Photocatalytic Activity and Optical Properties of Blue Persistent Phosphors under UV and Solar Irradiation

García, C. R.; Diaz-Torres, L. A.; Oliva, J.; Romero, M. T.; Salas, P.

doi:https://doi.org/10.1155/2016/1303247

International Journal of Photoenergy

On this page

Abstract Introduction Experimental Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2016 | Article ID 1303247 | https://doi.org/10.1155/2016/1303247

Photocatalytic Activity and Optical Properties of Blue Persistent Phosphors under UV and Solar Irradiation

C. R. García,^1,2L. A. Diaz-Torres ,¹J. Oliva,¹M. T. Romero,²and P. Salas³

Academic Editor: Meenakshisundaram Swaminathan

Received25 Feb 2016

Revised12 Jun 2016

Accepted25 Jul 2016

Published01 Sept 2016

Abstract

Blue phosphorescent strontium aluminosilicate powders were prepared by combustion synthesis route and a postannealing treatments at different temperatures. X-ray diffraction analysis showed that phosphors are composed of two main hexagonal phases: SrAl₂O₄ and Sr₃Al₃₂O₅₁. The morphology of the phosphors changed from micrograins (1000°C) to a mixture of bars and hexagons (1200°C) and finally to only hexagons (1300°C) as the annealing temperature is increased. Photoluminescence spectra showed a strong blue-green phosphorescent emission centered at nm, which is associated with transition of the Eu²⁺. The sample annealed at 1200°C presents the highest luminance value (40 Cd/m²) with CIE coordinates (0.1589, 0.1972). Also, the photocatalytic degradation of methylene blue (MB) under UV light (at 365 nm) was monitored. Samples annealed at 1000°C and 1300°C presented the highest percentage of degradation (32% and 38.5%, resp.) after 360 min. In the case of photocatalytic activity under solar irradiation, the samples annealed at 1000°C, 1150°C, and 1200°C produced total degradation of MB after only 300 min. Hence, the results obtained with solar photocatalysis suggest that our powders could be useful for water cleaning in water treatment plants.

1. Introduction

Long persistent phosphor (LPP) materials have several applications such as emergency signals in the darkness, wall painting, radiation detection, displays, lamps, and decorations [1]. Due to their importance, the development of new LPP with stable chemical and physical properties is still a challenge in the field of materials science. Long persistent SrAl₂O₄:Eu²⁺,Dy³⁺ (510 nm) phosphors have shown high brightness lasting for 10 h [2, 3]. Similarly, blue phosphorescent emission at around nm has been obtained from CaAl₂O₄:Eu²⁺,Nd³⁺ (430 nm), SrMgSi₂O₆:Dy³⁺ (455 nm), and BaMgAl₁₀O₁₇:Eu²⁺,Co³⁺ (450 nm) systems [1, 4]. Nonetheless, these systems showed less brightness and time of phosphorescence than those for the green SrAl₂O₄:Eu²⁺,Dy³⁺ phosphor. Thus, the development of new blue LPPs materials with blue emission at around 450 nm is required for the applications mentioned above.

Besides, few reports have demonstrated the use of the LPPs in the photocatalysis area. It has been proposed that the mixture of LPPs and photocatalyst composites can help to improve the photocatalytic process under ultraviolet (UV) light excitation: The photocatalyst/LPP composites such as TiO₂/SrAl₂O₄:Eu²⁺,Dy³⁺ have been proposed to enhance the benzene oxidation under UV light or in the darkness [5]. Another composite, Ti_2−xN_yO₂/CaAl₂O₄:Eu²⁺,Dy³⁺, was used to decompose gaseous acetaldehyde or nitrogen oxide acetaldehyde by a self-fluorescence assisted in the dark [6]. Another composite, Ag₃PO₄/Sr₄Al₁₄O₂₅:(Eu,Dy), decomposed the Rhodamine B without light assistance [7]. Here, the photocatalyst Ag₃PO₄ is excited by the light emitted from the LPP after turning off the UV excitation which was maintained during 30 minutes, this produced the degradation of rhodamine dissolved in an aqueous solution [7], then, and few studies about the photocatalytic properties of LPPs have been published.

