Fabrication and Characterization of CuInSe2 Thin Film Applicable for a Solar Energy Light Absorption Material via a Low Temperature Solid State Reaction

Figure 1

XRD patterns of as-prepared (a) InSe [13], (b) In2Se3 [14], (c) CuSe [14], and (d) Cu2Se [14] particles.