High-Active Metallic-Activated Carbon Catalysts for Selective Hydrogenation

Carrara, Nicolás; Betti, Carolina; Coloma-Pascual, Fernando; Almansa, María Cristina; Gutierrez, Laura; Miranda, Cristian; Quiroga, Mónica E.; Lederhos, Cecilia R.

doi:https://doi.org/10.1155/2018/4307308

International Journal of Chemical Engineering

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Data Availability Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2018 | Article ID 4307308 | https://doi.org/10.1155/2018/4307308

High-Active Metallic-Activated Carbon Catalysts for Selective Hydrogenation

Nicolás Carrara,¹Carolina Betti,¹Fernando Coloma-Pascual,²María Cristina Almansa,²Laura Gutierrez,^1,3Cristian Miranda,⁴Mónica E. Quiroga,^1,3and Cecilia R. Lederhos¹

Academic Editor: Raghunath V. Chaudhari

Received30 Jan 2018

Revised23 Apr 2018

Accepted30 Apr 2018

Published05 Jul 2018

Abstract

A series of low-loaded metallic-activated carbon catalysts were evaluated during the selective hydrogenation of a medium-chain alkyne under mild conditions. The catalysts and support were characterized by ICP, hydrogen chemisorption, Raman spectroscopy, temperature-programmed desorption (TPD), temperature-programmed reduction (TPR), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR micro-ATR), transmission electronic microscopy (TEM), and X-ray photoelectronic spectroscopy (XPS). When studying the effect of the metallic phase, the catalysts were active and selective to the alkene synthesis. NiCl/C was the most active and selective catalytic system. Besides, when the precursor salt was evaluated, PdN/C was more active and selective than PdCl/C. Meanwhile, alkyne is present in the reaction media, and geometrical and electronic effects favor alkene desorption and so avoid their overhydrogenation to the alkane. Under mild conditions, nickel catalysts are considerably more active and selective than the Lindlar catalyst.

1. Introduction

Olefins are of great academic and industrial interest. They are very important raw material for the synthesis of biologically active compounds, margarine, and lubricants, as well as in plastic industry [1]. Also, olefins present many applications in fine chemistry. The purification of olefins is a very important step in manufacturing polymers with a 0.35% content of impurities, as alkyne compounds, leading to a polymer with undesirable properties. There are several ways of purification of olefins stream, and the most common is solvent extraction, which is a nonecological friendly procedure. Another alternative for obtaining olefins is via the selective hydrogenation of alkynes. This catalytic process is the major challenge because they reduce the production costs and let obtaining good yields and high selectivities.

Different noble metals as Pd, Pt, Ru, and Rh anchored on inorganic supports are highly active and selective for carbon-carbon multiple bond hydrogenations [2–7]. During the partial hydrogenation of alkynes to alkenes, or dienes to olefins, many authors found that supported palladium catalysts presented the highest catalytic activities [8, 9]. The most used catalyst for alkyne partial hydrogenation is the commercial Lindlar catalyst, that contains palladium poisoned with lead (Pd/CaCO₃, 5 wt.% Pd modified with Pb(OAc)₂) [10]. The cost of this noble metal has increased greatly in the last decade, and the world tendency is to develop cheaper catalysts by lowering the Pd content or by using cheaper metals.

In previous papers [11, 12], we have studied the partial hydrogenation reaction of a medium-chain alkyne (1-heptyne) to obtain the corresponding olefin using monometallic catalysts using alumina and carbonaceous supports. In these papers, the influences of different supports, reaction, and reduction temperature and the metallic phase on the activity and the selectivity were evaluated.

Activated carbonaceous surfaces have been studied during the last decades [13, 14] in different reactions showing that they are very complex. Carbonaceous supports are widely used because of their inertness, stability, high specific surface, low cost, and ability to easily recover the metallic phase after ending their useful life. Besides, during the synthesis of the catalysts, on the surface of activated carbon, different oxygenated and nitrogenized functional groups are found, and both can be easily modified when the material is physically or chemically pretreated [15, 16].

The objectives of this work were to synthesize low-loaded Ru, Pd, and Ni catalysts using an activated carbon as support and evaluate their activities and selectivities during 1-heptyne selective hydrogenation reaction under mild conditions. The effect of the type of metal and the precursor salt on the activity and selectivity to the desired product (1-heptene) is also evaluated. The Lindlar catalyst was used as a reference.

2. Experimental

2.1. Catalyst Preparation

CNR-115 pelletized activated carbon provided by NORIT (S_BET: 1503 m²·g⁻¹, micropore volume: 0.738 mL·g⁻¹, and total pore volume: 1.010 mL·g⁻¹) was used as a support. Chloride acidic solutions of Ru, Pd, and Ni (purity >99.98%) at pH = 1 with HCl were used to prepare PdCl/C, RuCl/C, and NiCl/C catalysts by the incipient wetness technique. On the contrary, PdN/C was prepared from Pd(NO₃)₂ acidic solution (purity >99.98%) at pH = 1 with HNO₃. Solutions have the necessary concentration to obtain 0.4 wt.% of each metal (M: Pd, Ni, and Ru) on the final catalyst. After impregnation, all samples were dried overnight at 373 K and reduced under a hydrogen stream, flow rate of 25 mL·min⁻¹, at 393 K for 1 h before each catalytic evaluation.

2.2. Catalyst Characterization

Metal loadings of the catalysts were obtained by the ICP technique in PerkinElmer Optima 2100DV equipment, previous digesting the samples in a Start D Microwave Digestion system (Milestone).

Dispersion values were obtained by hydrogen chemisorption in Micromeritics Accusorb 2100e equipment after reducing each sample at 393 K for 1 h under 5% v/v H₂/Ar, and an atomic ratio H : M equal to 1 was assumed for all of the calculations as suggested by the other authors [17–19]. The particle diameter of the catalysts was calculated from the chemisorption results following the procedure reported by Paryjczac et al. [20, 21]. The adopted metallic surface area, σ value, was calculated from the average of the densities of the (100), (110), and (111) crystal planes [22, 23]; the values for Pd, Ru, and Ni were 1.27·10¹⁹, 1.63·10¹⁹, and 1.54·10¹⁹ atoms·m⁻², respectively.

