Characterization and Optimization of Mechanical Properties of ABS Parts Manufactured by the Fused Deposition Modelling Process
Table 2
Input process parameters that affect output responses.
| Run | layer thickness | part orientation | raster angle | raster width | air gap | Measured (MPa) |
| 1 | 0.127 | 0 | 0 | 0.2032 | −0.00254 | 32.56 | 2 | 0.127 | 0 | 0 | 0.2032 | 0.5588 | 6.52 | 3 | 0.127 | 0 | 0 | 0.5588 | −0.00254 | 24.81 | 4 | 0.127 | 0 | 0 | 0.5588 | 0.5588 | 10.44 | 5 | 0.127 | 0 | 45 | 0.2032 | −0.00254 | 34.61 | 6 | 0.127 | 0 | 45 | 0.2032 | 0.5588 | 4.78 | 7 | 0.127 | 0 | 45 | 0.5588 | −0.00254 | 30.15 | 8 | 0.127 | 0 | 45 | 0.5588 | 0.5588 | 8.08 | 9 | 0.127 | 90 | 0 | 0.2032 | −0.00254 | 12.86 | 10 | 0.127 | 90 | 0 | 0.2032 | 0.5588 | 4.39 | 11 | 0.127 | 90 | 0 | 0.5588 | −0.00254 | 23.55 | 12 | 0.127 | 90 | 0 | 0.5588 | 0.5588 | 9.56 | 13 | 0.127 | 90 | 45 | 0.2032 | −0.00254 | 15.1 | 14 | 0.127 | 90 | 45 | 0.2032 | 0.5588 | 4.01 | 15 | 0.127 | 90 | 45 | 0.5588 | −0.00254 | 24.3 | 16 | 0.127 | 90 | 45 | 0.5588 | 0.5588 | 8.09 | 17 | 0.3302 | 0 | 0 | 0.4572 | −0.00254 | 31.46 | 18 | 0.3302 | 0 | 0 | 0.4572 | 0.9652 | 8.43 | 19 | 0.3302 | 0 | 0 | 0.9652 | −0.00254 | 24.99 | 20 | 0.3302 | 0 | 0 | 0.9652 | 0.9652 | 9.39 | 21 | 0.3302 | 0 | 45 | 0.4572 | −0.00254 | 31.42 | 22 | 0.3302 | 0 | 45 | 0.4572 | 0.9652 | 7.12 | 23 | 0.3302 | 0 | 45 | 0.9652 | −0.00254 | 28.94 | 24 | 0.3302 | 0 | 45 | 0.9652 | 0.9652 | 11.07 | 25 | 0.3302 | 90 | 0 | 0.4572 | −0.00254 | 20.55 | 26 | 0.3302 | 90 | 0 | 0.4572 | 0.9652 | 8.89 | 27 | 0.3302 | 90 | 0 | 0.9652 | −0.00254 | 24.72 | 28 | 0.3302 | 90 | 0 | 0.9652 | 0.9652 | 11.28 | 29 | 0.3302 | 90 | 45 | 0.4572 | −0.00254 | 24.96 | 30 | 0.3302 | 90 | 45 | 0.4572 | 0.9652 | 8.82 | 31 | 0.3302 | 90 | 45 | 0.9652 | −0.00254 | 27.35 | 32 | 0.3302 | 90 | 45 | 0.9652 | 0.9652 | 11.63 |
|
|