International Journal of Corrosion / 2018 / Article / Tab 2 / Research Article
Experimental and Theoretical Studies on the Corrosion Inhibition of Brass in Hydrochloric Acid by N-(4-((4-Benzhydryl Piperazin-1-yl) Methyl Carbamoyl) Phenyl) Furan-2-Carboxamide Table 2 Tafel polarization parameters for brass in 1M HCl with BFC from 30°C to 60°C.
S.No. Temp. (°C) Conc. of inhibitor (mM) (V/SCE)- (mV dec−1 ) - (mV dec−1 ) (mA cm−2 )IE% 1 30°C Blank -0.483 6.85 6.78 3.846 - 0.20 -0.516 11.63 5.94 1.882 51.06 0.40 -0.548 10.54 5.70 1.723 55.20 0.60 -0.549 11.77 4.88 1.570 59.17 0.80 -0.546 11.10 4.17 1.401 63.57 1.01 -0.550 11.62 6.72 1.398 63.65 1.21 -0.566 11.82 6.87 1.354 64.79 1.41 -0.599 12.68 6.11 1.136 70.46 2 40°C Blank -0.466 5.663 6.36 5.728 - 0.20 -0.468 6.631 6.77 2.457 57.10 0.40 -0.470 6.178 8.82 2.280 60.19 0.60 -0.466 8.817 8.70 2.161 62.27 0.80 -0.474 8.875 8.97 1.986 65.32 1.01 -0.478 9.957 8.18 1.804 68.50 1.21 -0.482 13.25 8.50 1.629 71.56 1.41 -0.493 11.50 6.90 1.472 74.30 3 50°C Blank -0.433 6.307 6.09 8.532 - 0.20 -0.446 6.128 8.51 3.428 59.82 0.40 -0.451 8.695 7.62 3.276 61.60 0.60 -0.459 13.30 7.84 3.174 62.79 0.80 -0.466 13.81 6.81 2.862 66.45 1.01 -0.472 11..68 6.22 2.650 68.94 1.21 -0.473 8.105 8.90 2.266 73.44 1.41 -0.461 11.73 6.78 1.951 77.13 4 60°C Blank -0.423 5.681 6.36 9.578 - 0.20 -0.436 7.897 7.45 3.773 60.60 0.40 -0.437 11.32 6.95 3.562 62.81 0.60 -0.442 12.92 7.98 3.118 67.44 0.80 -0.448 10.91 7.44 3.046 68.19 1.01 -0.451 10.17 6.76 2.852 70.22 1.21 -0.457 10.33 9.06 2.312 75.86 1.41 -0.478 13.42 7.63 1.268 86.79