Abstract

The photocatalytic degradation of methyl violet using TiSiW12O40/TiO2 as a novel eco-friendly catalyst under simulated natural light irradiation was investigated. The physical characterizations were carried out by TG/DTA, FT-IR, XRD, and UV-visible spectra. The effects of the initial methyl violet concentration, the solution pH, and catalyst dosage on the photocatalytic degradation rate of methyl violet were also examined. The results demonstrated that at optimal condition (initial concentration of methyl violet is 20 mg/L, catalyst dosage is 0.3 g, and the pH is 5.5), the degradation rate of methyl violet is as high as 82.4% after 3 h under simulated natural light irradiation. The reaction of photocatalysis for methyl violet can be expressed as first-order kinetic model.

1. Introduction

With the remarkable steady growth of people’s living standard, organic dyes, which have been widely used in industry have become a concern because of their byproducts that constitute a serious risk for human health due to their high toxicity [1, 2]. However, they are difficult to be treated through generic chemical methods and biological techniques, such as condensation, ultrafiltration, membrane separation, bacterial, and adsorption [3, 4]. Hence, the treatment of organic pollutants has become a serious problem in environmental and chemical fields [5, 6]. It is noteworthy that the new opportunities and challenges in water treatment have led to the development of photocatalytic oxidation technology, which has the potential to completely oxidize organic compounds to CO2, H2O, and other inorganic substances [79]. Photocatalytic oxidation technology with semiconductor materials such as TiO2, TiOX, Fe2O3, and SrTiO3 as the catalyst has been investigated widely by several authors [1013]. Among these functional materials, TiO2 has received the greatest interest in the field of photocatalysis technology. TiO2 used in photocatalytic water treatment has many excellent properties such as high activity, chemical stability, and nontoxicity. Other than these, photocatalytic activity of TiO2 can be turned by various chemical methods to obtain visible light response [14].

Polyoxometalates (POMs) constituted by transition metals in their highest oxidation states and oxoanions have been extensively studied as catalysts for a wide range of reactions. They have the similar photochemical characteristics with TiO2 and can be activated by the light in the near ultraviolet (UV) or the visible region, and hence they are also used as photocatalysts in wastewater treatment [15]. POMs should be supported on a support like molecular sieves, carbon, or transition metal oxide to overcome their shortcomings, such as low surface area (1–10 m2/g), low thermal stability, and high solubility, which limit their industrial application. TiO2 was also an ideal support because of its higher surface area, chemical inertness, controlled porosity, and well dispersal for POMs while retaining the structure [16].

Since nearly 5% of the solar energy incident on the Earth’s surface lies in the ultraviolet light region, it is essential to use natural light efficiently to drive photocatalytic oxidation of organic dyes. In order to achieve the goal, we attempt to develop novel functional materials with a visible light response. In this paper, the preparation of TiSiW12O40/TiO2 composite was reported, and the photocatalytic degradation of methyl violet with the catalyst under simulated natural light irradiation was investigated.

2. Experimental

2.1. Preparation of Catalyst

The catalyst was prepared using Ti(OH)4 and H4SiW12O40·21H2O as the starting materials. H4SiW12O40·21H2O (10.0 g, 3.0707 mmol) was dissolved in 40 mL of water, and the solution was heated to near 100°C. Then, Ti(OH)4 (1.0 g, 8.6260 mmol) was slowly added to the boiling solution, and the resulting mixture was refluxed for 3 h. In this process, water was added to the solution to prevent it from searing. After drying at 100°C for 12 h, the white catalyst was obtained.

2.2. Characterization

The thermal stability of the catalyst was examined by means of DTA with a Netzsch STA 449 thermal analysis system at a heating rate of 10°C/min from 20 to 700°C in air atmosphere. The FT-IR spectra of the samples in KBr matrix were recorded on a Nicolet 5700 FT-IR spectrometer in the range 400–4000 cm−1. The X-ray powder diffraction pattern of the samples was measured by a Bruker AXS D8-advanced diffractometer (Bruker, Germany) employing Cu radiation.

