Status of Biomass Derived Carbon Materials for Supercapacitor Application

Enock, Talam Kibona; King’ondu, Cecil K.; Pogrebnoi, Alexander; Jande, Yusufu Abeid Chande

doi:https://doi.org/10.1155/2017/6453420

International Journal of Electrochemistry

On this page

Abstract Introduction Conclusion References Copyright Related Articles

Review Article | Open Access

Volume 2017 | Article ID 6453420 | https://doi.org/10.1155/2017/6453420

Status of Biomass Derived Carbon Materials for Supercapacitor Application

Talam Kibona Enock,^1,2Cecil K. King’ondu ,^1,3Alexander Pogrebnoi,¹and Yusufu Abeid Chande Jande¹

Academic Editor: Sergio Ferro

Received24 Aug 2016

Revised16 Dec 2016

Accepted25 Dec 2016

Published31 Jan 2017

Abstract

Environmental concerns and energy security uncertainties associated with fossil fuels have driven the world to shift to renewable energy sources. However, most renewable energy sources with exception of hydropower are intermittent in nature and thus need storage systems. Amongst various storage systems, supercapacitors are the promising candidates for energy storage not only in renewable energies but also in hybrid vehicles and portable devices due to their high power density. Supercapacitor electrodes are almost invariably made of carbon derived from biomass. Several reviews had been focused on general carbon materials for supercapacitor electrode. This review is focused on understanding the extent to which different types of biomasses have been used as porous carbon materials for supercapacitor electrodes. It also details hydrothermal microwave assisted, ionothermal, and molten salts carbonization as techniques of synthesizing activated carbon from biomasses as well as their characteristics and their impacts on electrochemical performance.

1. Introduction

As climate change concerns escalate and the depletion of fossil fuels becomes more eminent, renewable energy sources have gained momentum as viable cost-effective and environment-friendly energy sources. However, most renewable energy sources are intermittent and thus need storage strategies. Currently, secondary batteries are the most used storage systems. Batteries have high energy density but low power density. Since batteries store energy chemically, both the electrolytes and electrodes undergo physicochemical changes during charging and discharging, thereby leading to low cyclability and short lifespan. These limit their applications in energy storage. Contrary to batteries, supercapacitors have high power density and cycling stability [1–3]. Nonetheless, their utility in energy storage is limited by their low energy density, relatively high effective series resistance, and high cost. This review is focused on the status of maximum energy density attained and low cost electrode materials made so far for supercapacitor electrodes.

Supercapacitors have energy density lower than that of lead acid and lithium ion batteries; however, they have higher power density and exhibit long life cycles, high cyclability, and low safety concerns compared to secondary batteries [3–5]; they have attracted the attention as new energy storage system. The general description of comparison between batteries, conventional capacitors, and supercapacitors is given in Table 1.

Most research studies are currently focused on increasing the energy density of supercapacitors. Supercapacitors consist of electrode materials, separators, and electrolytes. The energy density and power density of a supercapacitor can be increased by increasing both specific capacitance () and operating voltage () window as well as reducing the equivalent series resistance (R). The voltage window can be increased by a good choice of electrolyte, while the specific capacitance of the supercapacitor can be improved by either finding new electrode materials or optimizing the existing materials [4] in terms of interconnected porosity, electrical conductivity, and surface area among others.

In principal, supercapacitors store energy based on two capacitive behaviors: Electrical Double-Layer (EDL) capacitance and pseudocapacitance. While the former is due to electrostatic interaction, pseudocapacitance is due to faradic phenomenon involving fast and reversible electrochemical reactions. In pseudocapacitance, the redox reactions are between the electrolyte and the electrode materials. The products of redox reactions are therefore electrons which are then transferred through electrode/electrolyte interfaces [4]. The EDL has the advantage that electrochemical kinetics is not limited by polarization resistance and no swelling of the active materials is experienced. The energy is stored in two porous electrodes with current collector on each electrode; the stored energy is released when charges accumulated at the electrode discharge as shown in Figure 1. The number of charges stored in the electrode is proportional to the surface of the electrode, and energy stored is proportional to the amount of charge stored. Therefore, materials with high surface area are regarded as good candidates for supercapacitor electrode.

The improvement of supercapacitor performance can be attributed through discovery of new electrode materials, understanding of ions behavior in small pores, and designing hybrid system by combining faradic and capacitive electrodes.

2. Materials for Supercapacitor Electrodes

2.1. Carbon Materials for Supercapacitor Electrodes

Different materials have been investigated as electrode materials for supercapacitors, the materials conducting polymers, porous materials, and metal oxides. The parameters like optimum pore size and high surface area of the electrode materials for a given electrolyte determine the performance of supercapacitor in terms of power density and energy storage capability [8]. High surface area is important because the energy in electrochemical storage systems is stored on the surface, while the pores size facilitates the storage and transport of charges. Carbon materials are more attractive because they are available in different forms (such as fibers, powders, nanotubes, and nanospheres) and are rich in dimensionality [2].

The microstructure and surface chemistry of carbon can be adjusted easily, thus altering the electrochemical performance of the material [9]. It has been reported further that carbon materials based electrodes have reasonably high electrical conductivity, high thermal stability, excellent corrosion resistance, tailorable pore distribution, relatively high surface area, low cost, and satisfactory compatibility with a number of materials in making composites [2, 10].

2.1.1. Activated Carbons

Porous carbon is prepared through different methods depending on the intended application. One of the mainly used methods for supercapacitors is activating the carbon either chemically or physically. Activated carbon is synthesized through carbonization of carbon precursor followed by activation at temperature around 600–800°C in an inert atmosphere. The type of carbon precursor is one of the determining factors of the properties of the activated carbons.

Physical activation involves two processes; first is pyrolysis, in an inert atmosphere, of the carbon precursor at temperatures between 400 and 1000°C, and second is gasification, where the porosity and surface area are developed using oxidizing gases such as carbon dioxide or air and steam between 700 and 1200°C [11–13]. Pyrolysis is intended to remove all volatile materials in the precursor, while gasification opens some closed pores by burning away the tar-like pyrolysis product within the pores. Furthermore, the active sites increase as more organics are burned away by oxidizing agent [14].

In contrast, chemical activation involves using potassium hydroxide [15–19], sodium hydroxide [20, 21], phosphoric acid [22–24], zinc chloride [19, 25, 26], and nitric acid and sulphuric acid [27]. Phosphoric acid and zinc chloride act as dehydrating agent, while potassium hydroxide is an oxidant. In comparison to physical activation method, chemical activation has the following advantages: () the pores are well developed and pore size is controllable, () materials with high surface area are produced, () yield carbon is high, () it involves only one step, and () it has lower pyrolysis temperature [14]. For energy storage applications such as supercapacitors, the first two advantages strengthen the use of chemical activation.

For KOH activation, which is mainly applied to supercapacitor electrode materials preparation, the ratio of alkali/carbon varies from 1 : 1 to 5 : 1 depending on the concentration of the impregnating solution [19]. The excess KOH is removed by suspending the activated carbon in 0.1 M HCl solution and then washed with water until pH of 7 is achieved. Samples are then oven-dried ready to be used in electrochemical testing and other characterizations. Activated carbons sometimes exhibit a high Brunauer-Emmet-Teller (BET) surface area which exceeds 2500 m²g⁻¹ and pore volume which is close to 2 cm³g⁻¹ [28]. The majority of pores in the activated carbon are micropores and only small number of mesopores; this is because at higher temperatures most of mesopores break and the pore diameter decreases [29].

Due to the availability, cheap cost, and ability to become highly porous after carbonization, different kinds of biomass feedstock have been used as precursors for carbon. Understanding the biomass derived porous carbon materials and their properties is of importance in order to match the carbon properties with those of supercapacitors. Porous carbon materials are classified depending on their pore width; those with < 2 nm pore width are classified as microporous, those with 2 to 50 nm pore width are classified as mesoporous, while those with pore width greater than 50 nm are classified as macroporous [4, 30]. For supercapacitors application, both micropores and mesopores play an important role. Micropores are important in storing charges, while mesopores store and facilitate charge transfer. The reported surface areas and capacitance exhibited by different biomass derived carbon materials are as described in Table 2. Generally, the higher the specific surface area of activated carbon is, the higher the active surface area is. However, despite high specific surface areas attained for activated carbons, that is, around 2500 to 3000 m²g⁻¹, some activated carbons exhibit low specific capacitance as depicted in Table 1. This might be due to wide pore size distributions, pore size, type of the electrolyte used, scan rate, mass, or surface area of the electrode. Small pore size of 0.68 nm limits the electrolyte from accessing the entire active surface area of activated carbon [31].

