Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H<sub>2</sub>O–CO–CO<sub>2</sub> Solutions

<table>Slow strain-rate test results showing the influence of the surface roughness on the stress-corrosion resistance of steel at 45°C and 800 kPa.</table>

International Journal of Corrosion

fig14

Figure 14

Figure 14: Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H<sub>2</sub>O–CO–CO<sub>2</sub> Solutions 

International Journal of Corrosion

Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions

Figure 14

Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H₂O–CO–CO₂ Solutions