The utilization of LPPs for photocatalytic applications has been attractive because the phosphorescent materials have electrons with high mobility from the valence band (VB) levels to the traps levels which can act as electrons storage and this fact can favor the photocatalytic properties [8]. These traps levels are usually generated by oxygen vacancy, defects, or impurities when the lattice is doped with Eu²⁺ and Dy³⁺ ions [8]. Based on the phosphorescence models, it is argued that electrons are stored in these traps states and, then, the energy can be slowly released to produce phosphorescence by electrons and holes recombination [9]. This slow release of electrons can allow larger amounts of electrons and holes (e-h⁺) to be available for the production of hydroxyl radicals (OH⁻) which promotes the photocatalysis process [10]. The study of the photocatalytic properties of LPPs is important to find alternative photocatalysts other than TiO₂ which has been recently pointed out as a toxic for aquatic ecosystems [11]. Furthermore, several studies show that nanosized TiO₂ is toxic for many aquatic species like fish Daphnia magna and Rainbow fish [12]. Bioaccumulation into the gills of river fishes has also been reported [13]. Hence, micrometric sizes of the grains of the photocatalyst are suitable because they can be easily removed from water after their use. In addition, there are very few studies about Eu²⁺,Dy³⁺ doped strontium/aluminosilicate powders and their utilization as photocatalysts. Thus, the aim of this work is to investigate the photocatalytic, structural, morphological, and optical properties of Eu²⁺,Dy³⁺ doped-aluminate/aluminosilicate phosphors annealed at different temperatures in the range of 1000°C–1300°C.

2. Experimental

2.1. Combustion Synthesis

Na₂O₃Si5H₂O (99.99%), Sr(NO₃)₃·H₂O (99.9965%), Al(NO₃)₃·9H₂O (99.5%), DyCl₃·6H₂O (99.9%), EuCl₃·6H₂O (99.9%), NH₄NO₃ (99.9%), and H₃BO₃ (95%) reagents from Sigma Aldrich were dissolved in 25 mL of deionized water for approximately 45 minutes in a quartz beaker on a magnetic stirrer, and a transparent solution was formed. The Al/Sr ratio was 7.6 for all samples and was prepared using 0.01 moles of Eu²⁺, 0.02 mole of Dy³⁺, mole of NH₄NO₃, and mole of H₃BO₃. Also 0.01 mole of urea [CH₄N₂O] was added as fuel and it maximizes the combustion reaction. Next, the transparent blend was annealed at 600°C in atmospheric pressure and the exothermic reaction occurred (combustion process) during 10–40 seconds. As a result, (Eu,Dy)-doped strontium aluminate/aluminosilicates as-synthesized powders were obtained. Finally, the as-synthesized powders were put in alumina crucibles and annealed under reductive atmosphere during 4 h at four different temperatures: 1000°C, 1150°C, 1200°C, and 1300°C. After this, the blue-emitting LPPs of (Eu,Dy)-doped strontium aluminate/aluminosilicate powders were obtained.

2.2. Photocatalysis under UV and Solar Irradiations

For the photocatalysis experiments, the powders were first ground in an agate mortar until we got fine powders. The photocatalytic degradation of the methylene blue (MB) was measured by monitoring the absorbance of MB dissolved in water at 665 nm. The photocatalytic process was carried out using a reactor fabricated with three 4 W UV lamps. Those lamps emitted UV light centered at 365 nm, with a FWHM around 12 nm. The samples for photocatalysis were prepared by mixing 30 mg of (Eu,Dy)-doped strontium aluminate/aluminosilicate powders with a solution 0.5 mM of MB in water. This solution was stirred in darkness during 1 h in order to adsorb the MB molecules on the surface of the powders. Afterwards, the UV lamps were turned on and samples of 1 mL were extracted every 30 minutes, the powders were separated from the liquid using centrifugation, and, then, the absorbance spectrum of the liquid was obtained by using a Cary-60 UV-Vis spectrophotometer in the range of 200 nm–700 nm. In the case of solar photocatalysis, the samples were exposed under sunlight during a sunny day from 10:00 am to 4:00 pm in Saltillo city, Mexico. The coordinates in this location were as follows: latitude, 25°25.706′ North, longitude, 100°58.616′ West, and height, 1581 m. The average solar irradiance was W/m² and it was measured with a photodiode 6450 Davis Solar Radiation Sensor.