Though it is suggested that the specific capacitance and BET surface area of activated carbon have close correlation, it is not the case for all carbon precursors as shown in Figure 2. The relationship between surface area and capacitance is not always obvious due to the fact that capacitance is contributed by other factors such as pore size, electrical conductivity, and pore distribution and interconnectivity [31, 54].

The increase in the fraction of pore size which cannot be accessed by the electrolyte (when the average pore size is below 0.68 nm) in organic electrolyte is expected to decrease the capacitance [31]; however, an anomalous behavior is observed, where the capacitance increases with the pores having pore size of less than 1 nm in acetonitrile organic electrolyte [63]. Figure 2 shows that there is no direct correlation between capacitance and the pore size of the electrode materials. Actually many factors have a huge impact on the capacitance: the materials surface chemistry, method of preparing electrodes, the electrolyte used, and electrode testing method.

Apart from plant wastes, animal wastes have been studied as potential carbon precursors for supercapacitors electrode. To date, cow dung [55], animal bones [56], chicken egg membranes [58], and human hair [59, 64] have been reported in the literature. The physical and electrochemical properties of these wastes are described in Table 3.

In order to know how fast energy can be stored in a unit volume of materials volumetric capacitance is of importance. Factors affecting the volumetric capacitance were reviewed by Wang and coworkers [65]. Surprisingly, a good number of researches overlook this parameter when evaluating the suitability of materials for supercapacitor electrodes application. At the same time, few authors had taken into account the volumetric capacitance for characterizing the biomass derived carbon. Xie et al. [66] composited corn straw and soy protein to obtain a surface area of 1412.9 m²g⁻¹ with gravimetric capacitance and volumetric capacitance of 321.1 F g⁻¹ and 213 F cm⁻³, respectively, at 20 A g⁻¹ in 6 M KOH. When soybean was chemically activated after carbonization and tested for supercapacitor electrodes, gravimetric capacitance and volumetric capacitance of 260 F g⁻¹ and 210 F cm⁻³, respectively, was obtained in H₂SO₄ [67]. In the same study, gravimetric capacitance and volumetric capacitance of 176 F g⁻¹ and 102 F cm⁻³, respectively, was obtained in Li₂SO₄ electrolyte. It was further revealed that volumetric capacitance decreased with activating temperature increase and it was an opposite trend for the gravimetric capacitance. The low volumetric capacitance at high temperature may be caused by low conductivity of biomass derived carbons as the high surface area decreases the density sites. Eukaryotic organism (Auricularia) was used as precursor for synthesizing porous carbon which exhibited bulk density of 0.96 g cm⁻³, surface area of 1103 m² g⁻¹, volumetric capacitance of 360 F cm⁻³, and cyclic stability of 99% after 10000 cycles were obtained [68]. It has been reported that the heteroatom functional groups of biomass derived carbon enhance volumetric capacitance. For example, high volumetric capacitance of 468 F cm⁻³, high packing density of 1.1 g cm⁻³, and capacitance retention of 91% after 10000 cycles were achieved when functionalized porous carbon was synthesized from soybean [69].

The differences in the reported capacitance are attributed to the method of testing. It is reported that the three-electrode cell gives higher capacitance results compared to its two-electrode counterpart [70]; thus there is a need to establish standardized best practice of determining the capacitance of the material. Although the testing method may be the same for different studies, differences in mass loading, electrode thickness, type and amount of binder, and type of current collector have huge impact on the capacitance obtained.

The presence of surface functionalities and heteroatoms such as O and N on carbon also play an important role in the pseudocapacitance behavior of the electrode [71, 72]. Oxygen comes from both the activation and biomass itself, while nitrogen can come from the biomass or is introduced into the carbon through doping [73]. It has been reported that the capacitance of O and N containing carbonized chicken egg shell membrane is 297 F g⁻¹ with cyclic efficiency of 97% after 10000 cycles [58]. The activated carbon from the same precursor has specific capacitance of 203 F g⁻¹, despite the fact that the specific surface area was 7 times higher than carbonized chicken egg shell membrane. It has been reported also that oxygen- and nitrogen-rich activated carbon enhances the specific capacitance differently. While oxygen-rich activated carbon exhibits lower capacitance because the electrolyte diffusion into pores is hindered by carboxyl surface, the nitrogen-rich one exhibits higher capacitance [52, 74]. Furthermore, it is reported that the adsorption and transport of electrolyte ions are enhanced by doping activated carbon with heteroatom such as sulphur [72, 75, 76]. Heteroatom increases the wettability of the electrode which in turn increases the capacitance; thus studies on doping different heteroatoms on the activated carbon are emphasized.

Microwave assisted heat treatment is one of the methods of activating carbon for supercapacitor applications. It is a facile, controllable, fast, and energy-saving technique. When carbon xerogel was activated chemically using microwave radiation, microspores and mesopores were produced at a time range between 6 and 30 min [77]. Although microwave radiation method produces well-modified surface chemistry of activated carbons, it causes significant reduction in micropore volume and size [78, 79].

Hydrothermal carbonization (HTC) is another way of producing porous carbon for supercapacitor electrodes. In this method, a mixture of water and carbon precursor is thermally treated at temperature ranges of 150–300°C and 300–800°C for low and high temperature HTC, respectively [80, 81]. Apart from high solid carbon yield, the method also reduces the oxygen and hydrogen content [82, 83] and produces materials with very high BET surface area. Jain and coworkers obtained BET and mesopore areas of up to 2440 and 1121 m²g⁻¹, respectively, after hydrothermal treatment of coconut shells with ZnCl₂ and H₂O₂ at temperature of 275°C [84]. When the same material was chemically activated using ZnCl₂ at 500°C for 3 h by Azevedo et al. [85], BET surface area of 1266 m²g⁻¹ was obtained. Elaigwu and Greenway [86] compared the chemical and structural properties of carbon derived from Prosopis africana waste plant material prepared by conventional hydrothermal and microwave assisted hydrothermal carbonization. They found that that microwave assisted hydrothermal carbonization was faster in decomposing Prosopis africana as the degree of structure alteration was achieved within a short time when compared to the conventional approach [86].

The comparison can easily be depicted in Table 4, where CPS represents combined pyrolysis and steam activation, OHCZ represents optimal hydrothermal treatment and chemical activation with ZnCl₂, CZ represents chemical activation with ZnCl₂, and CZP represents chemical activation with ZnCl₂ followed by physical activation. It is worth mentioning that the precursor for all the above-mentioned methods is the same (coconut shell).

The porosity of the carbon is also influenced by type of activation; for example, when firewood and pistachio were carbonized and activated using steam and KOH, KOH activated carbon had 9.2–15.3% mesopores, while steam activated carbon had 33.3–49.5% [88]. On the other hand, the surface capacitance has been reported to increase with the increase in mesopore content [89].

Electrochemical performances of different biomass derived carbon materials have also shown strong correlation between capacitance, morphology, and the method used to prepare the carbon. For instance, water hyacinth (WH) has been used to prepare porous carbon by different authors; however, their results differ probably due to their methods, morphology obtained, and/or surface area [47, 48, 90]. Senthilkumar and coworkers [48] activated the WH derived carbon using ZnCl₂ and obtained the porous carbon with no particular shape (Figure 3(a)); the specific capacitance of 472 F g⁻¹ was obtained in aqueous electrolyte H₂SO₄. Kurniawan and coworkers [47] developed microspheres (Figure 3(b)) through subcritical water carbonization followed by KOH activation and microwave treatment; the specific capacitance was 179.6 F g⁻¹ in aqueous electrolyte. From the same carbon precursor, Syarif and Pardede [90] developed porous carbon through hydrothermal treatment followed by microwave pyrolysis, the carbon has a shining bead chain and waffle structures with cavities, the capacitance obtained in aqueous electrolyte (H₂SO₄) was 0.0218 F g⁻¹, no conductive and activating agent was added, and the capacitance increased 10 times when graphite was added to the carbon in the ratio of 3 : 7. Carbon sheets (Figure 3(c)) were produced by Wu and coworkers [49] through acid (HCl) treatment and pyrolytic carbonization and KOH activation of water hyacinth biomass. Micropores and mesopores were developed which in electrochemical testing achieved specific capacity of 273 F g⁻¹ at current density of 1 A g⁻¹.

