Determination of Susceptibility to Intergranular Corrosion of UNS 31803 Type Duplex Stainless Steel by Electrochemical Reactivation Method
Table 4
EDS analysis of phases present in solution-annealed and aged condition of DSS.
| Heat treatment | Phase | Cr (wt. %) | Ni (wt. %) | Mo (wt. %) | Mn (wt. %) | Si (wt. %) | S (wt. %) | Fe (wt. %) |
| Solutionannealed | General composition | 22.04 | 4.45 | 2.69 | 1.49 | 0.45 | 0.003 | 68.29 |
| Solution annealed | | 26.32 | 4.87 | 4.15 | 1.59 | 0.74 | — | 62.32 | | 23.55 | 7.08 | — | 1.85 | — | 1.19 | 66.33 |
| 725°C/31622 min | | 23.81 | 6.43 | — | — | — | — | 69.76 | | 35.21 | — | 7.21 | — | — | — | 57.58 | | 23.03 | 6.91 | — | — | 1.04 | 1.26 | 67.75 | | 18.65 | 5.21 | | | | | 76.14 |
|
|