2.3. Structural and Morphological Characterization

The X-ray diffraction (XRD) patterns of the (Eu,Dy)-doped strontium aluminate/aluminosilicate (1000–1300°C) were performed in a Bruker D-8 Advance diffractometer having the Bragg-Brentano configuration and CuK_α radiation ( Å). The XRD patterns were measured in the range of with 0.02° step size. Morphology of the samples was analyzed using a field emission electron JSM-7800F microscope and 200 kV of accelerating voltage.

2.4. Optical Characterization

Excitation spectra, photoluminescence spectra, and phosphorescence decay curves were obtained by using an Acton Research modular 2300 fluorometer. The fluorometer was coupled with a pair of SP-500i monochromators (Acton Research), a Xenon lamp (75 W) as excitation source of 75 W Xenon lamp, and a photo multiplier tube R955 (Hamamatsu). The chromaticity coordinates and the luminance of the samples were taken by using a Konica Minolta CS-2000 luminometer. For the measurements of phosphorescence, the (Eu,Dy)-doped strontium aluminate/aluminosilicate powders were irradiated during 5 minutes with a 365 nm UV lamp; then, the excitation was stopped and the phosphorescent signal as well as the luminance was measured. The reflectance spectra of the powder samples were measured by utilizing Cary-5000 spectrophotometer coupled integrating sphere in the range of 200 nm–700 nm. All optical measurements were made at room temperature.

3. Results and Discussion

3.1. Structure and Morphology

Figure 1 show the XRD patterns of the (Eu,Dy)-doped strontium aluminate/aluminosilicate powders annealed in the range of 1000°C–1300°C. The samples annealed at 1150°C, 1200°C, and 1300°C presented three crystalline phases: firstly, the SrAl₂O₄ hexagonal phase (JCPDS 311336), second the Sr₃Al₃₂O₅₁ hexagonal phase (JCPDS 440024), and lastly the NaSiAlO₄ orthorhombic phase (JCPDS 390376). The sample annealed at 1000°C had a fourth phase SiO₂, and it is labeled with the symbol . The SrAl₂O₄ and Sr₃Al₃₂O₅₁ standard patterns are plotted at the bottom of Figure 1 in black and gray vertical lines and the NaSiAlO₄ phase is marked with the θ symbol on the XRD patterns in all the samples. Furthermore, the intensity of the diffraction peaks of the NaSiAlO₄ phase is higher for the samples annealed at 1150°C and 1200°C in comparison with the samples annealed at 1000°C and 1300°C. This suggests that the amount of the NaSiAlO₄ is lower in the samples annealed at 1150°C and 1200°C.

The morphology of the calcined samples is illustrated in Figures 2(a)–2(d). The sample annealed at 1000°C shows clusters of coalesced grains in the range of 1–5 μm. Also, it can be observed that these irregular grains are porous, which can be beneficial for the adsorption of MB molecules on the surface of the powders. The samples annealed at 1150°C, 1200°C, and 1300°C also show irregular grains (see Figures 2(b)–2(d)) and the degree of coalescence among grains increased as the temperature increases. A zoom of the samples annealed at 1150°C and 1300°C samples is shown in Figures 2(e) and 2(f), respectively. The sample annealed at 1150°C (see Figure 2(e)) shows a morphology composed of bars (0.3–0.8 μm of average length), hexagons (0.2–0.5 μm of average diameter), and irregular grains (0.1–0.5 μm of average size) and those ones are coalesced together to form bigger micrograins. In addition, the sample annealed at 1300°C consisted only in overlapped microhexagons with sizes in the range of 0.1–1.4 μm. Table 1 summarizes the morphologies found for each sample in this work.