(a) SEM micrography for water hyacinth derived carbon [48]

(b) SEM images of water hyacinth derived carbon activated using ZnCl2 [47]

(c) SEM images for water hyacinth activated with KOH [49]

It was further shown that the capacitance of water hyacinth derived carbon electrode increased from 472 to 912 F g⁻¹ when potassium iodide (0.08 M KI) was added to 1 M H₂SO₄ electrolyte, signifying the effect of electrolyte [48]. The addition of KI in the electrolyte enhanced the capacitance because KI can produce redox pairs (3I⁻/, /, and others) during electrochemical processes, which in turn could easily access the small micropores and mesopores. Through hydrothermal treatment, interconnected graphitic carbon nanosheets can also be produced. For example, Wang and coworkers [51] developed nanosheets from hemp back fibers with high specific surface area up to 2287 m²g⁻¹ with capacitance retention of 72–92% at current density of 100 A g⁻¹. The study also revealed that the materials were stable at different temperatures of 20, 60, and 100°C.

Ionothermal carbonization is another method of synthesizing porous carbon from biomass, where only one step is required. The ionic liquids possess high chemical and thermal stability, low melting point, electrical and ionic conductivity, and negligible vapor pressure. This method has been reported to produce carbon with high surface area and large pore volume [91]. A high surface area (2160 m²g⁻¹) and total pore volume of 1.74 cm³g⁻¹ were obtained when carbon was synthesized from glucose [92]. In this study, KCl-ZnCl₂ system molar ratio was varied to act as template/solvent during carbonization; it was further revealed that the higher content of KCl increased the pore size and surface area. The gravimetric capacitance obtained was 206 F g⁻¹. Lin et al. [93] synthesized microporous and mesoporous carbon from fructose through one-step ionothermal method using iron. The surface area of 1200 m²g⁻¹, pore volume of 0.8 cm³g⁻¹, and specific capacitance of 245 F g⁻¹ at current density of 1 A g⁻¹ were obtained. In the study different masses of fructose were dispersed in 10 mL of 1-butyl-3-methylimidazolium tetrachloroferrate [Bmim][FeCl₄]. [Bmim][FeCl₄] was used as template, solvent, and catalyst with advantage that it can be reused after recovery. Other biomass derived structured carbons were produced ionothermally from carbohydrates [94], sugar bagasse [95], and bamboo [96]. However, these carbons were not tested for supercapacitor applications.

Molten salt carbonization (MSC) is another method of synthesizing porous carbon from biomass, in which the molten salt cracks the large molecules of biomass. In MSC, the salt involved is melted at its melting point; then biomass is immersed into the molten salt and carbonized at temperature greater than 400°C in inert atmosphere. After carbonization, the furnace is cooled to room temperature and the product is washed with HCl and distilled water in order to remove salts within the product. It is reported that the particle size of the biomass alters the yield [97]. Table 5 shows different biomasses carbonized in different salts and the obtained gravimetric capacitance and specific surface area. It is difficult to tell the best biomass or salt because the carbonization temperature and electrolyte for electrochemical testing are different.

2.1.2. Carbon Aerogel Derived from Biomasses

Carbon aerogel is another form of carbon used in supercapacitor electrodes, whereby the porous carbon is produced through pyrolysis of organic aerogels [103]. The porosity is a result of a combination of interconnected colloidal particles. The porous carbon materials can be composites, monoliths, powders, microspheres, or thin films. The aerogels carbon materials have been reported to exhibit higher surface area compared to activated carbon [104]. Carbon fiber aerogels with surface areas ranging from 1536 to 2436 m²g⁻¹ and pore size ranging between 1.0 and 4.0 nm exhibited high specific capacitance of 282 F g⁻¹ (1 A g⁻¹) in 6 M KOH electrolyte [51, 105].

A green technology of fabricating sponge-like carbonaceous hydrogels/aerogels from watermelon was developed by Wu and coauthors [106]. The study revealed that watermelon can be polymerized and carbonized to form carbonaceous mesosphere and nanofibers during hydrothermal reaction.

The cellulose from bagasse has been utilized as the raw materials for carbon aerogel. Two procedures were followed. Firstly, cellulose was dissolved in a solvent mixture of NaOH/urea/H₂O and super cooling in −12°C. Secondly, the gels were regenerated in water at room temperature and then frozen at −80°C [107]. The synthesized aerogels exhibited large channels with average diameter in the range of 50–100 nm. The specific capacitance of the assembled supercapacitor was 142.1 F g⁻¹ at current density of 0.5 A g⁻¹.

In another study, the 3D N-doped carbonaceous aerogels were produced through one-pot hydrothermal synthesis using the soft tissue biomass of watermelon as a source of aerogel. The method produced specific capacitance of 281 F g⁻¹. It has been reported that nitrogen doped porous carbon possesses higher specific capacitance compared to the undoped porous carbon because of pseudocapacitive behavior of nitrogen functional groups [108].

2.2. Metal Oxides and Carbon/Metal Oxide Composites

The energy density of a carbon material is a function of both capacitance and electrical conductivity exhibited by the electrode. Though activated carbons have low capacitive behavior, their high electrical conductivity qualifies them for supercapacitor electrode. On the other hand, transition metal oxides (TMO) have high capacitance but low conductivity. Metal oxide electrodes have poor cyclic stability due to the cracks caused by the strain in the metal oxide during charging and discharging processes [109].

Studies on the application of ruthenium oxide (RuO₂) [110], manganese (IV) oxide (MnO₂), cobalt (II, III) oxides (Co₃O₄), nickel oxide (NiO) [111], molybdenum trioxide (MoO₃), molybdenum (IV) oxide (MoO₂), and vanadium nitride (VN) as the electrochemical active materials have been conducted [112]. Though RuO₂ has excellent capacitance, its high cost, toxic nature, and low porosity limit its application. Nickel oxide, cobalt oxide, and manganese dioxide are inexpensive and thus derive interest in improving their electrochemical performance.

Efforts have been made to composite biomass derived carbon and metal oxides so as to capture the strength of the two in increasing the energy density without sacrificing the high power density. An important consideration related to porous carbon/metal oxide is their performance in terms of capacitance, stability, power, and energy densities. Sawdust derived carbon was directly composited with FeCl₃ and TiCl₂ and the composite was oxidized in concentrated nitric acid [113]. From this study, it was revealed that the metal oxide loading and surface functionalities affect the voltammograms shapes. Moreover, with exception of RuO₂, the conductivity of other transition metal oxides is poor, resulting in low power and energy density. This is because the IR loss is very large at high current density caused by both the charge transfer resistance of the electrode and sheet resistance [114].

Based on its pseudocapacitive behavior, RuO₂ has been found to be an excellent electrode. RuO₂/carbon composite prepared by Lin et al. [115] exhibited a specific surface area of 520 m²g⁻¹ at current density of 1 A g⁻¹ and specific capacitance of 256 F g⁻¹. In another study, colloidal method was used to prepare a nanostructured composite of RuO₂ and carbon. The specific capacitance of RuO₂/carbon composite electrode (40% RuO₂) was reported to be 407 F g⁻¹ as calculated from cyclic voltammetry. When the contribution of double-layer capacitance resulting from carbon was subtracted, the specific capacitance of RuO₂·χH₂O was approximately 863 F g⁻¹. The volumetric capacitance of the composite increased as the weight of RuO₂ increased to 40 wt.% and then dropped due to increased particle size of RuO₂ [116]. However, due to the high cost of RuO₂, its practical application in supercapacitors is limited; thus exploitation of alternative metal oxides is very necessary.

