Comparison of Marginal and Internal Adaptation in Endocrowns Milled from Translucent Zirconia and Zirconium Lithium Silicate Table 1 The physical properties of ceramic materials used in the study.
Group Ceramic type Flexural strength Fracture toughness (SEVNB) E-modulus Vickers hardness Brittleness index ZLS (Celtra Duo) Zirconium lithium silicate ceramic Mill and polish: 210 MPa 2 MPa m0.5 Approx. 70 6.86 GPa 2.84 µ m−1/2† [15 ] Mill and fire: 370 MPa Zr (DD Bio ZX2 ) High-translucent zirconium oxide ceramic 1100–1250 MPa >10 MPa m0.5 >200 5.41–15.47 GPa† [18 , 19 ] 1.52–3.15 μ m−1/2† [18 ]
According to the manufacturer’s claim.
† According to the available data on the same material type, but different brand, due to the lack of data on the particular brand used in the present study.