Combating Corrosion Degradation of Turbine Materials Using HVOF Sprayed 25% (Cr3C2-25(Ni20Cr)) + NiCrAlY Coating
Figure 8
Plot of (weight gain/area)2 versus number of cycles for coated samples subjected to hot corrosion for 50 cycles in Na2SO4-50%V2O5 environment at 800°C. (a) Uncoated samples, (b) 25% (Cr3C2-25(Ni20Cr)) + NiCrAlY coated substrates. Multiplication factor for g2 cm−4 s−1).