The specific area and specific capacitance have been reported to increase when carbon is composited with metal oxide. Specific surface area of NiO/carbon composite increased from 150 m²g⁻¹ for NiO to 700 m²g⁻¹ when NiO was composited with carbon, while the specific capacitance increased from 20 to about 100 F g⁻¹ [117].

Apart from activated carbon being composited with metal oxides, attempts have been made to composite aerogels made from bagasse with Fe₂O₃. The aerogel/Fe₂O₃ composite exhibited high specific capacitance of 333.1 F g⁻¹ at current density of 1 A g⁻¹ with excellent cyclic stability of 96% at 1000 cycles [106]. The variation of specific capacitance, energy density, and power density of different composites can be seen in Table 6.

It has been shown that the composition with lowest metal oxide content displays the highest capacitance. This is attributed to the fact that, at high metal oxide content, the fraction of accessible active surface area is low and the resistance is high.

2.3. Activated Carbon/Conducting Polymers

Conducting polymers have also been used as electrode materials for supercapacitors due to their good electrochemistry, simplicity in doping, and easy preparation. However, during the charge-discharge cycles, the sites in polymers responsible for redox are not stable; thus resulting in low life cycle of the conducting polymers electrode. Wang and coworkers coated activated carbon with polyaniline (PANI) through polymerization of aniline using cyclic voltammetry. It was revealed that the PANI electrode and PANI-activated carbon composite maintained cyclic stability of 65 and 92%, respectively, at 50 cycles and high specific capacitance of 587 F g⁻¹ [121].

Lin and Teng demonstrated that the capacitance of a carbon electrode can be increased by at least 50% if 5 wt.% of polyaniline is deposited on the carbon [122]. It has been further reported that the composite made from natural bamboo and polyaniline attained high energy density of 47.5 Wh kg⁻¹, demonstrating that the composite was a good candidate for supercapacitor [123].

2.4. Activated Carbon/Carbon Nanotubes Composites

The electrochemical performance of activated carbon derived from biomass when composited with carbon nanotube (CNTs) has also been investigated. A coconut shell derived activated carbon was composited with CNTs. The capacitance of the coconut derived activated carbon alone was 92 F g⁻¹, while that of carbon nanotube alone was 25 F g⁻¹. However, when the two were composited, the capacitance decreased to 88 and 50 F g⁻¹ at 15 and 50 wt.% CNTs content, respectively [124]. The test was conducted in the nonaqueous electrolyte (NEt₄BF₄ 1.5 M in acetonitrile). These results imply that CNTs are not good for composites.

A carbon nanotube/self-adhesive carbon grain composite has been studied by Farma and coworkers [125]. The carbon grains were derived from oil palm empty fruit bunch fibers of different palm species. The specific capacitance obtained was 55, 77, and 85 F g⁻¹ for composites carbonized at 600, 700, and 800°C. The composite exhibited BET surface area of 434, 415, and 485 m²g⁻¹, though both the surface area and specific capacitance decreased when the CNTs were added; the equivalent series resistance (ESR) decreased by a factor of around 84, which in turn increased the power density as low ESR increases conductivity. Also specific capacitance fading was reduced significantly.

Porous structures from activated carbon, carbon aerogels, carbon nanotubes, and composites favor the accessibility of ions in an electrode. However, the type of an electrolyte used which is not the main focus of our review has significant effect. Aqueous, nonaqueous, and organic electrolytes are the mostly used electrolytes in energy storages.

3. Conclusion

In this review, different carbon forms produced from various biomass have been discussed. It has been shown that the capacitance and energy density of biomass based supercapacitor electrode depend on carbon nanostructures produced from individual carbon precursor. The influence of the pore structure (size and distribution), surface area, and heteroatoms present on the carbon has been discussed. From the perspective of this review, the following conclusions were drawn:(1)The variation of physical characteristics not only necessitates finding new materials for supercapacitor electrodes but also argues for improvement of already studied materials be it through method of preparation or compositing with other materials.(2)Though hydrothermal treatment route of producing carbonaceous material for supercapacitor electrode seems to be more efficient, the high temperatures and pressure involved increase the cost. Therefore, there is a need to search for catalysts to lower reaction temperature.(3)Most biomass derived electrodes have been demonstrating high cyclic capability; thus promising future commercial use.(4)The gravimetric capacitance attained by majority of the biomass derived carbon materials is not high enough; thus there is a need for compositing with other materials to improve the capacitance and energy density. The synergetic effect between metal oxides and biomass derived carbon needed to be optimized as the oxide contributes in the composite by providing high capacitance, while carbon ensures high conductivity and good rate capability.(5)Despite the achievements in synthesis of biomass derived carbon materials for supercapacitors, an optimization of the structure of materials is desirable to increase both gravimetric capacitance and volumetric capacitance.(6)The hydrothermal, ionothermal, and salt carbonization methods have shown high suitability in synthesizing of porous carbon materials; besides, a combination of methods may be suggested for further enhancement of the materials and energy storage devices.

Competing Interests

The authors declare that there are no competing interests regarding the publication of this paper.