Temperature-programmed desorption (TPD) allowed to determine the amount and type of oxygen-containing groups on the activated carbon surface. 10 mg of the sample were treated in a He stream at 100 mL·min⁻¹ from 293 to 1273 K at 20 K·min⁻¹. In the experiments, the effect of the thrust is corrected using a “white” curve. CO and CO₂ desorptions were measured in a simultaneous TG-DTA (Mettler Toledo model TGA/SDTA851e/LF/1600) coupled to a quadrupole mass spectrometer (Pfeiffer Vacuum model Thermostar GSD301T).

The FTIR micro-ATR technique was carried in a Shimadzu FTIR-8400 spectrophotometer which is based on the internal reflectance phenomenon. The FTIR micro-ATR technique is the most sensitive technique for surface analysis [24].

The Raman spectra were recorded using a LabRam spectrometer (Horiba–Jobin–Yvon) coupled to an Olympus confocal microscope (a 100x objective lens was used for simultaneous illumination and collection) and equipped with a CCD detector cooled to about 200 K using the Peltier effect. The excitation wavelength was 532 nm in all cases (Spectra-Physics diode pump solid state laser). The laser power was set at 30 mW.

X-ray diffraction (XRD) measurements of powdered samples were obtained using a Shimadzu XD-D1 instrument with CuK_α radiation (λ = 1.5405 Å) in the 21 < 2θ < 49° at 0.25°·min⁻¹ scan speed.

The electronic state of superficial species and their atomic ratios were determined by X-ray photoelectron spectroscopy (XPS), following Pd and Ru 3d_5/2, Ni and Cl 2p_3/2, N, C, and O 1s peaks’ binding energy (BE) for catalysts and support. Measurements were acquired in VG-Microtech Multilab equipment, with MgK_α (hν: 1253.6 eV) radiation and a pass energy of 50 eV. The analysis pressure during data acquisition was kept at 5.10⁻⁷ Pa. Samples were treated in situ in the presence of a H₂ stream following the same pretreatment conditions for each catalyst. A careful deconvolution of the spectra was made, and the areas of the peaks were estimated by calculating the integral of each peak after subtracting a Shirley background and fitting the experimental peak to a combination of Lorentzian/Gaussian lines of 30–70% proportions. The reference binding energy (BE) was C 1s peak at 285.0 eV. Determinations of the superficial atomic ratios were made by comparing the areas under the peaks after background subtraction and corrections due to differences in escape depth and in photoionization cross sections [25].

The reducibility of the surface species in all the catalysts was determined by temperature-programmed reduction (TPR) which was carried out in an Ohkura TP 2002 S instrument equipped with a thermal conductivity detector. Samples were pretreated at 373 K for 30 min under an argon stream, cooled up to room temperature under an argon flow, and then, the temperature was increased up to 1223 K at 10 K·min⁻¹ in a 5% hydrogen/argon mixture stream.

Transmission electronic microscopy (TEM) photographs were obtained using an electronic microscope JEOL JEM-2011 at 200 kV. The samples were reduced for 1 h at 393 K and dispersed in distilled water in order to obtain TEM images which are only used for comparative purposes.

2.3. Catalytic Evaluation

The reaction test accessed was 1-heptyne selective hydrogenation, carried out at 303 K, 150 kPa, and 800 rpm during 180 min. The possibility of external and internal diffusional limitations during the catalytic tests was discarded using a previously described procedure [26]. Experiments were performed in a stainless steel stirred tank reactor equipped with a magnetically driven stirrer with two blades in counterrotation. The inner wall of the reactor was completely coated with PTFE in order to neglect the catalytic action of the steel of the reactor found by other authors [27]. Samples of 0.75 g of the catalyst were used in a total volume of 75 mL of 5% (v/v) solution of 1-heptyne (Fluka, Cat. no. 51950) in toluene (Merck, Cat. no. TX0735-44).

Blank tests were obtained using CNR and CNR-N activated carbons, and no conversion of 1-heptyne was observed. The commercial Lindlar catalyst (Aldrich Cat. no. 20,573-7) was used as a reference, maintaining constant S : M (1-heptyne/metal molar ratio). Reactant and products were analyzed by gas chromatography using a flame ionization detector and a HP INNOWax polyethyleneglycol capillary column.

3. Results and Discussion

3.1. Catalysts and Support Characterization

A way to know the number and nature of oxygen functional groups present on the carbon surface is by the temperature-programmed desorption (TPD) technique. It is well known [15, 16] that the treatment of the catalysts with a strong oxidant acid, such as nitric acid, modifies the oxygen amount and the kind of superficial groups in the carbon surface. For this purpose, a sample of the carbon support (CNR) was treated with HNO₃ (CNR-N), and both were analyzed and compared by TPD. This allows studying the effect of nitric acid, which was used during the catalyst preparation step, on the CNR surface.

In Figures 1(a) and 1(b), the concentration profiles of CO and CO₂ as a function of temperature, respectively, for CNR and CNR-N samples are shown. During the TPD experiments, the samples analyzed showed highly different behaviors, mainly during the CO₂ desorption (Figure 1(b)) due to the decomposition of carboxyl and lactone groups. It can be seen that these surface groups had highly increased in the carbon sample treated with the oxidizing acid (HNO₃).

(a)

(b)

The quantitative results from TPD-MS analysis for the CNR and CNR-N supports are presented in Table 1. The amount of surface oxygen groups of carbonaceous supports, estimated by CO, CO₂, and O₂ evolved in TPD experiments (Table 1), shows that the oxidizing treatment with HNO₃ produces a large amount of surface oxygenated complexes, with 175% higher amount of carboxylic-type groups that decompose to give CO₂ under the heat treatment [28]. This enhancement is also observed in the TPD profile in Figure 1(b).

