TY - JOUR A2 - Seelam, Prem Kumar AU - Haghighi, Maryam AU - Fereidooni, Mehranoosh PY - 2021 DA - 2021/12/24 TI - Silica Coating of Metal-Loaded H-ZSM-22 to Form the Core-Shell Nanostructures: Characterization, Textural Properties, and Catalytic Potency in the Esterification of Oleic Acid SP - 5321383 VL - 2021 AB - In this study, ZSM-22 was synthesized using N,N-diethylaniline as a template through a hydrothermal method. The proton and various metals such as zirconium, strontium, and iron were immobilized on the surface of obtained zeolites through the ion exchange method. The catalysts were studied by Fourier-Transform Infrared Spectroscopy (FT-IR), X-Ray Diffraction (XRD), Brunauer–Emmett–Teller (BET) adsorption isotherms, Transmission Electron Microscope (TEM), Scanning Electron Microscope (SEM), Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES) elemental analysis, and Temperature-Programmed Desorption of ammonia (TPD-NH3) technique for determining the number of acid sites. In the esterification reaction of oleic acid, the operating conditions such as catalyst dosage, temperature, molar ratio of methanol to oil, and reaction time were optimized and adjusted at 11 wt%, 70°C, 10 : 1, and 48 h subsequently. The maximum yield% of 48.07% was achieved in the presence of Zr-H-ZSM-22 at optimum conditions. In order to improve the efficiency of three zeolites Zr-H-ZSM-22, Fe-H-ZSM-22, and Sr-H-ZSM-22, the core-shell structures with SiO2 coating were prepared. Zr-H-ZSM-22@SiO2 was less active than Zr-H-ZSM-22 due to the SiO2 coverage of Lewis active sites. SN - 1687-806X UR - https://doi.org/10.1155/2021/5321383 DO - 10.1155/2021/5321383 JF - International Journal of Chemical Engineering PB - Hindawi KW - ER -