References

M. S. Halper and J. C. Ellenbogen, Supercapacitors: A Brief Overview, The MITRE Corporation, Mclean, Va, USA, 2006.
L. L. Zhang and X. S. Zhao, “Carbon-based materials as supercapacitor electrodes,” Chemical Society Reviews, vol. 38, no. 9, pp. 2520–2531, 2009.
View at: Publisher Site | Google Scholar
A. Burke, “Ultracapacitors: why, how, and where is the technology,” Journal of Power Sources, vol. 91, no. 1, pp. 37–50, 2000.
View at: Publisher Site | Google Scholar
B. E. Conway, Electrochemical Supercapacitors: Scientific Fundamentals and Technological Applications, Springer US, Boston, Mass, USA, 1999.
View at: Publisher Site
M. Winter and R. J. Brodd, “What are batteries, fuel cells, and supercapacitors?” Chemical Reviews, vol. 104, no. 10, pp. 4245–4270, 2004.
View at: Publisher Site | Google Scholar
J. R. Miller and A. F. Burke, “Electrochemical capacitors: challenges and opportunities for real-world applications,” The Electrochemical Society Interface, vol. 17, no. 1, pp. 53–57, 2008.
View at: Google Scholar
V. V. N. Obreja, “On the performance of supercapacitors with electrodes based on carbon nanotubes and carbon activated material—a review,” Physica E: Low-Dimensional Systems and Nanostructures, vol. 40, no. 7, pp. 2596–2605, 2008.
View at: Publisher Site | Google Scholar
P. Simon and Y. Gogotsi, “Materials for electrochemical capacitors,” Nature Materials, vol. 7, no. 11, pp. 845–854, 2008.
View at: Publisher Site | Google Scholar
F. Béguin, V. Presser, A. Balducci, and E. Frackowiak, “Carbons and electrolytes for advanced supercapacitors,” Advanced Materials, vol. 26, no. 14, pp. 2219–2251, 2014.
View at: Publisher Site | Google Scholar
E. Frackowiak and F. Béguin, “Carbon materials for the electrochemical storage of energy in capacitors,” Carbon, vol. 39, no. 6, pp. 937–950, 2001.
View at: Publisher Site | Google Scholar
C. Bouchelta, M. S. Medjram, O. Bertrand, and J.-P. Bellat, “Preparation and characterization of activated carbon from date stones by physical activation with steam,” Journal of Analytical and Applied Pyrolysis, vol. 82, no. 1, pp. 70–77, 2008.
View at: Publisher Site | Google Scholar
M. L. Sekirifa, M. Hadj-Mahammed, S. Pallier, L. Baameur, D. Richard, and A. H. Al-Dujaili, “Preparation and characterization of an activated carbon from a date stones variety by physical activation with carbon dioxide,” Journal of Analytical and Applied Pyrolysis, vol. 99, pp. 155–160, 2013.
View at: Publisher Site | Google Scholar
K. Sun and J. Chun Jiang, “Preparation and characterization of activated carbon from rubber-seed shell by physical activation with steam,” Biomass and Bioenergy, vol. 34, no. 4, pp. 539–544, 2010.
View at: Publisher Site | Google Scholar
M. Sevilla and R. Mokaya, “Energy storage applications of activated carbons: supercapacitors and hydrogen storage,” Energy & Environmental Science, vol. 7, no. 4, pp. 1250–1280, 2014.
View at: Publisher Site | Google Scholar
Y. Sudaryanto, S. B. Hartono, W. Irawaty, H. Hindarso, and S. Ismadji, “High surface area activated carbon prepared from cassava peel by chemical activation,” Bioresource Technology, vol. 97, no. 5, pp. 734–739, 2006.
View at: Publisher Site | Google Scholar
M. Olivares-Marín, C. Fernández-González, A. Macías-García, and V. Gómez-Serrano, “Preparation of activated carbons from cherry stones by activation with potassium hydroxide,” Applied Surface Science, vol. 252, no. 17, pp. 5980–5983, 2006.
View at: Publisher Site | Google Scholar
N. Bagheri and J. Abedi, “Preparation of high surface area activated carbon from corn by chemical activation using potassium hydroxide,” Chemical Engineering Research and Design, vol. 87, no. 8, pp. 1059–1064, 2009.
View at: Publisher Site | Google Scholar
J. Wang and S. Kaskel, “KOH activation of carbon-based materials for energy storage,” Journal of Materials Chemistry, vol. 22, no. 45, pp. 23710–23725, 2012.
View at: Publisher Site | Google Scholar
K. Babel and K. Jurewicz, “KOH activated carbon fabrics as supercapacitor material,” Journal of Physics and Chemistry of Solids, vol. 65, no. 2-3, pp. 275–280, 2004.
View at: Publisher Site | Google Scholar
R.-L. Tseng, “Mesopore control of high surface area NaOH-activated carbon,” Journal of Colloid and Interface Science, vol. 303, no. 2, pp. 494–502, 2006.
View at: Publisher Site | Google Scholar
R.-L. Tseng, “Physical and chemical properties and adsorption type of activated carbon prepared from plum kernels by NaOH activation,” Journal of Hazardous Materials, vol. 147, no. 3, pp. 1020–1027, 2007.
View at: Publisher Site | Google Scholar
J. Laine, A. Calafat, and M. labady, “Preparation and characterization of activated carbons from coconut shell impregnated with phosphoric acid,” Carbon, vol. 27, no. 2, pp. 191–195, 1989.
View at: Publisher Site | Google Scholar
M. Molina-Sabio, F. RodRíguez-Reinoso, F. Caturla, and M. J. Sellés, “Porosity in granular carbons activated with phosphoric acid,” Carbon, vol. 33, no. 8, pp. 1105–1113, 1995.
View at: Publisher Site | Google Scholar
Q.-S. Liu, T. Zheng, P. Wang, and L. Guo, “Preparation and characterization of activated carbon from bamboo by microwave-induced phosphoric acid activation,” Industrial Crops and Products, vol. 31, no. 2, pp. 233–238, 2010.
View at: Publisher Site | Google Scholar
V. Subramanian, C. Luo, A. M. Stephan, K. S. Nahm, S. Thomas, and B. Wei, “Supercapacitors from activated carbon derived from banana fibers,” Journal of Physical Chemistry C, vol. 111, no. 20, pp. 7527–7531, 2007.
View at: Publisher Site | Google Scholar
I. A. W. Tan, A. L. Ahmad, and B. H. Hameed, “Preparation of activated carbon from coconut husk: optimization study on removal of 2,4,6-trichlorophenol using response surface methodology,” Journal of Hazardous Materials, vol. 153, no. 1-2, pp. 709–717, 2008.
View at: Publisher Site | Google Scholar
F. T. Ademiluyi and E. O. David-West, “Effect of chemical activation on the adsorption of heavy metals using activated carbons from waste materials,” ISRN Chemical Engineering, vol. 2012, Article ID 674209, 5 pages, 2012.
View at: Publisher Site | Google Scholar
P. Simon, P. L. Taberna, and F. Béguin, “Electrical double-layer capacitors and carbons for EDLCs,” in Supercapacitors: Materials, Systems, and Applications, pp. 131–165, Wiley-VCH, 2013.
View at: Google Scholar
T. Pagketanang, A. Artnaseaw, P. Wongwicha, and M. Thabuot, “Microporous activated carbon from KOH-activation of rubber seed-shells for application in capacitor electrode,” Energy Procedia, vol. 79, pp. 651–656, 2015.
View at: Publisher Site | Google Scholar
C. Liang, Z. Li, and S. Dai, “Mesoporous carbon materials: synthesis and modification,” Angewandte Chemie—International Edition, vol. 47, no. 20, pp. 3696–3717, 2008.
View at: Publisher Site | Google Scholar
C. Largeot, C. Portet, J. Chmiola, P.-L. Taberna, Y. Gogotsi, and P. Simon, “Relation between the ion size and pore size for an electric double-layer capacitor,” Journal of the American Chemical Society, vol. 130, no. 9, pp. 2730–2731, 2008.
View at: Publisher Site | Google Scholar
T. E. Rufford, D. Hulicova-Jurcakova, Z. Zhu, and G. Q. Lu, “Nanoporous carbon electrode from waste coffee beans for high performance supercapacitors,” Electrochemistry Communications, vol. 10, no. 10, pp. 1594–1597, 2008.
View at: Publisher Site | Google Scholar
X. Li, W. Xing, S. Zhuo et al., “Preparation of capacitor's electrode from sunflower seed shell,” Bioresource Technology, vol. 102, no. 2, pp. 1118–1123, 2011.
View at: Publisher Site | Google Scholar
T. E. Rufford, D. Hulicova-Jurcakova, K. Khosla, Z. Zhu, and G. Q. Lu, “Microstructure and electrochemical double-layer capacitance of carbon electrodes prepared by zinc chloride activation of sugar cane bagasse,” Journal of Power Sources, vol. 195, no. 3, pp. 912–918, 2010.