The FTIR micro-ART spectra are given in Figure 2(a) for the supports CNR and CNR-N and in Figure 2(b), for the catalysts PdCl/C, PdN/C, NiCl/C, and RuCl/C. On the one hand, in Figure 2(a), it can be seen that the CNR carbonaceous support did not show new bands in the support treated with nitric acid (CNR-N). The bands at 665, 1583, and 3346 cm⁻¹ correspond to ring deformation and C-O stretching vibrations in phenolic groups, but in general, the lack of parallel behavior between the growth of bands in 1000–1350 cm⁻¹ is attributed to primarily C-O stretching of ether groups, possibly furans, to C-OH species [29], and to O-H or C-N stretching [30].

(a)

(b)

On the other hand, in Figure 2(b), for all the catalysts, PdN/C, PdCl/C, NiCl/C, and RuCl/C, the following peaks can be seen in general: (i) a broad band centered at 3444 cm⁻¹ which was assigned mainly to O-H stretching, associated with the water absorbed on the surface of the material and hydroxylated groups; (ii) a NH₂ stretching band located at 3600–3100 cm⁻¹; and (iii) a C-H stretching band between 3000 and 2800 cm⁻¹ [31]. In the 1350–1000 cm⁻¹ range, the growth of bands for the PdN/C catalyst can be attributed mainly to C-N stretching [32] because of the support treatment with nitric acid during the synthesis of the catalyst.

Figure 3 shows the Raman spectra of the catalysts and carbon support in the range of 100–2000 cm⁻¹. The profile of all catalysts analyzed is very similar to the CNR support spectrum. Two intense bands at ca. 1600 cm⁻¹ and ca. 1350 cm⁻¹ are observed, which are the typical signals of the graphite spectrum. The first signal is known as the G band associated with the graphitic order, and the second is named the D band and is attributed to structural defects [32].

PdN/C, PdCl/C, RuCl/C, NiCl/C, and the CNR support diffractograms are shown in Figure 4. In this figure, it can be seen that there are no defined signals for the metallic samples or to the support, which could indicate the absence of the crystalline phases in all samples, or the crystals were very small (<100 Å). The absence of the crystalline phase is a consequence of the low-metallic loadings of the samples, 0.4 wt.%, low below the detection limit of the XRD equipment.

Figure 5 shows temperature-programmed reduction profiles of PdN/C, PdCl/C, RuCl/C, and NiCl/C catalysts. In this figure, the TPR profile of CNR carbon is also presented for a comparative way. As can be seen in Figure 5, the support and the catalysts profiles present a broad peak with a maximum at ca. 870 K, which can be attributed to the gasification of the carbonaceous support, the decomposition of chloride or nitrogen species, the reduction of superficial oxygenated groups of the support, or due to the possible presence of impurities (5-6%), producing CH₄, CO, and/or CO₂ [33–35]. de Miguel et al. [36], for carbonaceous supports, found these types of consumption at very high temperatures, between 923 and 1223 K, associated with decomposition of superficial oxygenated groups (C[O]) that can liberate CO in the presence of a reductive stream. In Figure 5, it can be seen that, at temperatures higher than 700 K, all metallic catalysts samples present very similar profile due to the reduction of surface groups of the carbonaceous support.

The palladium catalysts (PdN/C and PdCl/C) presented at high temperatures a much wider peak profiles with respect to the support, as can be observed in Figure 5, with a maximum at ca. 875 K. No peaks are present at low reduction temperature, and this is because the palladium can be reduced by carbon at low temperature, even at room temperature as was observed by other authors [37]. In Figure 5, it can be seen that the peak above 700 K is more intense for PdN/C and NiCl/C catalysts. Besides, the TPR profile of the NiCl/C sample shows a small peak at 610 K attributed to the reduction of NiO to Ni° species, which indicates a weak metal-support interaction [38–40]. Lastly, for the ruthenium catalyst (RuCl/C), the TPR profile presents a signal with maximum at 610 K, related to the reduction of ruthenium, Ru³⁺ → Ru²⁺ → Ru°, assigned to the reduction of the ruthenium chloride species [16, 35].

As an early conclusion, at the reduction temperature used during the preparation step of the catalysts (393 K, marked in Figure 5), the palladium metals on PdCl/C and PdN/C could be mostly as Pd° species on the catalyst surface; meanwhile, nickel and ruthenium are present as Ni²⁺ and Ru³⁺ species.

Table 2 summarizes all the catalysts under study, the results of ICP, dispersion and particle diameter by hydrogen chemisorption, XPS, initial reaction rate, and activity TOF values. For a comparative study, the Lindlar catalyst was also included in Table 2. The metal loadings of the synthetized catalysts are ca. 0.4 wt.% in the final catalyst, while a concentration of 5 wt.% of Pd was corroborated for commercial Lindlar. Dispersion values show the following order PdCl/C > PdN/C > RuCl/C, while NiCl/C and Lindlar catalysts present extremely low D values (lower than 5%). Higher dispersions are favored by low loadings of the metallic precursor and by low pretreatment conditions used during the preparation of the catalysts [41]; besides, high surface areas and large pore volume of the carbonaceous materials usually favor very high dispersion of an active phase. All these factors avoid the sintering of the active phase. In our case, the highest dispersion of the Pd catalyst prepared from chlorinated precursor can be due to the presence of complex oxychlorinated species formed during the pretreatment step. The presence of these species improves the metal dispersion due to the greater interaction between these oxychlorinated species and the support as compared to the weaker one displayed by palladium(II) oxide (PdO) [42–44]. Furthermore, the PdN/C catalyst presents a dispersion of ca. 50% attributed to the high concentration of carboxylic-type groups on the surface, as observed by TPD-MS analysis, that exert an electronic and geometrical effect over the nitrate precursor used. On the contrary, due to the high surface area, ruthenium particles would also be highly dispersed on these carbon supports [45]. However, there is no simple relationship between the value of the surface area of the activated carbon and the metal dispersion of the catalysts supported on activated carbon [46]. Some authors [47–51] reported the inhibition and drawbacks due to the use of RuCl₃ as a precursor salt because the chloride from this salt is a poison for CO and H₂ chemisorptions and may be partitioned between the metal and the support. In our case, the high degree of sintering of the ruthenium metal particles could be due to the fact that, during the pretreatment process, no oxychlorinated species interacting with the support are formed, as noted earlier while studying ruthenium catalysts of different metal contents over the alumina support [12, 21]. The low dispersion of nickel is a characteristic when this metal is used to prepare inorganic or carbonaceous catalysts [52, 53].

