Effect of Elemental Composition on the Structure, Electrochemical Properties, and Ozone Production Activity of Ti/SnO2-Sb-Ni Electrodes Prepared by Thermal Pyrolysis Method

Figure 2

CVs of a representative Ti/SnO₂-Sb-Ni electrode between −0.05 and 1.75 V in three 100 mV ranges in 0.1 M H₂SO₄ solution. Scan rate: 50 mV s⁻¹. The inset shows CVs of the electrode in the three 100 mV ranges at different scan rates: 5, 10, 20, 30, 40, and 50 mV s⁻¹ form a to f, respectively. The CVs at higher scan rates are not shown.