Enhancing Photocatalytic Performance through Tuning the Interfacial Process between -Assembled and Pt-Loaded Microspheres
Figure 4
(a) Typical time-dependent absorption spectra of MO solution in the presence of 3.0-Pt-TiO2 under ultraviolet light irradiation; (b) as a function of irradiating time of MO solution for different samples in 90 min under UV light irradiation; (c) degradation rate for different Pt loading content of TiO2 after irradiation for 30 min under UV light with a wavelength of 254 nm irradiation. The photocatalytic performances of PureTiO2 and commercial P25-TiO2 were measured in the same conditions for comparison.