2.3. Activity Test

For the evaluation of catalyst activity, the catalyst was suspended in an aqueous solution of methyl violet in a Pyrex reactor. The photoreactor was designed with a light source surrounded by a quartz jacket. Simulated sunlight irradiation was provided by a 500 W xenon lamp (Nanjing Xujiang Electromechanical Factory, China) and the intensity of the lamp was 1200 μmol·m−2·s−1. Solution pH was adjusted with dilute aqueous HCl and NaOH solutions. The system was cooled by circulating water and maintained at room temperature. Before irradiation, the suspensions were magnetically stirred in the dark for 30 min to reach the adsorption-desorption equilibrium of organic dyes on catalyst surface. At given time intervals, about 3 mL suspension was continually taken from the photoreactor for subsequent methyl violet concentration analysis after centrifuging. Decreases of the methyl violet concentrations were monitored via a UV-visible spectrometer (Hitachi U-3010, Japan). The degradation yield of organics was calculated by the following formula: where and referred to the absorbance of RhB before and after reaction, respectively.

3. Results and Discussion

3.1. Characterization of the Catalysts

The DTA curve of the catalyst is shown in Figure 1. The pyrolysis proceeds mainly in three steps. The endothermic peaks on the DTA curve at about 98.3°C correspond to the loss of the adsorbed water. The broad endothermic peak at about 258.8°C is associated with the loss of coordination water in HPA, and the loss is complete at 350°C, which is the activation temperature of TiSiW12O40/TiO2. Finally, TiSiW12O40/TiO2 starts to decompose and its Keggin structure collapses, as seen from the sharp exothermic peak at 563.6°C.

IR spectra of TiO2·H2O, H4SiW12O40·H2O, and TiSiW12O40/TiO2 are shown in Figure 2. The infrared spectra characteristic absorption peaks of TiO2 are explored at 1401 cm−1 and of H4SiW12O40·21H2O at 1631, 984, 935, 785, and 549 cm−1. In the infrared spectrum of TiSiW12O40/TiO2, the absorption bands at 1618, 1021, 984, 928, 885, 791, and 543 cm−1 can be assigned to the bending vibrations of H-O-H bond and the stretching vibrations of Si-O-Si, W-Od, Si-O, W-Ob-W, W-Oc-W, and Si-O-Si bonds, respectively. The stretching vibrations of Ti-O at 1401 cm−1 in titanium hydroxide decrease in the composite of TiSiW12O40/TiO2. Similar bands in the region of 935–543 cm−1 confirmed the presence of red shift of absorption peaks at the base of H4SiW12O40·21H2O. These indicate that the Keggin structure of H4SiW12O40·21H2O [17] was maintained after compounding at the surface of support.

XRD spectra of TiO2, H4SiW12O40·H2O, and TiSiW12O40/TiO2 are shown in Figure 3. The X-ray powder patterns of TiO2 calcinated at 350°C for 3 h show the anatase structure. The comparison of XRD patterns with H4SiW12O40·21H2O reveals that the salt TiSiW12O40 also shows the Keggin structure [17], which is in accordance with the results of IR spectrum analysis.

3.2. Investigation of Photocatalytic Activity of Catalysts
3.2.1. Comparison of Photocatalytic Activity of Catalysts

In order to observe the catalytic activity of TiSiW12O40/TiO2, comparison of photocatalytic activity of catalysts was carried out at the initial methyl violet concentration of 20 mg/L, pH 5.5, and 0.3 g of catalyst. The results showed that, after 2.5 h irradiation under the same conditions, no obvious methyl violet degradation was observed without any catalyst or light. However, in the presence of TiSiW12O40/TiO2 without any light, the degradation yield of methyl violet is about 11.9%, while with TiSiW12O40/TiO2 under simulated natural light irradiation the degradation yield can reach to 70.5%. So the photodegradation reaction of methyl violet in the presence of TiSiW12O40/TiO2 under simulated natural light irradiation is more effective than that of TiSiW12O40/TiO2 without any light.

3.2.2. Effect of the Initial Concentration of Dye

To investigate the influence of initial concentration on the degradation efficiency of methyl violet, the initial concentration was varied from 5 to 40 mg/L, keeping the other experimental conditions constant.

