Laser Enhanced Hydrogen Passivation of Silicon Wafers

Figure 7

The temperature profile of the centre of the sample illustrated in Figure 6 during the laser annealing process. It was conducted when laser power density was 3.26 × 102 W/cm2, a scan speed was 15 mm/s, and a hotplate was held at 723 K.