Abstract

The fabricated macroporous silicon with a porosity of 26.33% corrosion in NaOH solution was systemically investigated by open circuit potential measurements, linear polarization measurements, potentiodynamic polarization measurements, and scanning electron microscopy, respectively. Results show that the potential open circuit and linear polarization resistance decreases with the NaOH concentration increasing. The corrosion potential shifts significantly to more negative potentials and corrosion current density increases with NaOH concentration increasing. Adding ethanol to 1.0 M NaOH can lead to the linear polarization resistance decrease, corrosion potentials shift in the positive direction, and corrosion current density increase. In addition, the scanning electron microscopy images demonstrate that the macroporous silicon samples are seriously damaged by 1.0 M NaOH and 1.0 M NaOH/EtOH (30%).

1. Introduction

Porous silicon (PS), formed on the surface of crystalline silicon substrates by electrochemical anodization in hydrofluoric acid, was firstly observed by Uhlir in 1956 at the Bell Labs during the investigation of electrochemical methods for polishing germanium and silicon wafers [1]. Owing to the various potential applications in electronics and optoelectronics fields, the striking photoluminescence properties of PS at room temperature have attracted considerable research interest since their discovery in 1990 by Canham [2]. Over the past two decades, the fabrication methods, morphologies, microstructures, and optoelectronic properties of PS have been improved enormously.

At present, with numerous unique features, such as the high specific surface area, convenient surface chemistry, significant optical properties and electronic properties, biocompatibility, biodegradability, bioresorbability, and low toxicity, the PS has been applied in electronics, photonics, and biosensing [37] and used as an insulating layer in the silicon-on-insulator applications, a sensing layer in biosensors or chemical sensors, an energy carrier, and a sacrificial layer in micromachining, as an important material for solar cell, and as an excellent biomaterial in tissue engineering, tumor imaging, and bioreactor platform drug delivery [813].

However, there are few works focusing on researching about the applications of PS in alkaline solutions resulting from the dissolution/corrosion of PS in these solutions [1417]. According to our previous works [1820], although the corrosion of PS in NaOH, KOH, and (CH3)4NOH was studied by weight loss measurements, there are few works focusing on the investigation of PS corrosion in alkaline solutions using open circuit potential measurements, linear polarization measurements, and potentiodynamic polarization measurements.

Considering the importance of electrochemical parameters of PS corrosion in alkaline solutions, the aim of the present work is to report the corrosion behavior of macroporous silicon in NaOH solution by electrochemical methods. Firstly, several macroporous silicon samples were fabricated. Then, the corrosion behavior of macroporous silicon in NaOH solution without and with ethanol (EtOH) was systemically studied using open circuit potential measurements, linear polarization measurements, potentiodynamic polarization measurements, and scanning electron microscopy.

2. Experimental Details

2.1. Reagents and Materials

Hydrofluoric acid (40%, A. R., HF), ethanol (99.5%, A. R., EtOH), acetone (A. R.), and sodium hydroxide (A. R., NaOH) were purchased from Sinopharm Chemical Reagent Co., Ltd. All the reagents were commercially available and used without further purification. The silicon substrate of silicon wafers was purchased from Emei Semiconductor Material Institute (China), which was a phosphorus doped n-type wafer with a resistivity of 2–4 Ω cm, 500–550 μm thick and (100) oriented.

2.2. Preparation of Macroporous Silicon

Porous silicon (PS) samples were fabricated by electrochemical anodization of n-type silicon wafers in the etching solution of HF (40%) : EtOH (99.5%) = 1 : 1 at a current density of 30 mA cm−2 for 30 min [2123]. Anodization process was performed in a Teflon cell by using two-electrode configuration with Pt gauze as the cathode and silicon substrate as the anode. Meanwhile, the etching process was illuminated by a 150 W high pressure mercury lamp at a distance of 20 cm. After being prepared, the fresh PS samples were rinsed with double distilled water and ethanol. The most accepted model for describing etching mechanism for formation of PS has been proposed by Lehmann and Gösele [24]; in this model, the reaction of silicon etching to prepare PS is given in (1) [24, 25], where h+ and e represent hole and electron, respectively. Hence,