From the H₂ chemisorption results, the metal particle size (d) was determined on assuming a spherical particle in accordance with Badano et al. [21]. The particle size order is PdCl/C < PdN/C < RuCl/C ≪ NiCl/C ≪ Lindlar. The smallest particle size of PdCl/C catalysts is due to the higher surface interaction between Pd^δ+O_xCl_y and oxygenated groups of the carbonaceous support, as observed earlier when alumina was used as a support [21]. The higher particle size of NiCl/C could be related with the higher structural defects observed by the Raman spectra in Figure 3.

Figure 6 shows the XPS spectra of the Pd 3d_5/2 band for PdN/C and PdCl/C, Ru 3d_5/2 band for RuCl/C, and Ni 2p_3/2 band for the NiCl/C catalyst. Besides, the XPS spectra of the catalysts prepared from chlorine precursors (PdCl/C, RuCl/C, and NiCl/C) show a Cl 2p_3/2 peak at ca. 199.4 eV that corresponds to surface chloride species [54] that were not completely eliminated after reduction because of the high adsorption capacity of the carbonaceous material used. The maximum binding energy (BE) of Pd and Ru 3d_5/2, Ni 2p_3/2 peaks, and Cl/M atomic ratios are also listed in Table 2.

(a)

(b)

(c)

(d)

XPS results in Figure 6 show that both palladium catalysts present a Pd 3d_5/2 peak at 335.2 eV, which can be attributed to Pd^δ+ (δ ≈ 0) [16, 54]. Figure 6 also shows the spectra of palladium catalysts and the 3d_3/2 peak doublet shifted 5.2 eV with respect to the 3d_5/2 peak. No nitrogen was detected by XPS on the Pd catalyst prepared from the nitrate precursor. On the contrary, for the PdCl/C sample, the Cl/Pd atomic ratio was 1.56, confirming that chloride is present even after the reduction treatment. This could be attributed to the high absorption capacity of the carbon support. The chlorine content does not affect the palladium surface as it is totally reduced on the PdCl/C catalyst.

In the case of ruthenium, the BE reference is difficult because the Ru 3d peaks appear at the same region than the C 1s peak. There are also discrepancies in the BE reported in the literature for ruthenium compounds. The Ru 3d_5/2 signal for the RuCl/C catalyst was observed at 282.1 eV corresponding to ruthenium electrodeficient species as RuCl₃ [54]. For this catalyst, after the temperature pretreatments, the superficial atomic ratio Cl/Ru was 2.96.

According to the bibliography [54, 55], the Ni 2p_3/2 signal appears at 852.5 eV for Ni° species. For the NiCl/C catalyst, the two signals were observed in the spectrum of Figure 6 at 857.3 and 862.7 eV. The first peak could be assigned to the electrodeficient nickel species (Niⁿ⁺, with n → 2), probably corresponding to nickel interacting with the support [54–56], while the second peak corresponds to the characteristic shake-up satellite structure of Ni (II) [55, 57, 58]. This catalyst also presents a high Cl/Ni atomic ratio (2.05) as a consequence of the adsorption capacity or the carbonaceous support.

For the Lindlar catalyst, in Table 2, the main peaks at 335.2 eV (69%, at/at) and 336.9 eV (31%, at/at) are also registered, assigned to Pd^δ+ and electrodeficient Pdⁿ⁺ species (with δ → 0 and n → 2), respectively [53]. On the contrary, on the Lindlar catalyst, also two peaks of the Pb 4f_7/2 spectrum at 136.8 eV (20%, at/at) and 138.6 (80%, at/at) were attributed to Pb and Pb(OAc)₂, respectively [53].

In Figure 7, TEM micrographs of the carbonaceous catalysts are shown. The metal particle size for the PdCl/C catalyst is between 1 and 4 nm, presenting a high concentration of 2 nm Pd particles on the carbon surface. For PdN/C, the main palladium particle size is between 4 and 8 nm. The particle sizes of Ru on RuCl/C are mainly between 1 and 5 nm, although several bigger particles were observed on the micrographs. Besides, the NiCl/C catalyst presented the highest particle sizes between 25 and 40 nm.

(a)

(b)

(c)

(d)

3.2. Catalytic Tests

The catalytic performance during the selective hydrogenation of 1-heptyne for PdN/C, PdCl/C, RuCl/C, and NiCl/C catalysts is shown in Figure 8. 1-heptyne total conversion (%) and selectivity to 1-heptene (%) as a function of time (min) were plotted in this figure for all the studied catalysts. All the catalysts were active during the hydrogenation of 1-heptyne and presented high selectivity to 1-heptene, the desired product.

(a)

(b)

Besides, in Figure 9, 1-heptyne total conversion (%) and selectivity to 1-heptene (%) as a function of time (min) for the commercial Lindlar catalyst used as a reference is shown.

According to Figures 8 and 9 the order of selectivities to the corresponding alkene was:

In order to compare the performance of the catalytic systems, the initial reaction rate of hydrogenation of 1-heptyne () was estimated for all the catalysts using the following formula:where is the initial 1-heptyne reaction rate (mol·g_M⁻¹·s⁻¹), is the tangent value of the 1-heptyne total conversion versus time curve at , is the initial concentration of 1-heptyne (mol·L⁻¹), is the mass of the metal (Pd, Ru, or Ni) in the catalyst (g), is the reaction volume (L), and is the reaction time (s).

