Optical and Structural Characterization of Nickel Coatings for Solar Collector Receivers
Table 1
List of the investigated samples: (a) Wood bath and (b) Wood + Watts baths. f: sample front face; b: sample back face.
(a) |
| Sample | Thickness | m |
| 35 f | 0.80 | 35 b | 0.87 | 36 f | 1.03 | 36 b | 0.91 | 105 f | 1.73 | 105 b | 1.76 | 106 f | 1.32 | 106 b | 1.23 | 107 f | 2.06 | 107 b | 1.69 | 108 f | 2.03 | 108 b | 2.10 | 109 f | 2.46 | 109 b | 2.34 | 110 f | 2.59 | 110 b | 2.72 | 111 f | 3.02 | 111 b | 3.25 | 112 f | 2.87 | 112 b | 2.98 |
|
|
(b) |
| Sample | Thickness | m |
| 103 f | 1.11 | 103 b | 1.83 | 104 f |
1.20 | 104 b | 1.39 | 19 f | 2.01 | 20 b | 2.00 | 21 f | 2.38 | 22 b | 2.49 | 23 f | 2.82 | 23 b | 3.17 | 24 f | 2.66 | 24 b | 2.93 | 25 f | 4.23 | 25 b | 4.97 | 26 f | 3.72 | 26 b | 4.60 | 27 f | 5.07 | 27 b | 5.85 | 28 f | 4.72 | 28 b | 5.74 | 29 f | 6.75 | 29 b | 7.68 | 30 f | 6.96 | 30 b | 7.82 | 31 f | 9.51 | 31 b | 10.96 | 32 f | 9.93 | 32 b | 10.61 | 33 f | 12.41 | 33 b | 13.52 | 34 f | 12.90 | 34 b | 13.50 |
|
|