Based on the size of pore diameters, the fabricated PS can be divided into microporous silicon (≤2 nm), mesoporous silicon (2–50 nm), and macroporous silicon (>50 nm). According to the scanning electron microscopy analysis in Section 3.5, because of the pore diameter more than 50 nm, the prepared PS turns out to be macroporous silicon. Meanwhile, the porosity and thickness of macroporous silicon were estimated by weight loss measurements [26] using the optimized corrosion solution to completely rapidly remove the PS layer from PS samples [26]. The porosity and thickness of the prepared macroporous silicon are 26.33% and 144.10 μm, respectively.

2.3. Electrochemical Measurements

Electrochemical measurements were carried out by a conventional three-electrode cell that consisted of the macroporous silicon working electrode (0.95 cm2), a platinum gauze counter electrode, and a silver-silver chloride (Ag/AgCl) electrode as a reference electrode. The open circuit potential, linear polarization, and potentiodynamic polarization measurements were carried out using a computer to control CHI 660D Electrochemical Workstation (China) for investigating the electrochemical behavior of macroporous silicon in NaOH solution. According to our previous work [27], the whole schematic diagram of experimental setup for electrochemical measurements was shown in Figure 1.

It is generally required to stabilize the open circuit potential before running the linear polarization and potentiodynamic polarization measurements. Before measurements, the electrode was allowed to corrode freely and its open circuit potential was recorded as a function of time for 800 s. After this time a steady-state open circuit potential corresponding to the corrosion potential of the working electrode was obtained. As for linear polarization measurements, the potential of the electrode was scanned from −20 mV to +20 mV versus corrosion potential at scan rate of 0.166 mV s−1 and the polarization resistance was calculated from the slope of potential versus current curve in the vicinity of corrosion potential. Tafel polarization curves were obtained in the potential range of −800 mV to +800 mV in regard to open circuit potential. The corrosion current densities were estimated by extrapolation of the anodic and cathodic Tafel lines.

In this study, it should be noted that the electrochemical corrosion behavior of macroporous silicon in 1.0 M NaOH was investigated at a relative lower temperature of 291 K due to the existence of plenty of bubbles formed from the macroporous silicon in 1.0 M NaOH at the relative higher temperature, which would affect the accuracy of electrochemical measurements.

2.4. Scanning Electron Microscopy

The morphology images of macroporous silicon before and after electrochemical measurements in 1.0 M NaOH without and with 30% ethanol at 291 K were observed by scanning electron microscopy (SEM, JEOL JSM-6510).

3. Results and Discussion

3.1. Dissolution Chemistry

It is well known that different Si–Si bonds and various kinds of activated Si–H bonds present on macroporous silicon layer [20, 2628]. Meanwhile, both the macroporous silicon layer and silicon substrate (Si) can react with NaOH solution to form hydrogen gas (H2), which can be illustrated by (2) [20, 26, 29, 30]. The essence of corrosion/dissolution of macroporous silicon in NaOH solution is the reaction among macroporous silicon layer with various Si–H bonds, silicon substrate (Si) with different Si–Si bonds, and aqueous NaOH.

3.2. Open Circuit Potential Measurements

The open circuit potential-time curves of macroporous silicon corrosion in different concentrations of NaOH solution at 291 K are shown in Figure 2. It is evident from the graph that the increase of NaOH concentration finally caused a shift in the direction of negative potential. In 0.1 M NaOH, the curve shows a marked increase of potential towards positive direction, which indicates that the macroporous silicon electrode surface is oxidized by low concentration of NaOH solution. It takes about 600 s to reach the steady-state value about −1.020 V. In 0.2 M NaOH, the curve shows a slight increase of potential towards positive direction followed by sharp shift in lower values of potential. This demonstrates that the performed oxide layer on the electrode surface will be dissolved after macroporous silicon electrode immersion in 0.2 M NaOH. In 0.5 and 1.0 M NaOH, the curve shows a marked decrease of potential towards negative direction, which shows the corrosion of macroporous silicon in the higher concentration of NaOH (>0.5 M).

