The Effect of Applied Stress on Environment-Induced Cracking of Aluminum Alloy 5052-H3 in 0.5 M NaCl Solution

<table>The corrosion elongation curves for A5052-H3-LT at T = 353 K and <i>σ</i> = 240 MPa in 0.5 M sodium chloride solution.</table>

International Journal of Corrosion

Figure 2: The Effect of Applied Stress on Environment-Induced Cracking of Aluminum Alloy 5052-H3 in 0.5 M NaCl Solution 