(a)

(b)

(c)

(d)

(e)

(f)

3.2. Optical Properties

Figure 3 shows the diffuse reflectance spectra of samples with different annealing temperatures from 1000°C to 1300°C. The spectra show that the samples are highly reflective for wavelengths above 456 nm and they have a huge absorption band in the range of 225 nm–456 nm. The sample annealed at 1000°C showed the highest absorption of light in the visible range. The reflectance spectra show two main absorption bands: the first one is centered at 270 nm and it is attributed to the absorption of Eu²⁺ ions [8, 9]; the second absorption band located at 385 nm is attributed to 5d → 4f allowed transition of Eu²⁺ [14]. The band-gap values of the samples were estimated by using the Kubelka-Munk function methodology [15, 16]. Figure 4 shows the Kubelka-Munk function for each sample; the values of band gap were obtained by intercepting the extrapolated linear part of the curves with the -axis of the plot (K-M)^1/2 versus energy (eV). After this, the values of band-gaps obtained were in the range of 5.5–5.8 eV. Those high values suggest that our material behaves as an insulator.

Figure 5(a) depicts the excitation spectra of the samples annealed at different temperatures that were obtained by monitoring the emission at 455 nm. Those excitation spectra are broad bands centered at 363 nm and they are composed of three peaks at 270 nm, 355 nm, and 372 nm. The excitation peaks at 372 nm and 355 nm are related to Eu²⁺ excitation [9, 17] while the shoulder observed at 270 nm is associated with the well-known Eu-O charge transfer band [18]. Figure 5(b) shows the emission spectra of the samples annealed in the range of 1000°C–1300°C; it shows for all the samples an asymmetrical emission band centered at nm which is attributed to the allowed transitions of the Eu²⁺ [3, 9, 19, 20]. This figure also shows on the left side images of the samples under UV and we can appreciate how the phosphorescent intensity increases as the temperature increases; however, the intensity decreased after we annealed the samples at 1300°C. This decrease of luminescence as a function of the temperature increase has been observed in SrAl₂O₄:Eu²⁺,Dy³⁺ and it is attributed to higher degree of coalescence of particles, which, in turn, decreases the surface where the photoluminescence process can occur [21]. The asymmetrical band profiles shown in Figure 5(b) are related to the simultaneous presence of the SrAl₂O₄ and Sr₃Al₃₂O₅₁ phases as observed in the XRD patterns. In both phases, the Eu²⁺ ions should be substituting the Sr²⁺ ions and, therefore, we observed a combined emission of SrAl₂O₄:Eu²⁺/Sr₃Al₃₂O₅₁:Eu²⁺ which produced a broad blue-green emission band centered at 455 nm. If we have only SrAl₂O₄:Eu²⁺ or Sr₃Al₃₂O₅₁:Eu²⁺, we should observe a sharp emission band of Eu²⁺ centered at 516 nm (SrAl₂O₄:Eu²⁺) or at 450 nm (Sr₃Al₃₂O₅₁:Eu²⁺) [3, 19, 20] but those single emissions were not observed in our case. Moreover, the NaSiAlO₄ phase does not contribute to the overall emission since it did not show yellow-orange emissions in the visible region under UV irradiation [22]. Further, it is worth noting that no emission of Eu³⁺ was observed, which suggests that our process of reduction is good enough to dope with only Eu²⁺.