Meanwhile, the open circuit potential-time curves of macroporous silicon in 1.0 M NaOH with different volume ratios of ethanol (0~50%) at 291 K are shown in Figure 3. It can be found that the open circuit potential-time curves are obviously influenced by volume ratio of ethanol in 1.0 M NaOH. From Figure 3, the increase of volume ratio of ethanol in 1.0 M NaOH finally caused a shift in the direction of positive potential. All curves show a marked decrease of potential towards negative direction followed by sharp shift in higher values of potential after adding ethanol to NaOH. It takes about 100 s to reach the steady-state values, which indicates that addition of ethanol can shorten the stabilizing time of macroporous silicon in 1.0 M NaOH. This is due to the fact that adding ethanol to NaOH solution can decrease the surface tension of NaOH solution and increase wettability to the macroporous silicon sample surface, which are an advantage to the hydrogen gas overflow from the NaOH solution.

3.3. Linear Polarization Measurements

Figure 4 reveals the typical linear polarization curves of macroporous silicon corrosion in 1.0 M NaOH in the absence and presence of 30% ethanol (1.0 M NaOH/EtOH (30%)) at 291 K. Meanwhile, the linear polarization resistances (, Ω cm2) of macroporous silicon corrosion in different concentrations of NaOH and in 1.0 M NaOH with various volume ratios of ethanol are shown in Figures 5 and 6, respectively.

The linear polarization resistance of macroporous silicon corrosion in different concentrations of NaOH solution at 291 K is shown in Figure 5. This figure illustrates that the linear polarization resistance decreases with the NaOH concentration increasing, which indicates that the corrosion rate of macroporous silicon in NaOH solution increases with concentration of NaOH increasing. This confirms that the higher the NaOH concentration, the faster the corrosion rate. As seen in Figure 5, the linear polarization resistance sharply decreases with the concentration of NaOH increasing from 0.1 M to 0.2 M. Then, it decreases slightly. This result indicates that the oxidation of macroporous silicon is more obvious in low concentration of NaOH solution than that in high concentration of NaOH. Additionally, the corrosion and dissolution of macroporous silicon are more obvious in high concentration of NaOH solution than in low concentration of NaOH [20, 31].

The rapid decrease in linear polarization resistance can be attributed to the dissolution/corrosion of macroporous silicon in NaOH solution, which shows that the corrosion is the predominant process for macroporous silicon in high concentration of NaOH solution (>0.1 M) [20, 31]. Based on (2) and the above fact, it must be mentioned that lower NaOH concentration can increase the linear polarization resistance and reduce the corrosion rate of macroporous silicon in NaOH solution, and higher NaOH concentration can reduce the linear polarization resistance and increase the corrosion rate. Hence,

Figure 6 shows the relationship between the linear polarization resistance and the volume ratio of ethanol in 1.0 M NaOH at 291 K. The value of linear polarization resistance decreases with the volume ratio of ethanol increasing until reaching the minimum value of 1009.5 Ω cm2 (1.0 M NaOH/EtOH (30%)) and then increases with the volume ratio of ethanol further increasing. The result is well consistent with the fact that the solvent of H2O directly participated in the corrosion reaction of macroporous silicon as shown in (2) and the number of H2O molecules decreases with the increase of ethanol volume ratio in 1.0 M NaOH. The obvious decrease of linear polarization resistance indicates that the addition of ethanol can lead to the corrosion rate increase, possibly because ethanol can reduce the surface tension of NaOH solution and increase wettability of macroporous silicon surface [1820].