From these initial reaction rates of 1-heptyne hydrogenation, TOF values were calculated for all the catalysts and are summarized in Table 2. For hydrogenation reactions, TOF values between 10⁻² and 10² indicate a structure-insensitive system, not influenced by particle size [59, 60], so the differences in activities and selectivities between the catalysts may be associated with geometrical and/or geometrical effects. The order of activities of low-loaded catalysts is

The effect of the precursor salt was studied by comparing PdCl/C and PdN/C catalysts. The results obtained for these catalysts show differences in both activity and selectivity. For the catalyst synthetized from palladium nitrate as the precursor salt, the obtained TOF was 17 s⁻¹ versus the activity of palladium chloride precursor salt 8.6 s⁻¹. That is, each active site of the PdN/C catalyst is almost two times more active than that of PdCl/C. As observed by XPS and RTP, both catalysts have Pd^δ+ (with δ ≅ 0) as the active site, so no electronic effects are generated by the metallic phase; besides as observed by Raman, quite higher structural effects were found on PdN/C than on the PdCl/C sample. When comparing the catalytic behavior of the different Pd precursors, higher selectivities to 1-heptene were obtained when palladium nitrate was used, ca. 86% at 180 min, while for PdCl/C selectivities, ca. 70% was obtained.

In Figure 10, the main superficial groups present on carbonaceous supports are summarized. Between them carboxylic groups by heterolytic rupture of the O-H bond, could favor the adsorption of the cationic metallic precursors Mⁿ⁺. In our case, the higher distribution of carboxylic and lactone groups on the surface of PdN/C could favor the adsorption of Pd²⁺, and its reduction to Pd° (as detected by XPS and TPR) during the pretreatment step: for 1 h at 393 K under a hydrogen stream. Also, the high concentration of carboxylic groups favors the high dispersion of the active sites and the small particle sizes. So, the observed differences in activity between PdN/C and PdCl/C could be originated, at least in part, by geometrical effects due to higher structural defects (as noted in D-bands on the Raman spectra) and electronic effects originated by the high concentration of carboxylic superficial groups on PdN/C (the favorable effect) and high remnants of chloride on PdCl/C catalysts (the negative effect). Besides, differences in selectivity between the PdN/C and PdCl/C catalysts could be caused on the one hand to the electronic and geometrical effects that favors the formation of 1-heptene and on the other hand to higher amount of carbonaceous superficial groups that favors the desorption of the alkene, avoiding its overhydrogenation, while alkyne is present in the reaction media.

When analyzing the effect of the metal type used to synthesize the carbonaceous catalysts, PdCl/C, RuCl/C, and NiCl/C, the highest activity and selectivity were achieved when the supported metal is nickel, a very low cost precursor salt. The high activity and selectivity of NiCl/C could be related to electronic or geometrical effects of active sites, which would control the dissociative adsorption of hydrogen being this the controlling step [61], and/or to the aromatic superficial groups of the support that would preferentially adsorb remaining 1-heptyne desorbing 1-heptene from the reaction media, so avoiding its total hydrogenation to the alkane.

4. Conclusions

The effect of metallic salt and the kind of metal was studied using a carbonaceous support. A series of low-loaded catalysts supported on an activated carbon (ca. 0.4 wt.%) were synthetized by the incipient wetness technique. Nanoparticles of palladium, ruthenium, and nickel were deposited using Pd(NO₃)₂, PdCl₂, RuCl₃, and NiCl₂ aqueous acidic solutions as precursor salts. The catalysts were pretreated under moderate conditions.

PdN/C, PdCl/, RuCl/C, and NiCl/C were characterized by ICP, TPD, FTIR micro-ATR, Raman, XRD, TPR, hydrogen chemisorption, XPS, and TEM.

All the catalytic systems were assessed during the selective hydrogenation of 1-heptyne, a medium-chain alkyne under moderate operational conditions: 303 K, 150 kPa, and 800 rpm during 180 min. The catalysts were active and selective to 1-heptene. The order of activity and selectivity found was NiCl/C > RuCl/C > PdCl/C. Geometrical and electronic effects over the NiCl/C catalyst favors alkyne adsorption and 1-heptene desorption in the reaction media, avoiding alkyne total hydrogenation to the alkane. Besides, the PdN/C catalyst is more active and selective than PdCl/C due to geometrical and electronic effects, and the first ones are caused by structural defects (observed by Raman), while the seconds ones are originated by the high loading of carboxylic superficial on PdN/C and the chloride remnants on PdCl/C catalysts (as observed by TPD-MS and XPS, resp.).

Data Availability

The data used to support the findings of this study are available from the corresponding author upon request.

Conflicts of Interest

The authors declare that they have no conflicts of interest.

Acknowledgments

The financial assistance of UNL (CAI+D), CONICET (PIP 457), and ANPCyT (PICT-2013-2021 and PICT-2016-1453) is greatly acknowledged.

