Study of New Thiazole Based Pyridine Derivatives as Potential Corrosion Inhibitors for Mild Steel: Theoretical and Experimental Approach
Table 6
Impedance parameters for the corrosion of MS in 0.5 M HCl in the absence and presence of different concentrations of inhibitors at 303 K.
| Inhibitor | Concentration (mM) | (Ohm cm2) | (F cm−2) | (Ohm cm2) | % IE |
| | Blank | 124 | 59.7 | 2.84 | — |
| 2-MTPH | 0.22 | 393 | 33.1 | 8.10 | 68.5 | 0.44 | 486 | 25.9 | 3.40 | 74.6 | 0.66 | 998 | 25.6 | 4.66 | 87.6 | 0.88 | 1360 | 14.9 | 1.32 | 91.0 |
| 3-MTPH | 0.22 | 262 | 33.7 | 3.72 | 52.8 | 0.44 | 400 | 21.9 | 3.91 | 69.1 | 0.66 | 581 | 17.5 | 9.58 | 78.7 | 0.88 | 815 | 14.0 | 4.68 | 84.8 |