International Journal of Electrochemistry / 2020 / Article / Tab 9 / Research Article
Synthesis, Electrochemical, Thermodynamic, and Quantum Chemical Investigations of Amino Cadalene as a Corrosion Inhibitor for Stainless Steel Type 321 in Sulfuric Acid 1M Table 9 Mulliken charges and Fukui indices of ACM.
Atom Mulliken charge 1C −0.205 −0.296122 −0.217434 2C 0.088 0.090084 0.153727 3C 0.041 0.043488 0.055688 4C 0.019 0.036875 0.036388 5C 0.081 0.037768 0.110354 6C 0.200 0.123649 0.174388 9C −0.211 −0.279292 −0.179320 10C −0.173 −0.227862 −0.139367 11C −0.150 −0.212445 −0.150402 12C 0.119 0.111155 0.121676 15C 0.495 −0.493384 −0.502078 19N −0.824 −0.797001 −0.720655 22C −0.484 −0.519184 −0.524307 26C −0.168 −0.133326 −0.178921 28C −0.393 −0.413773 −0.449291 32C −0.403 −0.434435 −0.459154