References

A. Molnár, A. Sárkány, and M. Varga, “Hydrogenation of carbon–carbon multiple bonds: chemo-, regio- and stereo-selectivity,” Journal of Molecular Catalysis A: Chemical, vol. 173, no. 1-2, pp. 185–221, 2001.
View at: Publisher Site | Google Scholar
D. Teschner, E. Vass, M. Hävecker et al., “Alkyne hydrogenation over Pd catalysts: a new paradigm,” Journal of Catalysis, vol. 242, no. 1, pp. 26–37, 2006.
View at: Publisher Site | Google Scholar
P. Kačer, M. Kuzma, and L. Ćervenỳ, “The molecular structure effects in hydrogenation of cycloalkylsubstituted alkynes and alkenes on platinum and palladium catalysts,” Applied Catalysis A: General, vol. 259, no. 2, pp. 179–183, 2004.
View at: Publisher Site | Google Scholar
B. M. Choudary, M. Lakshmi Kantam, N. Mahender Reddy et al., “Hydrogenation of acetylenics by Pd-exchanged mesoporous materials,” Applied Catalysis A: General, vol. 181, no. 1, pp. 139–144, 1999.
View at: Publisher Site | Google Scholar
J. Lei, L. B. Su, K. Zeng et al., “Recent advances of catalytic processes on the transformation of alkynes into functional compounds,” Chemical Engineering Science, vol. 171, pp. 404–425, 2017.
View at: Publisher Site | Google Scholar
C. Oger, L. Balas, T. Durand, and J.-M. Galano, “Are alkyne reductions chemo-, regio-, and stereoselective enough to provide pure (Z)-olefins in polyfunctionalized bioactive molecules?” Chemical Reviews, vol. 113, no. 3, pp. 1313–1350, 2013.
View at: Publisher Site | Google Scholar
G. A. Attard, J. A. Bennett, I. Mikheenko et al., “Semi-hydrogenation of alkynes at single crystal, nanoparticle and biogenic nanoparticle surfaces: the role of defects in Lindlar-type catalysts and the origin of their selectivity,” Faraday Discussions, vol. 162, pp. 57–75, 2013.
View at: Publisher Site | Google Scholar
S. Nishimura, Handbook of Heterogeneous Catalytic Hydrogenation for Organic Synthesis, Wiley, New York, NY, USA, 2001.
B. Chen, U. Dingerdissen, J. G. E. Krauter et al., “New developments in hydrogenation catalysis particularly in synthesis of fine and intermediate chemicals,” Applied Catalysis A: General, vol. 280, no. 1, pp. 17–46, 2005.
View at: Publisher Site | Google Scholar
H. Lindlar and R. Dubuis, “Palladium catalyst for partial reduction of acetylenes,” Organic Syntheses, vol. 46, pp. 89–92, 1966.
View at: Publisher Site | Google Scholar
C. Lederhos, P. C. L’Argentière, and N. S. Fígoli, “1-heptyne selective hydrogenation over Pd supported catalysts,” Industrial & Engineering Chemistry Research, vol. 44, no. 6, pp. 1752–1766, 2005.
View at: Publisher Site | Google Scholar
C. Lederhos, P. C. L’Argentière, F. Coloma-Pascual, and N. S. Fígoli, “A study about the effect of the temperature of hydrogen treatment on the properties of Ru/Al2O3 and Ru/C and their catalytic behavior during 1-heptyne semi-hydrogenation,” Catalysis Letters, vol. 110, no. 1-2, pp. 23–28, 2006.
View at: Publisher Site | Google Scholar
E. Auer, A. Freund, J. Pietsch, and T. Tacke, “Carbons as supports for industrial precious metal catalysts,” Applied Catalysis A: General, vol. 173, no. 2, pp. 259–271, 1998.
View at: Publisher Site | Google Scholar
F. Rodríguez-Reinoso, “The role of carbon materials in heterogeneous catalysis,” Carbon, vol. 36, no. 3, pp. 159–175, 1998.
View at: Publisher Site | Google Scholar
J. L. Figueiredo, M. F. R. Pereira, M. M. A. Freitas, and J. J. M. Orfão, “Modification of the surface chemistry of activated carbons,” Carbon, vol. 37, no. 9, pp. 1379–1389, 1999.
View at: Publisher Site | Google Scholar
C. R. Lederhos, J. M. Badano, N. Carrara et al., “Metal and precursor effect during 1-heptyne selective hydrogenation using an activated carbon as support,” The Scientific World Journal, vol. 2013, Article ID 528453, 9 pages, 2013.
View at: Publisher Site | Google Scholar
J. Okal, M. Zawadzki, L. Kępiński, L. Krajczyk, and W. Tylus, “The use of hydrogen chemisorption for the determination of Ru dispersion in Ru/γ-alumina catalysts,” Applied Catalysis A: General, vol. 319, pp. 202–209, 2007.
View at: Publisher Site | Google Scholar
C.-B. Wang, H.-K. Lin, and C.-M. Ho, “Effects of the addition of titania on the thermal characterization of alumina-supported palladium,” Journal of Molecular Catalysis A: Chemical, vol. 180, no. 1-2, pp. 285–291, 2002.
View at: Publisher Site | Google Scholar
F. Pompeo, N. N. Nichio, M. M. V. M. Souza, D. V. Cesar, O. A. Ferretti, and M. Schmal, “Study of Ni and Pt catalysts supported on α-Al₂O₃ and ZrO₂ applied in methane reforming with CO₂,” Applied Catalysis A: General, vol. 316, no. 2, pp. 175–183, 2007.
View at: Publisher Site | Google Scholar
T. Paryjczac and J. A. Szymura, “Electron microscopic and chemisorption comparison studies on the metal dispersion of Pd, Rh, and Ir supported catalysts,” Zeitschrift für Anorganische und Allgemeine Chemie, vol. 449, no. 1, pp. 105–114, 1979.
View at: Publisher Site | Google Scholar
J. M. Badano, M. Quiroga, C. Betti, C. Vera, S. Canavese, and F. Coloma-Pascual, “Resistance to sulfur and oxygenated compounds of supported Pd, Pt, Rh, Ru catalysts,” Catalysis Letters, vol. 137, no. 1-2, pp. 35–44, 2010.
View at: Publisher Site | Google Scholar
