ADA specifications for denture base polymers to make it possible to compare results between different studies.

Titanium nanoparticles remain under focus because of the antimicrobial efficacy against candida species despite their negative effect on a number of properties. Incorporation of TiO₂NP into PMMA matrix proved to have antimicrobial effects, specifically on candida species [24]. Not to be lost in this discussion is the effect of TiO₂NP surface modification on antimicrobial properties of the final product. It was shown that modification with noble metals such as (Ag, Au, Pt, and Pd) on TiO₂NP surface enhanced the photocatalytic ability of the nanoparticles and bactericidal activity thereafter [12].

Even with this number of studies on recently introduced TiO₂NP into PMMA, no clear evidence on the clinical applicability of this nanocomposite has been demonstrated. Further investigations are required to interpret and confirm the chemical structure changes in PMMA/TiO₂ nanocomposite and also to determine the need from otherwise for surface treatment as well as the proper percentage of addition that will not affect the final product adversely.

Research to improve upon existing nanomaterials is still ongoing with emphasis on efficiency. Although the science behind nanotechnology is intriguing, the lack of long-term evidence addressing their clinical performance restricts their wide clinical use. Overall, there is an essential requirement to investigate the durability of these PMMA/TiO₂ composites in different environmental conditions to extend the applicability of these hybrid materials.

3. Conclusion

Based on the current review, we could conclude that the addition of TiO₂NP to PMMA denture bases is still questionable for working as a reinforcing material and requires further investigations following the ADA specifications. These investigations must explore the chemical and structural changes happening in the nanocomposite after TiO₂ addition. The improvements in properties mentioned above were dominantly seen with lower concentrations of TiO₂ and the increase in the amount of added nanoparticles caused adverse effects on resulting PMMA/TiO₂ composite.

In conclusion, there is an essential need to investigate the clinical performance and durability of these nanocomposites in different conditions simulating the oral environment to verify their applicability and provide an insight of possible future researches in this field.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

