Application of Diaminium Iodides in Binary Ionic Liquid Electrolytes for Dye-Sensitized Solar Cells

Table 3

Photovoltaic performance of DSCs with electrolytes A~G.


Electrolyte	/(mA·cm⁻²)	/V	FF	η (%)

(A) m(HEEDAI) : m(MPII) = 1 : 9 Without TBP	6.88	0.68	0.46	2.16
(B) m(HEEDAI) : m(MPII) = 1 : 9, 0.5 mol·L⁻¹ TBP	6.64	0.69	0.45	2.06
(C) m(HEEDAI) : m(MPII) = 1 : 4 Without TBP	9.36	0.67	0.52	3.24
(D) m(HEEDAI) : m(MPII) = 1 : 4, 0.5 mol·L⁻¹ TBP	8.96	0.66	0.52	3.06
(E) m(HEEDAI) : m(MPII) = 1 : 1 Without TBP	5.76	0.63	0.50	1.80
(F) m(HEEDAI) : m(MPII) = 1 : 1, 0.5 mol·L⁻¹ TBP	5.68	0.64	0.48	1.74
(G) m(HEPI) : m(MPII) =1 : 9 Without TBP	7.20	0.65	0.53	2.44

The electrolyte component of A~G: (A) m(HEEDAI) : m(MPII) = 1 : 9; (B) m(HEEDAI) : m(MPII) = 1 : 9, 0.5 mol·L⁻¹ TBP, (C) m(HEEDAI) : m(MPII) = 1 : 4; (D) m(HEEDAI) : m(MPII) = 1 : 4, 0.5 mol·L⁻¹ TBP; (E) m(HEEDAI) : m(MPII) = 1 : 1; (F) m(HEEDAI) : m(MPII) = 1 : 1, 0.5 mol·L⁻¹ TBP; and 0.15 mol·L⁻¹ I₂; (G) m(HEPI) : m(MPII) =1 : 9 and 0.15 mol·L⁻¹ I₂, 0.1 mol·L⁻¹ LiI. Illumination: AM 1.5, 100 mV·cm⁻², active areas of DSCs: 0.25 cm².