(a)

(b)

Figure 6 shows the phosphorescence decay curves of the samples annealed at different temperatures. Those ones were measured immediately after we stopped the excitation with UV light at 365 nm (we were exciting the samples during 5 minutes). As expected, the phosphorescence intensity of the sample annealed at 1200°C was the highest and it decreased by three orders of magnitude after 65 minutes, while the rest of samples decreased their intensity by three orders of magnitude after only 10 minutes. This trend can be related to the fact that we have bars and hexagons at the same time in the sample annealed at 1200°C, since the other samples had grains or only hexagons and their intensity was lower. This means that bars can favor the phosphorescence but irregular grains can be detrimental for it. Furthermore, the mixture of morphologies can create intrinsic defects which enhances the phosphorescence intensity as reported in literature [23, 24]. We measured the luminance and CIE coordinates of our samples and the results are presented in Table 1; the sample annealed at 1200°C had the highest luminance (40 Cd/m²) and its CIE coordinates were (0.1589, 0.1972); this last coordinate indicates that the color of phosphorescence is located in the blue-green region. Finally, the CIE coordinates of the rest of samples were similar even though the annealing temperature increased from 1000°C to 1300°C (see Table 1).

3.3. Photocatalytic Activity of Powders

Photocatalysis experiments were achieved by monitoring the percentage degradation of methylene blue (MB) in aqueous solution. Typically, the MB shows an absorbance band () at 665 nm and we measured the absorbance intensity of this peak as a function of time, since a decrease of intensity of this band indicates a decrement of the MB concentration (). The following equation was used in order to calculate the MB degradation (%) as function of the time [25, 26]:where and are the absorbance intensity values of the dye solution before and after irradiation, respectively. Figure 7(a) shows the percentage degradation of MB as a function of time. The degradation percentages of MB for the samples annealed at 1000°C, 1150°C, 1200°C, and 1300°C after 360 min of UV excitation were 32%, 20%, 15%, and 38.5%, respectively. Thus, the samples annealed at 1000°C and 1300°C presented the highest percentage degradation and the lowest luminescent intensities. In contrast, the samples with the highest luminescent intensity (1150°C and 1200°C) exhibited the lowest photocatalytic activity. The decrease in the photocatalytic activity has been observed in other luminescent systems [25, 27] and this is due to the fact that the samples with lower luminescence generate more free-carriers (electron or holes) during the phosphorescence process compared with the samples with higher luminescence which use most of the electron/hole pairs to generate light emission. In consequence, as the availability of free-carriers is better, the photocatalytic activity is enhanced [28, 29]. Figure 7(b) shows the percentage degradation of the samples exposed to solar irradiation as a function of time. It is observed that the samples annealed at 1000°C, 1150°C, and 1200°C degraded 100% the MB dye after 300 min; this means an increase of 68%, 80%, and 85% of the MB degradation compared with the results obtained under UV light. The sample calcined at 1300°C degrades only ~88% of methylene blue in water solution after 360 min (see Figure 7(b)). This lower degradation percentage is related to the fact that higher annealing temperature promotes the coalescence of grains, which, in turn, reduces the surface area and this reduces the amount of methylene blue molecules adsorbed on the powders. This can be corroborated from SEM images, since we find bigger pieces of coalesced material in the samples annealed at 1300°C in comparison with the rest of samples (see Figures 2(a)–2(d)).

(a)

(b)

Based on the results mentioned above, we consider that our phosphors have modest photocatalysis activity (under UV light) compared to conventional TiO₂ nanoparticles [26, 28]. However, an advantage of our (Eu,Dy)-doped strontium aluminates/aluminosilicates as photocatalyst is the fact that they can be separated easily from water by using simple precipitation, which is more difficult for conventional TiO₂ nanoparticles. The best performance of our phosphors is presented under solar irradiation; this suggests that they can be used as photocatalysts in water treatment plans. We are currently working to obtain only one single phase, that is, only strontium aluminate or aluminosilicates in order to obtain the photocatalytic performance of each phase separately. Those results will be published in a subsequent article.