References

R. L. Sakaguchi and J. M. Powers, Craig's Restorative Dental Materials, Elsevier Health Sciences, Philadelphia, PA, USA, pp. 163-176, 2012.
N. Murakami, N. Wakabayashi, R. Matsushima, A. Kishida, and Y. Igarashi, “Effect of high-pressure polymerization on mechanical properties of PMMA denture base resin,” Journal of the Mechanical Behavior of Biomedical Materials, vol. 20, pp. 98–104, 2013.
View at: Publisher Site | Google Scholar
R. Adhikari and G. H. Michler, “Polymer nanocomposites characterization by microscopy,” Polymer Reviews, vol. 49, no. 3, pp. 141–180, 2009.
View at: Publisher Site | Google Scholar
A. Navidfar, T. Azdast, and A. Karimzad Ghavidel, “Influence of processing condition and carbon nanotube on mechanical properties of injection molded multi-walled carbon nanotube/poly(methyl methacrylate) nanocomposites,” Journal of Applied Polymer Science, vol. 133, no. 31, Article ID 43738, pp. 1–9, 2016.
View at: Google Scholar
P. Chaijareenont, H. Takahashi, N. Nishiyama, and M. Arksornnukit, “Effect of different amounts of 3-methacryloxypropyltrimethoxysilane on the flexural properties and wear resistance of alumina reinforced PMMA,” Dental Materials, vol. 31, no. 4, pp. 623–628, 2012.
View at: Publisher Site | Google Scholar
J. Jordan, K. I. Jacob, R. Tannenbaum, M. A. Sharaf, and I. Jasiuk, “Experimental trends in polymer nanocomposites—a review,” Materials Science and Engineering: A, vol. 393, no. 1-2, pp. 1–11, 2005.
View at: Publisher Site | Google Scholar
M. M. Gad, S. M. Fouda, F. A. Al-Harbi, R. Näpänkangas, and A. Raustia, “PMMA denture base material enhancement: A review of fiber, filler, and nanofiller addition,” International Journal of Nanomedicine, vol. 12, pp. 3801–3812, 2017.
View at: Publisher Site | Google Scholar
F. Li, S. Zhou, B. You, and L. Wu, “Kinetic study on the UV-induced photopolymerization of epoxy acrylate/TiO2 nanocomposites by FTIR spectroscopy,” Journal of Applied Polymer Science, vol. 99, no. 6, pp. 3281–3287, 2006.
View at: Publisher Site | Google Scholar
A. Chatterjee, “Properties improvement of PMMA using nano TiO2,” Journal of Applied Polymer Science, vol. 118, no. 5, pp. 2890–2897, 2010.
View at: Publisher Site | Google Scholar
P. Harini, K. Mohamed, and T. V. Padmanabhan, “Effect of Titanium dioxide nanoparticles on the flexural strength of polymethylmethacrylate: An in vitro study,” Indian Journal of Dental Research, vol. 25, no. 4, pp. 459–463, 2014.
View at: Publisher Site | Google Scholar
G. Venkatesh Anehosur, R. D. Kulkarni, M. G. Naik et al., “Synthesis and Determination of Antimicrobial Activity of Visible Light Activated TiO2 Nanoparticles with Polymethyl Methacrylate Denture Base Resin Against Staphylococcus Aureus,” Journal of Gerontology & Geriatric Research, vol. 01, no. 01, pp. 103–111, 2012.
View at: Publisher Site | Google Scholar
A. Sodagar, A. Bahador, S. Khalil, A. Saffar Shahroudi, and M. Zaman Kassaee, “The effect of TiO₂ and SiO₂ nanoparticles on flexural strength of poly (methyl methacrylate) acrylic resins,” Journal of Prosthodontic Research, vol. 57, no. 1, pp. 15–19, 2013.
View at: Publisher Site | Google Scholar
I. M. Hamouda and M. M. Beyari, “Addition of glass fibers and titanium dioxide nanoparticles to the acrylic resin denture base material: comparative study with the conventional and high impact types,” Oral Health and Dental Management, vol. 13, pp. 107–112, 2014.
View at: Google Scholar
E. E. Totu, C. M. Cristache, E. Voicila et al., “On physical and chemical characteristics of Poly(methylmethacrylate) nanocomposites for dental applications. I.,” Materiale Plastice, vol. 54, no. 4, pp. 666–672, 2017.
