Influence of Breast Implant Surface Finishing on Physicochemical and Mechanical Properties before and after Extreme Degradation Studies
Table 3
Mechanical properties for samples as received and after acidic and basic degradation.
| Roughness | Smooth membranes | Rough membranes | Degradation | As received | Acidic | Basic | As received | Acidic | Basic |
| Mechanical strength (MPa) at 450% straina | 6.7 ± 0.5 | 7.6 ± 1.3 | 4.9 ± 1.6 | 5.3 ± 0.6 | 7.3 ± 1.2 | 6.0 ± 1.5 | Mechanical strength (MPa) at rupture | 9.2 ± 0.9 | 8.1 ± 0.9 | 5.2 ± 1.9 | 7.9 ± 1.5 | 8.0 ± 0.5 | 6.7 ± 2.7 | Deformation (%) at rupture | 556 ± 61 | 465 ± 48 | 416 ± 66 | 539 ± 119 | 473 ± 51 | 396 ± 147 |
|
|
aAverage of samples that reached 450% deformation.
|