Dye-Sensitized Solar Cells with Anatase TiO2 Nanorods Prepared by Hydrothermal Method
Table 2
Taguchi L9 orthogonal array.
| Order | Factor | A NaOH concentration (M) | B TiO2 particle size (nm) | C Autoclave temperature (°C) | D Annealing temperature (°C) |
| 1 | 10 M | 14 nm | 180°C | 450°C | 2 | 10 M | 21 nm | 200°C | 500°C | 3 | 10 M | 100 nm | 230°C | 550°C | 4 | 8 M | 14 nm | 200°C | 550°C | 5 | 8 M | 21 nm | 230°C | 450°C | 6 | 8 M | 100 nm | 180°C | 500°C | 7 | 12 M | 14 nm | 230°C | 500°C | 8 | 12 M | 21 nm | 180°C | 550°C | 9 | 12 M | 100 nm | 200°C | 450°C |
|
|