View at: Google Scholar
S. Shirkavand and E. Moslehifard, “Effect of TiO2 nanoparticles on tensile strength of dental acrylic resins,” Journal of Dental Research, Dental Clinics, Dental Prospects, vol. 8, no. 4, pp. 197–203, 2014.
View at: Publisher Site | Google Scholar
M. Karci, N. Demir, and S. Yazman, “Evaluation of Flexural Strength of Different Denture Base Materials Reinforced with Different Nanoparticles,” Journal of Prosthodontics, 2018.
View at: Publisher Site | Google Scholar
O. Gurbuz, F. Unalan, and I. Dikbas, “Comparison of the transverse strength of six acrylic denture resins,” Ohdmbsc Magazines, vol. 9, pp. 21–24, 2010.
View at: Google Scholar
S. A. Alwan and S. S. Alameer, “The Effect of the Addition of Silanized Nano Titania Fillers on Some Physical and Mechanical Properties of Heat Cured Acrylic Denture Base Materials,” Journal of Baghdad College of Dentistry, vol. 27, no. 1, pp. 86–91, 2015.
View at: Publisher Site | Google Scholar
M. Ashour Ahmed, M. El-Shennawy, Y. M. Althomali, and A. A. Omar, “Effect of Titanium Dioxide Nano Particles Incorporation on Mechanical and Physical Properties on Two Different Types of Acrylic Resin Denture Base,” World Journal of Nanoscience and Engineering, vol. 06, no. 03, pp. 111–119, 2016.
View at: Publisher Site | Google Scholar
A. Sodagar, S. Khalil, M. Z. Kassaee, A. S. Shahroudi, B. Pourakbari, and A. Bahador, “Antimicrobial properties of poly (methyl methacrylate) acrylic resins incorporated with silicon dioxide and titanium dioxide nanoparticles on cariogenic bacteria,” Journal of Orthodontic Science, vol. 5, no. 1, pp. 7–13, 2016.
View at: Publisher Site | Google Scholar
M. A. Ahmed, A. A. Omar, M. El-Shennawy, M. I. Ebrahim, and Y. M. Althomali, “Influence of addition of different types of nano-fillers on the microstructure and mechanical properties of PMMA based denture resin,” Kasmera Journal, vol. 45, pp. 48–59, 2017.
View at: Google Scholar
M. Hashem, M. F. Al Rez, H. Fouad et al., “Influence of titanium oxide nanoparticles on the physical and thermomechanical behavior of poly methyl methacrylate (pmma): A denture base resin,” Science of Advanced Materials, vol. 9, no. 6, pp. 938–944, 2017.
View at: Publisher Site | Google Scholar
L. Ghahremani, S. Shirkavand, F. Akbari, and N. Sabzikari, “Tensile strength and impact strength of color modified acrylic resin reinforced with titanium dioxide nanoparticles,” Journal of Clinical and Experimental Dentistry, vol. 9, no. 5, pp. e661–e665, 2017.
View at: Google Scholar
E. E. Totu, A. C. Nechifor, G. Nechifor, H. Y. Aboul-Enein, and C. M. Cristache, “Poly(methyl methacrylate) with TiO2 nanoparticles inclusion for stereolitographic complete denture manufacturing − the fututre in dental care for elderly edentulous patients,” Journal of Dentistry, vol. 59, pp. 68–77, 2017.
View at: Publisher Site | Google Scholar
H. K. Aziz, “TiO-Nanofillers Effects on Some Properties of Highly- Impact Resin Using Different Processing Techniques,” The Open Dentistry Journal, vol. 12, no. 1, pp. 202–212, 2018.
View at: Publisher Site | Google Scholar
M. Tsuji, T. Ueda, K. Sawaki, M. Kawaguchi, and K. Sakurai, “Biocompatibility of a titanium dioxide-coating method for denture base acrylic resin,” Gerodontology, vol. 33, no. 4, pp. 539–544, 2016.
View at: Publisher Site | Google Scholar
S. Podzimek, M. Tomka, P. Sommerova, Y. Lyuya-Mi, J. Bartova, and J. Prochazkova, “Immune markers in oral discomfort patients before and after elimination of oral galvanism,” Neuroendocrinology Letters, vol. 34, no. 8, pp. 802–808, 2013.
