Inhibition Effect of Natural Pozzolan and Zinc Phosphate Baths on Reinforcing Steel Corrosion
Table 5
Bond stresses (MPa) of the investigated phosphate steel rebars.
| Concrete type | Rebar type | Bond stresses (MPa) | 28 days of curing | 90 days of curing | at 0.25 mm slip | at failure | at 0.25 mm slip | at failure |
| NP0 | Bare steel | 8.21 | 14.23 | 8.64 | 15.09 | ZnP | 7.93 | 13.79 | 8.61 | 15.47 | ZnP-Ni | 8.45 | 14.34 | 8.87 | 16.08 | ZnP-Cu | 8.28 | 14.41 | 8.91 | 15.88 | ZnP-Mn | 8.14 | 14.03 | 8.78 | 15.27 |
| NP10 | Bare steel | 8.05 | 13.96 | 8.75 | 15.51 | ZnP | 7.87 | 13.81 | 8.79 | 15.69 | ZnP-Ni | 8.44 | 13.96 | 9.14 | 16.58 | ZnP-Cu | 8.31 | 14.31 | 8.97 | 15.89 | ZnP-Mn | 8.06 | 13.85 | 8.95 | 15.73 |
| NP20 | Bare steel | 8.23 | 15.09 | 8.69 | 15.54 | ZnP | 8.11 | 15.01 | 9.1 | 15.69 | ZnP-Ni | 8.56 | 15.61 | 8.95 | 15.98 | ZnP-Cu | 8.49 | 15.74 | 8.77 | 16.04 | ZnP-Mn | 8.19 | 14.98 | 8.85 | 15.66 |
| NP30 | Bare steel | 8.51 | 15.34 | 9.04 | 15.83 | ZnP | 8.46 | 15.09 | 8.81 | 15.95 | ZnP-Ni | 8.97 | 16.32 | 9.23 | 16.69 | ZnP-Cu | 8.60 | 15.96 | 9.11 | 16.48 | ZnP-Mn | 8.51 | 15.51 | 9.03 | 16.01 |
|
|