A Large-Scale Synthesis and Characterization of Quaternary <mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML"><mml:mrow><mml:msub><mml:mrow><mml:mtext>CuIn</mml:mtext></mml:mrow><mml:mi>x</mml:mi></mml:msub><mml:msub><mml:mrow><mml:mtext>Ga</mml:mtext></mml:mrow><mml:mrow><mml:mn mathvariant="bold">1</mml:mn><mml:mo>−</mml:mo><mml:mi>x</mml:mi></mml:mrow></mml:msub><mml:msub><mml:mtext>S</mml:mtext><mml:mn mathvariant="bold">2</mml:mn></mml:msub></mml:mrow></mml:math> Chalcopyrite Nanoparticles via Microwave Batch Reactions

<table>(a) Normalized XRD data of CuIn<sub>0.72</sub>Ga<sub>0.28</sub>S<sub>2</sub> soluble nanoparticles prepared 195°C. (b) Normalized UV-Vis absorption spectra of CuIn<sub>0.72</sub>Ga<sub>0.28</sub>S<sub>2</sub> soluble nanoparticles prepared 195°C.</table>

International Journal of Chemical Engineering

fig7

Figure 7

Figure 7: A Large-Scale Synthesis and Characterization of Quaternary <mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML"><mml:mrow><mml:msub><mml:mrow><mml:mtext>CuIn</mml:mtext></mml:mrow><mml:mi>x</mml:mi></mml:msub><mml:msub><mml:mrow><mml:mtext>Ga</mml:mtext></mml:mrow><mml:mrow><mml:mn mathvariant="bold">1</mml:mn><mml:mo>−</mml:mo><mml:mi>x</mml:mi></mml:mrow></mml:msub><mml:msub><mml:mtext>S</mml:mtext><mml:mn mathvariant="bold">2</mml:mn></mml:msub></mml:mrow></mml:math> Chalcopyrite Nanoparticles via Microwave Batch Reactions 

International Journal of Chemical Engineering

A Large-Scale Synthesis and Characterization of Quaternary CuInxGa1−xS2 Chalcopyrite Nanoparticles via Microwave Batch Reactions

Figure 7