View at: Google Scholar
S. Kiat-amnuay, M. Beerbower, J. M. Powers, and R. D. Paravina, “Influence of pigments and opacifiers on color stability of silicone maxillofacial elastomer,” Journal of Dentistry, vol. 37, no. 1, pp. e45–e50, 2009.
View at: Publisher Site | Google Scholar
S. H. Tuna, F. Keyf, H. O. Gumus, and C. Uzun, “The evaluation of water sorption/solubility of various acrylic resins,” European Journal of Dental Education, vol. 2, pp. 191–197, 2008.
View at: Google Scholar
S. M. Khaled, R. Sui, P. A. Charpentier, and A. S. Rizkalla, “Synthesis of TiO₂-PMMA nanocomposite: using methacrylic acid as a coupling agent,” Langmuir, vol. 23, no. 7, pp. 3988–3995, 2007.
View at: Publisher Site | Google Scholar
L. Reijnders, “The release of TiO2 and SiO2 nanoparticles from nanocomposites,” Polymer Degradation and Stability, vol. 94, no. 5, pp. 873–876, 2009.
View at: Publisher Site | Google Scholar
G. Nazirkar, S. Bhanushali, S. Singh, B. Pattanaik, and N. Raj, “Effect of Anatase Titanium Dioxide Nanoparticles on the Flexural Strength of Heat Cured Poly Methyl Methacrylate Resins: An In-Vitro Study,” Journal of Indian Prosthodontist Society, vol. 14, pp. 144–149, 2014.
View at: Google Scholar
A. Chatterjee, “Effect of nanoTiO₂ addition on poly(methyl methacrylate): an exciting nanocomposite,” Journal of Applied Polymer Science, vol. 116, no. 6, pp. 3396–3407, 2010.
View at: Publisher Site | Google Scholar
S. Rashahmadi, R. Hasanzadeh, and S. Mosalman, “Improving the Mechanical Properties of Poly Methyl Methacrylate Nanocomposites for Dentistry Applications Reinforced with Different Nanoparticles,” Polymer—Plastics Technology and Engineering, vol. 56, no. 16, pp. 1730–1740, 2017.
View at: Publisher Site | Google Scholar
A. H. Yuwono, B. Liu, J. Xue et al., “Controlling the crystallinity and nonlinear optical properties of transparent TiO₂-PMMA nanohybrids,” Journal of Materials Chemistry, vol. 14, no. 20, pp. 2978–2987, 2004.
View at: Publisher Site | Google Scholar
J. K. Pandey, K. Raghunatha Reddy, A. P. Kumar, and R. P. Singh, “An overview on the degradability of polymer nanocomposites,” Polymer Degradation and Stability, vol. 88, no. 2, pp. 234–250, 2005.
View at: Publisher Site | Google Scholar
C. Tao, S. Jianping, J. Weng, L. Ting, and H. Xiaozhu, “Preparation and properties of PMMA/TiO2 nanocomposite,” Chemical Reaction Engineering and Technology, vol. 23, pp. 435–440, 2007.
View at: Google Scholar
A. H. Yuwono, J. Xue, J. Wang et al., “Transparent nanohybrids of nanocrystalline TiO2 in PMMA with unique nonlinear optical behavior,” Journal of Materials Chemistry, vol. 13, no. 6, pp. 1475–1479, 2003.
View at: Publisher Site | Google Scholar
R. Alla, K. N. Raghavendra, R. Vyas, and A. Konakanchi, “Conventional and contemporary polymers for the fabrication of denture prosthesis: Part I overview, composition and properties,” International Journal of Applied Dental Sciences, vol. 1, no. Part I, pp. 82–89, 2015.
View at: Google Scholar
C. C. Trapalis, P. Keivanidis, G. Kordas et al., “TiO2(Fe³⁺) nanostructured thin films with antibacterial properties,” Thin Solid Films, vol. 433, no. 1-2, pp. 186–190, 2003.
View at: Publisher Site | Google Scholar
L. S. Acosta-Torres, L. M. López-Marín, R. E. Núñez-Anita, G. Hernández-Padrón, and V. M. Castaño, “Biocompatible Metal-Oxide Nanoparticles: Nanotechnology Improvement of Conventional Prosthetic Acrylic Resins,” Journal of Nanomaterials, vol. 2011, Article ID 941561, 8 pages, 2011.
View at: Publisher Site | Google Scholar