J. J. F. Scholten, A. P. Pijpers, and A. M. L. Hustings, “Surface characterization of supported and nonsupported hydrogenation catalysts,” Catalysis Reviews, vol. 27, no. 1, pp. 151–206, 1985.
View at: Publisher Site | Google Scholar
R. J. Matyi, L. H. Schwartz, and J. B. Butt, “Particle size, particle size distribution, and related measurements of supported metal catalysts,” Catalysis Reviews, vol. 29, no. 1, pp. 41–99, 1987.
View at: Publisher Site | Google Scholar
S. Shin, J. Jang, S.-H. Yoon, and I. Mochida, “A study on the effect of heat treatment on functional groups of pitch based activated carbon fiber using FTIR,” Carbon, vol. 35, no. 12, pp. 1739–1743, 1997.
View at: Publisher Site | Google Scholar
R. Borade, A. Sayari, A. Adnot, and S. Kaliaguine, “Characterization of acidity in ZSM-5 zeolites: an X-ray photoelectron and IR spectroscopy study,” Journal of Physical Chemistry, vol. 94, no. 15, pp. 5989–5994, 1990.
View at: Publisher Site | Google Scholar
D. Liprandi, M. Quiroga, E. Cagnola, and P. L’Argentière, “A new more sulfur-resistant rhodium complex as an alternative to the traditional Wilkinson’s catalyst,” Industrial & Engineering Chemistry Research, vol. 41, no. 19, pp. 4906–4910, 2002.
View at: Publisher Site | Google Scholar
S. Hu and Y. Chen, “Partial hydrogenation of benzene: a review,” Chinese Journal of Chemical Engineering, vol. 29, pp. 387–396, 1998.
View at: Google Scholar
J. A. Díaz-Auñón, M. C. Román-Martı́nez, C. Salinas-Martı́nez de Lecea et al., “[PdCl₂(NH₂(CH₂)12CH₃)₂] supported on an active carbon: effect of the carbon properties on the catalytic activity of cyclohexene hydrogenation,” Journal of Molecular Catalysis A: Chemical, vol. 153, no. 1-2, pp. 243–256, 2000.
View at: Publisher Site | Google Scholar
B. J. Meldrum and C. H. Rochester, “In situ infrared study of the surface oxidation of activated carbon in oxygen and carbon dioxide,” Journal of the Chemical Society, Faraday Transactions, vol. 86, no. 5, pp. 861–865, 1990.
View at: Publisher Site | Google Scholar
R. M. Silverstein, G. Clayton Basler, and T. C. Morril, Spectrometric Identification of Organic Compounds, Chapter III, Wiley, New York, NY, USA, 5th edition, 1991.
C. J. Pouchert, The Aldrich Library of Infrared Spectra, Wiley, New York, NY, USA, 3rd edition, 1981.
R. Haritha Gangupomu, M. L. Sattler, and D. Ramirez, “Comparative study of carbon nanotubes and granular activated carbon: physicochemical properties and adsorption capacities,” Journal of Hazardous Materials, vol. 302, pp. 362–374, 2016.
View at: Publisher Site | Google Scholar
L. Oliviero, J. Barbier Jr., D. Duprez, A. Guerrero-Ruiz, B. Bachiller-Baeza, and I. Rodrı́guez-Ramos, “Catalytic wet air oxidation of phenol and acrylic acid over Ru/C and Ru–CeO₂/C catalysts,” Applied Catalysis B: Environmental, vol. 25, no. 4, pp. 267–275, 2000.
View at: Publisher Site | Google Scholar
J. Krishna Murthy, S. Chandra Shekar, V. Siva Kumar, and K. S. Rama Rao, “Highly selective zirconium oxychloride modified Pd/C catalyst in the hydrodechlorination of dichlorodifluoromethane to difluoromethane,” Catalysis Communications, vol. 3, no. 4, pp. 145–149, 2002.
View at: Publisher Site | Google Scholar
F. Pinna, M. Signoretto, G. Strukul, A. Benedetti, M. Malentacchi, and N. Pernicone, “Ruthenium as a dispersing agent in carbon-supported palladium,” Journal of Catalysis, vol. 155, no. 1, pp. 166–169, 1995.
View at: Google Scholar
S. R. de Miguel, O. A. Scelza, M. C. Román-Martı́nez, C. Salinas-Martı́nez de Lecea, D. Cazorla-Amorós, and A. Linares-Solano, “States of Pt in Pt/C catalyst precursors after impregnation, drying and reduction steps,” Applied Catalysis A: General, vol. 170, no. 1, pp. 93–103, 1998.
View at: Publisher Site | Google Scholar
S. R. de Miguel, J. I. Vilella, E. L. Jablonski, O. A Scelza, C. Salinas-Martinez de Lecea, and A. Linares-Solano, “Preparation of Pt catalysts supported on activated carbon felts (ACF),” Applied Catalysis A: General, vol. 232, no. 1-2, pp. 237–246, 2002.
View at: Publisher Site | Google Scholar
F. Cardenas-Lizana, S. Gómez-Quero, and M. A. Keane, “Clean production of chloroanilines by selective gas phase hydrogenation over supported Ni catalysts,” Applied Catalysis A: General, vol. 334, no. 1-2, pp. 199–206, 2008.
View at: Publisher Site | Google Scholar
P. Kim, H. Kim, J. B. Joo, W. Kim, I. K. Song, and J. Yi, “Effect of nickel precursor on the catalytic performance of Ni/Al₂O₃ catalysts in the hydrodechlorination of 1,1,2-trichloroethane,” Journal of Molecular Catalysis A: Chemical, vol. 256, no. 1-2, pp. 178–183, 2006.
View at: Publisher Site | Google Scholar
G. Li, L. Hu, and J. M. Hill, “Comparison of reducibility and stability of alumina-supported Ni catalysts prepared by impregnation and co-precipitation,” Applied Catalysis A: General, vol. 301, no. 1, pp. 16–24, 2006.
View at: Publisher Site | Google Scholar
K. V. R. Chary, D. Naresh, V. Vishwanathan, M. Sadakave, and W. Ueda, “Vapour phase hydrogenation of phenol over Pd/C catalysts: a relationship between dispersion, metal area and hydrogenation activity,” Catalysis Communications, vol. 8, no. 3, pp. 471–477, 2007.
View at: Publisher Site | Google Scholar