View at: Publisher Site | Google Scholar
M. R. Jisha, Y. J. Hwang, J. S. Shin et al., “Electrochemical characterization of supercapacitors based on carbons derived from coffee shells,” Materials Chemistry and Physics, vol. 115, no. 1, pp. 33–39, 2009.
View at: Publisher Site | Google Scholar
M. Biswal, A. Banerjee, M. Deo, and S. Ogale, “From dead leaves to high energy density supercapacitors,” Energy and Environmental Science, vol. 6, no. 4, pp. 1249–1259, 2013.
View at: Publisher Site | Google Scholar
M. S. Balathanigaimani, W.-G. Shim, M.-J. Lee, C. Kim, J.-W. Lee, and H. Moon, “Highly porous electrodes from novel corn grains-based activated carbons for electrical double layer capacitors,” Electrochemistry Communications, vol. 10, no. 6, pp. 868–871, 2008.
View at: Publisher Site | Google Scholar
X. Xia, H. Liu, L. Shi, and Y. He, “Tobacco stem-based activated carbons for high performance supercapacitors,” Journal of Materials Engineering and Performance, vol. 21, no. 9, pp. 1956–1961, 2012.
View at: Publisher Site | Google Scholar
M. Chen, X. Kang, T. Wumaier et al., “Preparation of activated carbon from cotton stalk and its application in supercapacitor,” Journal of Solid State Electrochemistry, vol. 17, no. 4, pp. 1005–1012, 2013.
View at: Publisher Site | Google Scholar
R. Wang, P. Wang, X. Yan, J. Lang, C. Peng, and Q. Xue, “Promising porous carbon derived from celtuce leaves with outstanding supercapacitance and CO₂ capture performance,” ACS Applied Materials & Interfaces, vol. 4, no. 11, pp. 5800–5806, 2012.
View at: Publisher Site | Google Scholar
X. He, P. Ling, M. Yu, X. Wang, X. Zhang, and M. Zheng, “Rice husk-derived porous carbons with high capacitance by ZnCl₂ activation for supercapacitors,” Electrochimica Acta, vol. 105, pp. 635–641, 2013.
View at: Publisher Site | Google Scholar
C. Kim, J.-W. Lee, J.-H. Kim, and K.-S. Yang, “Feasibility of bamboo-based activated carbons for an electrochemical supercapacitor electrode,” Korean Journal of Chemical Engineering, vol. 23, no. 4, pp. 592–594, 2006.
View at: Publisher Site | Google Scholar
D. Kalpana, S. H. Cho, S. B. Lee, Y. S. Lee, R. Misra, and N. G. Renganathan, “Recycled waste paper—a new source of raw material for electric double-layer capacitors,” Journal of Power Sources, vol. 190, no. 2, pp. 587–591, 2009.
View at: Publisher Site | Google Scholar
J. Mi, X.-R. Wang, R.-J. Fan, W.-H. Qu, and W.-C. Li, “Coconut-shell-based porous carbons with a tunable micro/mesopore ratio for high-performance supercapacitors,” Energy and Fuels, vol. 26, no. 8, pp. 5321–5329, 2012.
View at: Publisher Site | Google Scholar
C.-C. Hu, C.-C. Wang, F.-C. Wu, and R.-L. Tseng, “Characterization of pistachio shell-derived carbons activated by a combination of KOH and CO₂ for electric double-layer capacitors,” Electrochimica Acta, vol. 52, no. 7, pp. 2498–2505, 2007.
View at: Publisher Site | Google Scholar
C. Peng, X.-B. Yan, R.-T. Wang, J.-W. Lang, Y.-J. Ou, and Q.-J. Xue, “Promising activated carbons derived from waste tea-leaves and their application in high performance supercapacitors electrodes,” Electrochimica Acta, vol. 87, pp. 401–408, 2013.
View at: Publisher Site | Google Scholar
F. Kurniawan, M. Wongso, A. Ayucitra et al., “Carbon microsphere from water hyacinth for supercapacitor electrode,” Journal of the Taiwan Institute of Chemical Engineers, vol. 47, pp. 197–201, 2015.
View at: Publisher Site | Google Scholar
S. T. Senthilkumar, R. K. Selvan, Y. S. Lee, and J. S. Melo, “Electric double layer capacitor and its improved specific capacitance using redox additive electrolyte,” Journal of Materials Chemistry A, vol. 1, no. 4, pp. 1086–1095, 2013.
View at: Publisher Site | Google Scholar
K. Wu, B. Gao, J. Su et al., “Large and porous carbon sheets derived from water hyacinth for high-performance supercapacitors,” RSC Advances, vol. 6, no. 36, pp. 29996–30003, 2016.
View at: Publisher Site | Google Scholar
Y.-Q. Zhao, M. Lu, P.-Y. Tao et al., “Hierarchically porous and heteroatom doped carbon derived from tobacco rods for supercapacitors,” Journal of Power Sources, vol. 307, pp. 391–400, 2016.
View at: Publisher Site | Google Scholar
H. Wang, Z. Xu, A. Kohandehghan et al., “Interconnected carbon nanosheets derived from hemp for ultrafast supercapacitors with high energy,” ACS Nano, vol. 7, no. 6, pp. 5131–5141, 2013.
View at: Publisher Site | Google Scholar
A. Elmouwahidi, Z. Zapata-Benabithe, F. Carrasco-Marín, and C. Moreno-Castilla, “Activated carbons from KOH-activation of argan (Argania spinosa) seed shells as supercapacitor electrodes,” Bioresource Technology, vol. 111, pp. 185–190, 2012.
View at: Publisher Site | Google Scholar
J. Li, G. Zan, and Q. Wu, “Nitrogen and sulfur self-doped porous carbon from brussel sprouts as electrode materials for high stable supercapacitors,” RSC Advances, vol. 6, no. 62, pp. 57464–57472, 2016.
View at: Publisher Site | Google Scholar
H. Shi, “Activated carbons and double layer capacitance,” Electrochimica Acta, vol. 41, no. 10, pp. 1633–1639, 1996.
View at: Publisher Site | Google Scholar
D. Bhattacharjya and J.-S. Yu, “Activated carbon made from cow dung as electrode material for electrochemical double layer capacitor,” Journal of Power Sources, vol. 262, pp. 224–231, 2014.
View at: Publisher Site | Google Scholar
W. Huang, H. Zhang, Y. Huang, W. Wang, and S. Wei, “Hierarchical porous carbon obtained from animal bone and evaluation in electric double-layer capacitors,” Carbon, vol. 49, no. 3, pp. 838–843, 2011.
View at: Publisher Site | Google Scholar
P. A. Goodman, H. Li, Y. Gao, Y. F. Lu, J. D. Stenger-Smith, and J. Redepenning, “Preparation and characterization of high surface area, high porosity carbon monoliths from pyrolyzed bovine bone and their performance as supercapacitor electrodes,” Carbon, vol. 55, pp. 291–298, 2013.
View at: Publisher Site | Google Scholar
Z. Li, L. Zhang, B. S. Amirkhiz et al., “Carbonized chicken eggshell membranes with 3D architectures as high-performance electrode materials for supercapacitors,” Advanced Energy Materials, vol. 2, no. 4, pp. 431–437, 2012.
View at: Publisher Site | Google Scholar
W. Qian, F. Sun, Y. Xu et al., “Human hair-derived carbon flakes for electrochemical supercapacitors,” Energy & Environmental Science, vol. 7, no. 1, pp. 379–386, 2014.
View at: Publisher Site | Google Scholar
W. Chen, H. Zhang, Y. Huang, and W. Wang, “A fish scale based hierarchical lamellar porous carbon material obtained using a natural template for high performance electrochemical capacitors,” Journal of Materials Chemistry, vol. 20, no. 23, pp. 4773–4775, 2010.
View at: Publisher Site | Google Scholar
Q. Wang, Q. Cao, X. Wang, B. Jing, H. Kuang, and L. Zhou, “A high-capacity carbon prepared from renewable chicken feather biopolymer for supercapacitors,” Journal of Power Sources, vol. 225, pp. 101–107, 2013.
View at: Publisher Site | Google Scholar
J. Li, S. Ma, L. Cheng, and Q. Wu, “Egg yolk-derived three-dimensional porous carbon for stable electrochemical supercapacitors,” Materials Letters, vol. 139, pp. 429–432, 2015.
View at: Publisher Site | Google Scholar
J. Chmiola, G. Yushin, Y. Gogotsi, C. Portet, P. Simon, and P. L. Taberna, “Anomalous increase in carbon capacitance at pore sizes less than 1 nanometer,” Science, vol. 313, no. 5794, pp. 1760–1763, 2006.
View at: Publisher Site | Google Scholar
W. Si, J. Zhou, S. Zhang, S. Li, W. Xing, and S. Zhuo, “Tunable N-doped or dual N, S-doped activated hydrothermal carbons derived from human hair and glucose for supercapacitor applications,” Electrochimica Acta, vol. 107, pp. 397–405, 2013.