3.4. Potentiodynamic Polarization Measurements

At 291 K, the potentiodynamic polarization curves of macroporous silicon in NaOH solution in the absence and presence of ethanol are shown in Figures 7 and 8. Meanwhile, the electrochemical parameters of corrosion potential and corrosion current density for macroporous silicon in NaOH solution with and without ethanol were listed in Table 1.

From Figure 7 and Table 1, it can be found that the corrosion potential shifts significantly to more negative potentials and the corrosion current density increases with concentration of NaOH increasing. The result indicates that NaOH with high concentration can cause serious corrosion of macroporous silicon.

From Figure 8 and Table 1, it is shown that the addition of ethanol to 1.0 M NaOH can lead to the corrosion potentials shift in the positive direction and corrosion current density increases. The corrosion potential of macroporous silicon in 1.0 M NaOH, 1.0 M NaOH/EtOH (30%), and 1.0 M NaOH/EtOH (50%) is −1.474, −1.404, and −1.360 V, respectively. The significant increase of corrosion current density for macroporous silicon corrosion also indicates that the addition of ethanol to NaOH solution can increase the corrosion rate. This may be attributed to the decreasing of surface tension and increasing of wettability. The result obtained from potentiodynamic polarization measurements is in good agreement with linear polarization measurements, where the two different techniques gave the same trend of macroporous silicon corrosion in different concentrations of NaOH solution in the absence and presence of ethanol. Meanwhile, the obtained result is in good agreement with the weight loss measurements from the reported study [19, 20].

3.5. Scanning Electron Microscopy

The scanning electron microscopy (SEM) images of macroporous silicon before and after electrochemical measurements at 291 K are shown in Figures 9(a)9(d). These images give a comparison about the surface microstructures on macroporous silicon before corrosion and after corrosion in 1.0 M NaOH in the absence (c) and presence (d) of 30% EtOH. The SEM results show that the addition of ethanol to NaOH has a significant effect on the morphology of macroporous silicon. From Figure 9(a), a few pores and cracks can be seen on the surface of macroporous silicon prepared at the current density of 30 mA cm−2 for 30 min. According to the cross-sectional SEM images (Figure 9(b)), it can be found that the thickness of the porous layer is about 135–140 μm, which confirms the weight loss measurements results obtained from Section 2.2.

Along with the corrosion reaction, as can be seen, the samples (a, b) are seriously damaged and the porous structure (c, d) is clearly seen after electrochemical measurements in 1.0 M NaOH and 1.0 M NaOH/EtOH (30%), resulting in more pores exposed on the surface of macroporous silicon. The fabricated porous silicon turns out to be macroporous silicon for the average pore diameters of each porous silicon sample of about 1 μm. Comparing Figure 9(c) with Figure 9(d), the corrosion surface of the macroporous silicon obtained in 1.0 M NaOH suffers from lack of uniformity with the appearance of heterogeneous pores. On the contrary, the corrosion surface of the macroporous silicon obtained in 1.0 M NaOH/EtOH (30%) shows a uniform porous surface.

4. Conclusions

All the macroporous silicon samples were fabricated by electrochemical anodization of n-type silicon wafers in the electrolyte solution of HF (40%) : EtOH (99.5%) = 1 : 1 with a constant current density of 30 mA cm−2 for 30 min. The addition of ethanol to 1.0 M NaOH can shorten the stabilizing time for macroporous silicon corrosion. The oxidation of macroporous silicon in low concentration of NaOH solution is more obvious than that in high concentration of NaOH. The corrosion potential shifts significantly to more negative potentials and the corrosion current density increases with concentration of NaOH increasing. Adding ethanol to 1.0 M NaOH can lead to the corrosion potentials shift in the positive direction and corrosion current density increase. Macroporous silicon is seriously damaged by 1.0 M NaOH and 1.0 M NaOH/EtOH (30%).

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgments

This project is supported by the Opening Project of Key Laboratory of Green Catalysis of Sichuan Institutes of Higher Education (no. LYJ1503) and the Opening Project of Material Corrosion and Protection Key Laboratory of Sichuan Province (no. 2015CL09).