Effect of Minor Alloying Elements on the Corrosion Behavior of Fe40Al in NaCl-KCl Molten Salts
Table 1
Electrochemical parameters obtained from polarization curves.
| Alloy | (mV/dec) | (mV/dec) | (mA/cm2) | (mV) |
| FeAl-base | 311 | 223 | 1.5 | −927 | FeAl-1Ag | 293 | 398 | 2.3 | −730 | FeAl-3Ag | 269 | 432 | 4.0 | −510 | FeAl-1Li | 159 | 65 | 0.5 | −363 | FeAl-3Li | 346 | 134 | 1.4 | −1212 | FeAl-3Cu | 169 | 180 | 1.4 | −1212 | FeAl-5Cu | 78 | 191 | 4 | −460 | FeAl-3Ni | 159 | 207 | 2.2 | −395 | FeAl-5Ni | 177 | 222 | 0.9 | −340 | 304SS | 243 | 311 | 10.4 | 125 |
|
|