View at: Publisher Site | Google Scholar
Q. Wang, J. Yan, and Z. Fan, “Carbon materials for high volumetric performance supercapacitors: design, progress, challenges and opportunities,” Energy & Environmental Science, vol. 9, no. 3, pp. 729–762, 2016.
View at: Publisher Site | Google Scholar
Q. Xie, R. Bao, A. Zheng et al., “Sustainable low-cost green electrodes with high volumetric capacitance for aqueous symmetric supercapacitors with high energy density,” ACS Sustainable Chemistry and Engineering, vol. 4, no. 3, pp. 1422–1430, 2016.
View at: Publisher Site | Google Scholar
G. A. Ferrero, A. B. Fuertes, and M. Sevilla, “From Soybean residue to advanced supercapacitors,” Scientific Reports, vol. 5, Article ID 16618, 2015.
View at: Publisher Site | Google Scholar
C. Long, X. Chen, L. Jiang, L. Zhi, and Z. Fan, “Porous layer-stacking carbon derived from in-built template in biomass for high volumetric performance supercapacitors,” Nano Energy, vol. 12, pp. 141–151, 2015.
View at: Publisher Site | Google Scholar
C. Long, L. Jiang, X. Wu et al., “Facile synthesis of functionalized porous carbon with three-dimensional interconnected pore structure for high volumetric performance supercapacitors,” Carbon, vol. 93, pp. 412–420, 2015.
View at: Publisher Site | Google Scholar
M. D. Stoller and R. S. Ruoff, “Best practice methods for determining an electrode material's performance for ultracapacitors,” Energy & Environmental Science, vol. 3, no. 9, pp. 1294–1301, 2010.
View at: Publisher Site | Google Scholar
M. Seredych, D. Hulicova-Jurcakova, G. Q. Lu, and T. J. Bandosz, “Surface functional groups of carbons and the effects of their chemical character, density and accessibility to ions on electrochemical performance,” Carbon, vol. 46, no. 11, pp. 1475–1488, 2008.
View at: Publisher Site | Google Scholar
Y. Zhao, M. Liu, X. Deng et al., “Nitrogen-functionalized microporous carbon nanoparticles for high performance supercapacitor electrode,” Electrochimica Acta, vol. 153, pp. 448–455, 2015.
View at: Publisher Site | Google Scholar
P.-Z. Cheng and H. Teng, “Electrochemical responses from surface oxides present on HNO₃-treated carbons,” Carbon, vol. 41, no. 11, pp. 2057–2063, 2003.
View at: Publisher Site | Google Scholar
Z. Li, Z. Xu, X. Tan et al., “Mesoporous nitrogen-rich carbons derived from protein for ultra-high capacity battery anodes and supercapacitors,” Energy & Environmental Science, vol. 6, no. 3, pp. 871–878, 2013.
View at: Publisher Site | Google Scholar
D. Zhang, L. Zheng, Y. Ma et al., “Synthesis of nitrogen- and sulfur-codoped 3D cubic-ordered mesoporous carbon with superior performance in supercapacitors,” ACS Applied Materials & Interfaces, vol. 6, no. 4, pp. 2657–2665, 2014.
View at: Publisher Site | Google Scholar
M. Seredych and T. J. Bandosz, “S-doped micro/mesoporous carbon-graphene composites as efficient supercapacitors in alkaline media,” Journal of Materials Chemistry A, vol. 1, no. 38, pp. 11717–11727, 2013.
View at: Publisher Site | Google Scholar
E. G. Calvo, N. Ferrera-Lorenzo, J. A. Menéndez, and A. Arenillas, “Microwave synthesis of micro-mesoporous activated carbon xerogels for high performance supercapacitors,” Microporous and Mesoporous Materials, vol. 168, pp. 206–212, 2013.
View at: Publisher Site | Google Scholar
J. M. V. Nabais, P. J. M. Carrott, M. M. L. R. Carrott, and J. A. Menéndez, “Preparation and modification of activated carbon fibres by microwave heating,” Carbon, vol. 42, no. 7, pp. 1315–1320, 2004.
View at: Publisher Site | Google Scholar
P. Puligundla, S. Oh, and C. Mok, “Microwave-assisted pretreatment technologies for the conversion of lignocellulosic biomass to sugars and ethanol: a review,” Carbon Letters, vol. 17, no. 1, pp. 1–10, 2016.
View at: Publisher Site | Google Scholar
M. Sevilla and A. B. Fuertes, “The production of carbon materials by hydrothermal carbonization of cellulose,” Carbon, vol. 47, no. 9, pp. 2281–2289, 2009.
View at: Publisher Site | Google Scholar
L. Zhang, Q. Wang, B. Wang, G. Yang, L. A. Lucia, and J. Chen, “Hydrothermal carbonization of corncob residues for hydrochar production,” Energy & Fuels, vol. 29, no. 2, pp. 872–876, 2015.
View at: Publisher Site | Google Scholar
L. Zhang, S. Liu, B. Wang, Q. Wang, G. Yang, and J. Chen, “Effect of residence time on hydrothermal carbonization of corn cob residual,” BioResources, vol. 10, no. 3, 2015.
View at: Publisher Site | Google Scholar
D. Kalderis, M. S. Kotti, A. Méndez, and G. Gascó, “Characterization of hydrochars produced by hydrothermal carbonization of rice husk,” Solid Earth, vol. 5, no. 1, pp. 477–483, 2014.
View at: Publisher Site | Google Scholar
A. Jain, C. Xu, S. Jayaraman, R. Balasubramanian, J. Y. Lee, and M. P. Srinivasan, “Mesoporous activated carbons with enhanced porosity by optimal hydrothermal pre-treatment of biomass for supercapacitor applications,” Microporous and Mesoporous Materials, vol. 218, pp. 55–61, 2015.
View at: Publisher Site | Google Scholar
D. C. S. Azevedo, J. C. S. Araújo, M. Bastos-Neto, A. E. B. Torres, E. F. Jaguaribe, and C. L. Cavalcante, “Microporous activated carbon prepared from coconut shells using chemical activation with zinc chloride,” Microporous and Mesoporous Materials, vol. 100, no. 1–3, pp. 361–364, 2007.
View at: Publisher Site | Google Scholar
S. E. Elaigwu and G. M. Greenway, “Microwave-assisted and conventional hydrothermal carbonization of lignocellulosic waste material: comparison of the chemical and structural properties of the hydrochars,” Journal of Analytical and Applied Pyrolysis, vol. 118, pp. 1–8, 2015.
View at: Publisher Site | Google Scholar
A. Jain, R. Balasubramanian, and M. Srinivasan, “Hydrothermal pre-treatment of biomass waste for high surface area mesoporous activated carbons,” in Proceedings of the Asia Pacific Confederation of Chemical Engineering Congress: APCChE 2015, Incorporating (CHEMECA '15), p. 981, Engineers Australia, 2015.
View at: Google Scholar
F.-C. Wu, R.-L. Tseng, C.-C. Hu, and C.-C. Wang, “Effects of pore structure and electrolyte on the capacitive characteristics of steam- and KOH-activated carbons for supercapacitors,” Journal of Power Sources, vol. 144, no. 1, pp. 302–309, 2005.
View at: Publisher Site | Google Scholar
G. Gryglewicz, J. Machnikowski, E. Lorenc-Grabowska, G. Lota, and E. Frackowiak, “Effect of pore size distribution of coal-based activated carbons on double layer capacitance,” Electrochimica Acta, vol. 50, no. 5, pp. 1197–1206, 2005.
View at: Publisher Site | Google Scholar
N. Syarif and M. C. Pardede, “Hydrothermal assisted microwave pyrolysis of water hyacinth for electrochemical capacitors electrodes,” Concrete Structures in Thailand Hydrothermal Assisted Microwave Pyrolysis of Water Hyacinth for Electrochemical Capacitors Electrodes Group Technology Paves the Road for Automation Effect of Laser Priming on Accumulation of Free Proline in Spring, p. 95, 2013.
View at: Google Scholar
Y. Chang, M. Antonietti, and T.-P. Fellinger, “Synthesis of nanostructured carbon through ionothermal carbonization of common organic solvents and solutions,” Angewandte Chemie—International Edition, vol. 54, no. 18, pp. 5507–5512, 2015.
View at: Publisher Site | Google Scholar
J. Pampel, C. Denton, and T.-P. Fellinger, “Glucose derived ionothermal carbons with tailor-made porosity,” Carbon, vol. 107, pp. 288–296, 2016.
View at: Publisher Site | Google Scholar
X.-X. Lin, B. Tan, L. Peng, Z.-F. Wu, and Z.-L. Xie, “Ionothermal synthesis of microporous and mesoporous carbon aerogels from fructose as electrode materials for supercapacitors,” Journal of Materials Chemistry A, vol. 4, no. 12, pp. 4497–4505, 2016.
View at: Publisher Site | Google Scholar
