Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions
Figure 12
The same sample as shown above at a slightly higher magnification revealing how the cracks followed the grinding marks on the sample after a slow strain-rate test at 45°C and 800 kPa 25% CO–75% CO2.