A. Bahador, S. Khalil, B. Pourakbari et al., “Photocatalytic Effects of Acrylic Resins Incorporated with Nano-titanium Dioxide on Planktonic and Biofilm Growth of Four Cariogenic Bacteria,” Annual Research & Review in Biology, vol. 4, no. 17, pp. 2695–2708, 2014.
View at: Publisher Site | Google Scholar
A. Alrahlah, H. Fouad, M. Hashem, A. Niazy, and A. AlBadah, “Titanium Oxide (TiO2)/Polymethylmethacrylate (PMMA) Denture Base Nanocomposites: Mechanical, Viscoelastic and Antibacterial Behavior,” Materials, vol. 11, no. 7, Article ID 1096, pp. 1096:1–1096:15, 2018.
View at: Publisher Site | Google Scholar
A. Kubacka, M. Ferrer, M. L. Cerrada et al., “Boosting TiO2-anatase antimicrobial activity: Polymer-oxide thin films,” Applied Catalysis B: Environmental, vol. 89, no. 3-4, pp. 441–447, 2009.
View at: Publisher Site | Google Scholar
Y. Cheng, T. Sakai, R. Moroi et al., “Self-cleaning ability of a photocatalyst-containing denture base material,” Dental Materials, vol. 27, no. 2, pp. 179–186, 2008.
View at: Publisher Site | Google Scholar
C. M. Bollen, P. Lambrechts, and M. Quirynen, “Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: a review of the literature,” Dental Materials, vol. 13, no. 4, pp. 258–269, 1997.
View at: Publisher Site | Google Scholar
N. Elshereksi, M. Ghazali, A. Muchtar, and C. Azhari, “Effect of nanobarium titanate addition on the surface characteristics of denture base resin,” International Journal of Mechanical and Production Engineering, vol. 5, pp. 1–8, 2017.
View at: Publisher Site | Google Scholar
Y. Xia, Z. Feimin, H. Xie, and N. Gu, “Nanoparticles reinforced resin based dental composites,” Journal of Dentistry, vol. 36, pp. 450–455, 2008.
View at: Google Scholar
S. Mosalman, S. Rashahmadi, and R. Hasanzadeh, “The effect of TiO2 nanoparticles on mechanical properties of poly methyl methacrylate nanocomposites,” International Journal of Engineering, Transactions B: Applications, vol. 30, no. 5, pp. 807–813, 2017.
View at: Google Scholar
Y. Han, S. Kiat-amnuay, J. M. Powers, and Y. Zhao, “Effect of nano-oxide concentration on the mechanical properties of a maxillofacial silicone elastomer,” The Journal of Prosthetic Dentistry, vol. 100, no. 6, pp. 465–473, 2008.
View at: Publisher Site | Google Scholar
I. N. Safi, “Evaluation the effect of nano—fillers (TiO₂ , AL₂O₃ , SiO₂) addition on glass transition temperature, E-moudulus and coefficient of thermal expansion of acrylic denture base material,” Journal of Baghdad College of Dentistry, vol. 26, no. 1, pp. 37–41, 2014.
View at: Publisher Site | Google Scholar
W. Wang, S. Liao, Y. Zhu, M. Liu, Q. Zhao, and Y. Fu, “Recent Applications of Nanomaterials in Prosthodontics,” Journal of Nanomaterials, vol. 2015, Article ID 408643, 11 pages, 2015.
View at: Publisher Site | Google Scholar
L. Sun, R. F. Gibson, F. Gordaninejad, and J. Suhr, “Energy absorption capability of nanocomposites: A review,” Composites Science and Technology, vol. 69, no. 14, pp. 2392–2409, 2009.
View at: Publisher Site | Google Scholar
Š. Podzimek, K. Hána, M. Mikšovský et al., “The Influence of galvanic currents and voltage on the proliferation activity of lymphocytes and expression of cell surface molecules,” Folia Biologica, vol. 54, no. 5, pp. 146–150, 2008.
View at: Google Scholar
E. E. Totu, E. Voicila, V. Pistritu, G. Nechifor, and C. M. Cristache, “Evaluation of electrical characteristics for PMMA-TiO2 nanocomposites used in dentistry,” Evista de Chimie, vol. 69, no. 1, pp. 155–159, 2018.
View at: Google Scholar

Copyright

Copyright © 2019 Mohammed M. Gad and Reem Abualsaud. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

8099

Downloads

3176

Citations