Z.-L. Xie, R. J. White, J. Weber, A. Taubert, and M. M. Titirici, “Hierarchical porous carbonaceous materials via ionothermal carbonization of carbohydrates,” Journal of Materials Chemistry, vol. 21, no. 20, pp. 7434–7442, 2011.
View at: Publisher Site | Google Scholar
P. Zhang, Y. Gong, Z. Wei et al., “Updating biomass into functional carbon material in ionothermal manner,” ACS Applied Materials & Interfaces, vol. 6, no. 15, pp. 12515–12522, 2014.
View at: Publisher Site | Google Scholar
F. Guo and Z. Fang, “Shape-controlled synthesis of activated bio-chars by surfactant-templated ionothermal carbonization in acidic ionic liquid and activation with carbon dioxide,” BioResources, vol. 9, no. 2, pp. 3369–3383, 2014.
View at: Google Scholar
X. Liu, C. Giordano, and M. Antonietti, “A facile molten-salt route to graphene synthesis,” Small, vol. 10, no. 1, pp. 193–200, 2014.
View at: Publisher Site | Google Scholar
B. Lu, L. Hu, H. Yin, W. Xiao, and D. Wang, “One-step molten salt carbonization (MSC) of firwood biomass for capacitive carbon,” RSC Advances, vol. 6, no. 108, pp. 106485–106490, 2016.
View at: Publisher Site | Google Scholar
X. Deng, B. Zhao, L. Zhu, and Z. Shao, “Molten salt synthesis of nitrogen-doped carbon with hierarchical pore structures for use as high-performance electrodes in supercapacitors,” Carbon, vol. 93, pp. 48–58, 2015.
View at: Publisher Site | Google Scholar
H. Yin, B. Lu, Y. Xu et al., “Harvesting capacitive carbon by carbonization of waste biomass in molten salts,” Environmental Science and Technology, vol. 48, no. 14, pp. 8101–8108, 2014.
View at: Publisher Site | Google Scholar
B. Lu, L. Hu, H. Yin, X. Mao, W. Xiao, and D. Wang, “Preparation and application of capacitive carbon from bamboo shells by one step molten carbonates carbonization,” International Journal of Hydrogen Energy, vol. 41, no. 41, pp. 18713–18720, 2016.
View at: Publisher Site | Google Scholar
B. Lu, J. Zhou, Y. Song, H. Wang, W. Xiao, and D. Wang, “Molten-salt treatment of waste biomass for preparation of carbon with enhanced capacitive properties and electrocatalytic activity towards oxygen reduction,” Faraday Discussions, vol. 190, pp. 147–159, 2016.
View at: Publisher Site | Google Scholar
A. G. Pandolfo and A. F. Hollenkamp, “Carbon properties and their role in supercapacitors,” Journal of Power Sources, vol. 157, no. 1, pp. 11–27, 2006.
View at: Publisher Site | Google Scholar
U. Fischer, R. Saliger, V. Bock, R. Petricevic, and J. Fricke, “Carbon aerogels as electrode material in supercapacitors,” Journal of Porous Materials, vol. 4, no. 4, pp. 281–285, 1997.
View at: Publisher Site | Google Scholar
P. Cheng, T. Li, H. Yu, L. Zhi, Z. Liu, and Z. Lei, “Biomass-derived carbon fiber aerogel as a binder-free electrode for high-rate supercapacitors,” Journal of Physical Chemistry C, vol. 120, no. 4, pp. 2079–2086, 2016.
View at: Publisher Site | Google Scholar
X.-L. Wu, T. Wen, H.-L. Guo, S. Yang, X. Wang, and A.-W. Xu, “Biomass-derived sponge-like carbonaceous hydrogels and aerogels for supercapacitors,” ACS Nano, vol. 7, no. 4, pp. 3589–3597, 2013.
View at: Publisher Site | Google Scholar
P. Hao, Z. Zhao, J. Tian et al., “Hierarchical porous carbon aerogel derived from bagasse for high performance supercapacitor electrode,” Nanoscale, vol. 6, no. 20, pp. 12120–12129, 2014.
View at: Publisher Site | Google Scholar
Y. Ren, J. Zhang, Q. Xu et al., “Biomass-derived three-dimensional porous N-doped carbonaceous aerogel for efficient supercapacitor electrodes,” RSC Advances, vol. 4, no. 45, pp. 23412–23419, 2014.
View at: Publisher Site | Google Scholar
D. Yang, Application of Nanocomposites for Supercapacitors: Characteristics and Properties, INTECH Open Access, 2012.
X. Wu, W. Xiong, Y. Chen et al., “High-rate supercapacitor utilizing hydrous ruthenium dioxide nanotubes,” Journal of Power Sources, vol. 294, pp. 88–93, 2015.
View at: Publisher Site | Google Scholar
M.-S. Wu, Y.-A. Huang, C.-H. Yang, and J.-J. Jow, “Electrodeposition of nanoporous nickel oxide film for electrochemical capacitors,” International Journal of Hydrogen Energy, vol. 32, no. 17, pp. 4153–4159, 2007.
View at: Publisher Site | Google Scholar
X. Zhang, X. Sun, H. Zhang, D. Zhang, and Y. Ma, “Microwave-assisted reflux rapid synthesis of MnO2 nanostructures and their application in supercapacitors,” Electrochimica Acta, vol. 87, pp. 637–644, 2013.
View at: Publisher Site | Google Scholar
N. Syarif, I. A. Tribidasari, and W. Wibowo, “Binder-less activated carbon electrode from gelam wood for use in supercapacitors,” Journal of Electrochemical Science and Engineering, vol. 3, no. 2, pp. 37–45, 2013.
View at: Publisher Site | Google Scholar
M. Zhi, C. Xiang, J. Li, M. Li, and N. Wu, “Nanostructured carbon-metal oxide composite electrodes for supercapacitors: a review,” Nanoscale, vol. 5, no. 1, pp. 72–88, 2013.
View at: Publisher Site | Google Scholar
C. Lin, J. A. Ritter, and B. N. Popov, “Development of carbon-metal oxide supercapacitors from sol-gel derived carbon-ruthenium xerogels,” Journal of the Electrochemical Society, vol. 146, no. 9, pp. 3155–3160, 1999.
View at: Publisher Site | Google Scholar
H. Kim and B. N. Popov, “Characterization of hydrous ruthenium oxide/carbon nanocomposite supercapacitors prepared by a colloidal method,” Journal of Power Sources, vol. 104, no. 1, pp. 52–61, 2002.
View at: Publisher Site | Google Scholar
K. Lota, A. Sierczynska, and G. Lota, “Supercapacitors based on nickel oxide/carbon materials composites,” International Journal of Electrochemistry, vol. 2011, Article ID 321473, 6 pages, 2011.
View at: Publisher Site | Google Scholar
S. He and W. Chen, “Application of biomass-derived flexible carbon cloth coated with MnO₂ nanosheets in supercapacitors,” Journal of Power Sources, vol. 294, pp. 150–158, 2015.
View at: Publisher Site | Google Scholar
L. Wang, Y. Zheng, S. Chen et al., “Three-dimensional kenaf stem-derived porous carbon/MnO₂ for high-performance supercapacitors,” Electrochimica Acta, vol. 135, pp. 380–387, 2014.
View at: Publisher Site | Google Scholar
W. Xiong, Y. Gao, X. Wu et al., “Composite of macroporous carbon with honeycomb-like structure from mollusc shell and NiCo₂O₄ nanowires for high-performance supercapacitor,” ACS Applied Materials & Interfaces, vol. 6, no. 21, pp. 19416–19423, 2014.
View at: Publisher Site | Google Scholar
Q. Wang, J.-L. Li, F. Gao, W.-S. Li, K.-Z. Wu, and X.-D. Wang, “Activated carbon coated with polyaniline as an electrode material in supercapacitors,” New Carbon Materials, vol. 23, no. 3, pp. 275–280, 2008.
View at: Publisher Site | Google Scholar
Y.-R. Lin and H. Teng, “A novel method for carbon modification with minute polyaniline deposition to enhance the capacitance of porous carbon electrodes,” Carbon, vol. 41, no. 14, pp. 2865–2871, 2003.
View at: Publisher Site | Google Scholar
X. Zhou, L. Li, S. Dong et al., “A renewable bamboo carbon/polyaniline composite for a high-performance supercapacitor electrode material,” Journal of Solid State Electrochemistry, vol. 16, no. 3, pp. 877–882, 2012.
View at: Publisher Site | Google Scholar
P.-L. Taberna, G. Chevallier, P. Simon, D. Plée, and T. Aubert, “Activated carbon-carbon nanotube composite porous film for supercapacitor applications,” Materials Research Bulletin, vol. 41, no. 3, pp. 478–484, 2006.
View at: Publisher Site | Google Scholar
R. Farma, M. Deraman, Awitdrus et al., “Physical and electrochemical properties of supercapacitor electrodes derived from carbon nanotube and biomass carbon,” International Journal of Electrochemical Science, vol. 8, no. 1, pp. 257–273, 2013.
View at: Google Scholar

Copyright

Copyright © 2017 Talam Kibona Enock et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

7999

Downloads

4380

Citations