A. B. Gaspar, G. R. dos Santos, R. de Souza Costa, and M. A. P. da Silva, “Hydrogenation of synthetic PYGAS—effects of zirconia on Pd/Al₂O₃,” Catalysis Today, vol. 133–135, pp. 400–405, 2008.
View at: Publisher Site | Google Scholar
D. O. Simone, T. Kennelly, N. L. Brungard, and R. J. Farrauto, “Reversible poisoning of palladium catalysts for methane oxidation,” Applied Catalysis, vol. 70, no. 1, pp. 87–100, 1991.
View at: Publisher Site | Google Scholar
A. B. Gaspar and L. C. Dieguez, “Dispersion stability and methylcyclopentane hydrogenolysis in Pd/Al₂O₃ catalysts,” Applied Catalysis A: General, vol. 201, no. 2, pp. 241–251, 2000.
View at: Publisher Site | Google Scholar
L. Li, Z. H. Zhu, Z. F. Yan, G. Q. Lu, and L. Rintoul, “Catalytic ammonia decomposition over Ru/carbon catalysts: the importance of the structure of carbon support,” Applied Catalysis A: General, vol. 320, pp. 166–172, 2007.
View at: Publisher Site | Google Scholar
A. Guerrero-Ruiz, P. Badenes, and I. Rodríguez-Ramos, “Study of some factors affecting the Ru and Pt dispersions over high surface area graphite-supported catalysts,” Applied Catalysis A: General, vol. 173, no. 2, pp. 313–321, 1998.
View at: Publisher Site | Google Scholar
M. Nurunnabi, K. Murata, K. Okabe, M. Inaba, and I. Takahara, “Effect of Mn addition on activity and resistance to catalyst deactivation for Fischer–Tropsch synthesis over Ru/Al₂O₃ and Ru/SiO₂ catalysts,” Catalysis Communications, vol. 8, no. 10, pp. 1531–1537, 2007.
View at: Publisher Site | Google Scholar
V. Ragaini, R. Carli, C. L. Bianchi, D. Lorenzetti, and G. Vergani, “Fischer—Tropsch synthesis on alumina-supported ruthenium catalysts I. Influence of K and Cl modifiers,” Applied Catalysis A: General, vol. 139, no. 1-2, pp. 17–29, 1996.
View at: Publisher Site | Google Scholar
K. Lu and B. Tatarchuk, “Activated chemisorption of hydrogen on supported ruthenium I. Influence of adsorbed chlorine on accurate surface area measurements,” Journal of Catalysis, vol. 106, no. 1, pp. 166–175, 1987.
View at: Publisher Site | Google Scholar
T. Narita, H. Miura, M. Ohira et al., “The effect of reduction temperature on the chemisorptive properties of Ru/Al₂O₃: effect of chlorine,” Applied Catalysis, vol. 32, pp. 185–190, 1987.
View at: Publisher Site | Google Scholar
T. Narita, H. Miura, K. Sugiyama, T. Matsuda, and R. D. Gourales, “The effect of reduction temperature on the chemisorptive properties of Ru/SiO₂: effect of chlorine,” Journal of Catalysis, vol. 103, no. 2, pp. 492–495, 1987.
View at: Publisher Site | Google Scholar
C. R. Lederhos, J. M. Badano, M. E. Quiroga, F. Coloma-Pascual, and P. C. L’Argentière, “Influence of Ni addition to a low-loaded palladium catalyst on the selective hydrogenation of 1-heptyne,” Química Nova, vol. 33, no. 4, pp. 816–820, 2010.
View at: Publisher Site | Google Scholar
M. J. Maccarrone, C. R. Lederhos, G. Torres et al., “Partial hydrogenation of 3-hexyne over low-loaded palladium mono and bimetallic catalysts,” Applied Catalysis A: General, vol. 441-442, pp. 90–98, 2012.
View at: Publisher Site | Google Scholar
NIST X-ray Photoelectron Spectroscopy Database-NIST Standard Reference Database 20 Version 4.1, National Institute of Standards and Technology, Gaithersburg, MD, USA, December 2017, https://srdata.nist.gov/xps/.
M. M. Telkar, J. M. Nadjeri, C. V. Rode, and R. V. Chaudhari, “Role of a co-metal in bimetallic Ni–Pt catalyst for hydrogenation of m-dinitrobenzene to m-phenylenediamine,” Applied Catalysis A: General, vol. 295, no. 1, pp. 23–30, 2005.
View at: Publisher Site | Google Scholar
J. Juan-Juan, M. C. Roman-Martinez, and M. J. Illan-Gomez, “Catalytic activity and characterization of Ni/Al₂O₃ and NiK/Al₂O₃ catalysts for CO₂ methane reforming,” Applied Catalysis A: General, vol. 264, no. 2, pp. 169–174, 2004.
View at: Publisher Site | Google Scholar
B. W. Hoffer, A. D. van Langeveld, J. P. Janssens, R. L. C. Bonné, C. M. Lok, and J. A. Moulijn, “Stability of highly dispersed Ni/AlO catalysts: effects of pretreatment,” Journal of Catalysis, vol. 192, no. 2, pp. 432–440, 2000.
View at: Publisher Site | Google Scholar
E. Heracleous, A. F. Lee, K. Wilson, and A. A. Lemonidou, “Investigation of Ni-based alumina-supported catalysts for the oxidative dehydrogenation of ethane to ethylene: structural characterization and reactivity studies,” Journal of Catalysis, vol. 231, no. 1, pp. 159–171, 2005.
View at: Publisher Site | Google Scholar
M. Boudart, “Catalysis by supported metals,” Advances in Catalysis, vol. 20, pp. 153–166, 1969.
View at: Publisher Site | Google Scholar
J. A. Pajares, P. Reyes, L. A. Oro, and R. Sariego, “Hydrogenation of 1-hexene by rhodium catalysts,” Journal of Molecular Catalysis, vol. 11, no. 2-3, pp. 181–192, 1981.
View at: Publisher Site | Google Scholar
M. J. Maccarrone, G. Torres, C. Lederhos et al., “Kinetic study of the partial hydrogenation of 1-heptyne over Ni and Pd supported on alumina,” in Hydrogenation, I. Karamé, Ed., Chapter 7, pp. 159–184, InTech, Rijeka, Croatia, 2012.
View at: Google Scholar

Copyright

Copyright © 2018 Nicolás Carrara et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2949

Downloads

1523

Citations