On the Stress Corrosion Cracking and Hydrogen Embrittlement Behavior of Austenitic Stainless Steels in Boiling Saturated Magnesium Chloride Solutions
Figure 3
(a) Transgranular cracking for type 304 at K, (b) intergranular cracking for type 304 austenitic stainless steel at K (x550), (c) transgranular cracking for type 316 austenitic stainless steel at K, (d) intergranular cracking for type 316 austenitic stainless steel at K (x550), and (e) transgranular cracking for type 310 austenitic stainless steel at K in boiling saturated MgCl2 solutions.