Magnetron Sputtered NbN Films with Nb Interlayer on Mild Steel

<table class="table-group" id="tab4"><tr><td><table class="table"><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr class="thead"><td align="left">Biasing (−V)</td><td align="center">Lc<sub>1 </sub>(N)</td><td align="center">Lc<sub>2</sub> (N)</td></tr><tr><td class="thead-hr" colspan="3"><hr/></td></tr><tr><td align="left">0</td><td align="center">6.5</td><td align="center">10.5</td></tr><tr><td align="left">25</td><td align="center">10.5</td><td align="center">20</td></tr><tr><td align="left">50</td><td align="center">12.0</td><td align="center">24</td></tr><tr><td align="left">75</td><td align="center">15.6</td><td align="center">26</td></tr><tr><td align="left">100</td><td align="center">7.0</td><td align="center">11</td></tr><tr class="table-tr"><td colspan="3"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

Effect of biasing on critical loads during scratch tests for NbN coatings on SS.

International Journal of Corrosion

tab4

Table 4

Table 4: Magnetron Sputtered NbN Films with Nb Interlayer on Mild Steel 