Research Article
The Influence of Titania Electrode Modification with Lanthanide Ions Containing Thin Layer on the Performance of Dye-Sensitized Solar Cells
Table 1
The photoelectrochemical properties of the presented RE-modified photoelectrodes.
| RE | (eV) | (Ω) | (10−8 mol cm−2) | (mAcm−2) | (mV) | FF (%) | |
| Ti | 3.26 | 163 | 7.28 | 16.9 | 715 | 56.07 | 6.76 | Sc | 3.23 | 205 | 6.66 | 19.2 | 737 | 44.58 | 6.30 | Y | 3.21 | 144 | 7.60 | 17.0 | 674 | 44.52 | 5.11 | La | 3.25 | 128 | 8.84 | 18.0 | 696 | 61.55 | 7.71 | Ce | 3.08 | 232 | 6.52 | 19.3 | 730 | 63.06 | 8.88 | Pr | 3.24 | 148 | 6.43 | 18.5 | 667 | 50.73 | 6.25 | Nd | 3.28 | 136 | 7.35 | 18.9 | 683 | 55.33 | 7.15 | Sm | 3.29 | 210 | 5.42 | 17.4 | 697 | 48.91 | 5.95 | Eu | 3.33 | 131 | 5.85 | 18.2 | 663 | 46.14 | 5.55 | Gd | 3.30 | 96 | 7.10 | 16.2 | 701 | 49.11 | 5.57 | Tb | 3.28 | 175 | 7.87 | 17.9 | 718 | 56.66 | 7.29 | Dy | 3.32 | 137 | 9.23 | 18.2 | 722 | 47.79 | 6.28 | Ho | 3.33 | 245 | 7.74 | 17.8 | 716 | 58.95 | 7.49 | Er | 3.24 | 137 | 6.33 | 18.6 | 712 | 53.17 | 7.03 | Tm | 3.30 | 206 | 6.71 | 18.6 | 743 | 46.96 | 6.48 | Yb | 3.23 | 100 | 7.41 | 19.8 | 702 | 63.21 | 8.80 | Lu | 3.20 | 182 | 8.51 | 18.0 | 725 | 59.98 | 7.84 |
|
|