As can be seen in Figure 4, the degradation rate decreased with increase of initial concentration of methyl violet. This might be due to the excessive adsorption of the methyl violet molecules on the surface of catalyst at higher concentration. Moreover, light through the solution is reduced significantly. The results indicated that the degradation rate gradually increased with increase of the initial concentration of dye from 5 to 20 mg/L. However, the degradation efficiency gradually decreased with increase of the initial concentration of dye from 20 to 40 mg/L. Thus, the efficiency of degradation was decreased in the higher concentration. From the practical point of wastewater treatment, the initial concentration of the 20 mg/L is more appropriate.

3.2.3. Effect of pH

It is well known that the pH of the solution is one of the most important parameters in the photocatalytic degradation of organic compounds. This is attributed to the fact that the pH not only determines chemical properties of the photocatalyst but also influences adsorption behaviour of the pollutants. Therefore, the effect of pH on the degradation of methyl violet was studied at pH range from 3.5 to 7.5.

As shown in Figure 5, the most effective pH condition is at 5.5. This may be ascribed to the fact that the pH value could influence the amount of hydroxyl radicals () formed and the stable of H4SiW12O40. So the optimum pH of the solution is 5.5.

3.2.4. Effect of Catalyst Dosage

The catalyst dosage is also an important parameter for optimizing the operational conditions. Therefore, the effect of catalyst dosage on the degradation of methyl violet was investigated in the catalyst dosage from 0.15 to 0.60 g, and the result shown was in Figure 6. The results indicated that the degradation rate gradually increased with increase of catalyst dosage from 0.15 to 0.30 g. However, the degradation efficiency gradually decreased with increase of catalyst dosage from 0.30 to 0.60 g. This may be attributed to the fact that the surplus catalyst can scatter the photons in the photoreaction system.

3.2.5. Kinetic Analysis

It is well known that the photodegradation of organic dyes mainly follows first-order kinetics. The kinetics of photocatalytic degradation of methyl violet was also studied under optimized conditions. The results are shown in Figure 7.

The results showed that the photocatalytic degradation of methyl violet over TiSiW12O40/TiO2 under simulated sunlight irradiation can be described by the first-order kinetic model,  , where is the rate constant (h−1), is the initial concentration, and is the concentration of dye at time . It can be seen from Figure 7 that the plots represented a straight line. The correlation constant for the line was 0.992. The rate constant was 0.6 h−1.

3.2.6. Comparison of Photocatalytic Activity of Catalysts

The photodegradation rate of TiSiW12O40/TiO2 was compared with those of Co-SBA-15 [18], Fe-doped anatase TiO2 [19], TiO2, and H4SiW12O40, and the results are shown in Table 1.

The catalytic activity of TiSiW12O40/TiO2 is much higher than that of H4SiW12O40 and TiO2 under simulated natural light irradiation. This might be ascribed to the synergistic effect between H4SiW12O40 and TiO2. It was also observed that TiSiW12O40/TiO2 shows a higher photocatalytic efficiency of degradation dyes than Co-SBA-15, and Fe-doped anatase TiO2. The results indicate that TiSiW12O40/TiO2 has an excellent photocatalytic performance with a degradation of methyl violet more than 82% in 3 h, suggesting that the catalyst TiSiW12O40/TiO2 has an excellent application in environmental protection.

4. Conclusion

The photocatalytic degradation of methyl violet using TiSiW12O40/TiO2 as a novel eco-friendly catalyst under simulated natural light irradiation was investigated. The results demonstrated that at optimal condition (initial concentration of methyl violet is 20 mg/L, catalyst dosage is 0.3 g, and the pH is 5.5), the degradation rate of methyl violet is as high as 82.4% after 3 h under simulated natural light irradiation. The reaction of photocatalysis for methyl violet can be expressed as first-order kinetic mode.

Acknowledgments

This work was financially supported by the Young and Middle-Aged Natural Science Foundation of Hubei Province Education Department (nos. Q20112507 and Q20082202) and Hubei Key Laboratory of Pollutant Analysis and Reuse Technology (no. KY2010G13).