Hot Corrosion Behaviour of Detonation Gun Sprayed
Al2O3-40TiO2 Coating on Nickel Based Superalloys at 900°C
Figure 3
(Cumulative weight gain/area)2 vs. number of cycles for bare and Al2O3-40TiO2 coated superalloys subjected to Na2SO4-82%Fe2(SO4)3 at 900°C for 50 cycles.