4. Conclusions

Strontium aluminate/aluminosilicate phosphorescent phosphors based on the mixture of SrAl₂O₄:Eu²⁺,Dy³⁺, Sr₃Al₃₂O₅₁:Eu²⁺,Dy³⁺, and NaSiAlO₄ were successfully fabricated by combustion synthesis and postannealed. The blue-green phosphorescence emission at 455 nm is ascribed to the 4f-5d allowed transition of the Eu²⁺. The sample with the longest phosphorescence was that annealed at 1200°C and it had a luminance of 40 Cd/m². The photocatalyst experiments with our samples demonstrated that these samples annealed at 1000°C and 1300°C showed the lowest luminescence intensity but the highest percentage degradation of MB under UV excitation at 365 nm (32% and 38.5%, resp.). When solar irradiation was used for the photocatalysis experiments, total degradation of MB was observed by using the samples annealed at 1000°C, 1150°C, and 1200°C after 300 minutes. Also those powders were separated easily from water by simple precipitation. Hence, the results suggest that our strontium aluminate/aluminosilicate phosphorescent blue phosphor powders can be useful for water cleaning systems.

Competing Interests

The authors declare that they have no competing interests.

Acknowledgments

The authors appreciate the excellent technical work performed by R. Valdivia, C. Albor, and M. Olmos. C. R. García thanks CONACYT-México for national postdoctoral fellowship, PRODEP-SEP 2015 project, and FONCYT-COECYT 2016 project. One of the author thanks Drs. R. Narro, C. Méndez, and K. Linganna for their helpful comments and discussions.

References

K. van den Eeckhout, D. Poelman, and P. F. Smet, “Persistent luminescence in non-Eu²⁺-doped compounds: a review,” Materials, vol. 6, no. 7, pp. 2789–2818, 2013.
View at: Publisher Site | Google Scholar
T. Matsuzawa, Y. Aoki, N. Takeuchi, and Y. Murayama, “A new long phosphorescent phosphor with high brightness, SrAl₂O₄:Eu²⁺, Dy³⁺,” Journal of the Electrochemical Society, vol. 143, no. 8, pp. 2670–2673, 1996.
View at: Publisher Site | Google Scholar
N. M. Son, L. T. T. Vien, L. V. K. Bao, and N. N. Trac, “Synthesis of SrAl₂O₄: Eu²⁺ Dy³⁺ phosphorescence nanosized powder by combustion method and its optical properties,” Journal of Physics: Conference Series, vol. 187, article 012017, 2009.
View at: Publisher Site | Google Scholar
K. Van den Eeckhout, P. F. Smet, and D. Poelman, “Persistent luminescence in Eu²⁺-doped compounds: a review,” Materials, vol. 3, no. 4, pp. 2536–2566, 2010.
View at: Publisher Site | Google Scholar
J. B. Zhong, D. Ma, X. Y. He, J. Z. Li, and Y. Q. Chen, “Sol-gel preparation and photocatalytic performance of TiO₂/SrAl₂O₄: Eu²⁺, Dy³⁺ toward the oxidation of gaseous benzene,” Journal of Sol-Gel Science and Technology, vol. 52, no. 1, pp. 140–145, 2009.
View at: Publisher Site | Google Scholar
H. Li, S. Yin, Y. Wang, and T. Sato, “Persistent luminescence assisted photocatalytic properties of CaAl₂O₄:(Eu,Nd)/TiO_{2 − x}N_y and Sr₄Al₁₄O₂₅:(Eu,Dy)/TiO_{2 − x}N_y,” Journal of Molecular Catalysis A: Chemical, vol. 363-364, pp. 129–133, 2012.
View at: Publisher Site | Google Scholar
H. Li, S. Yin, Y. Wang, T. Sekino, S. W. Lee, and T. Sato, “Green phosphorescence-assisted degradation of rhodamine B dyes by Ag₃PO₄,” Journal of Materials Chemistry A, vol. 1, no. 4, pp. 1123–1126, 2013.
View at: Publisher Site | Google Scholar
T. Peng, L. Huajun, H. Yang, and C. Yan, “Synthesis of SrAl₂O₄:Eu, Dy phosphor nanometer powders by sol-gel processes and its optical properties,” Materials Chemistry and Physics, vol. 85, no. 1, pp. 68–72, 2004.
View at: Publisher Site | Google Scholar
F. Clabau, X. Rocquefelte, S. Jobic et al., “Mechanism of phosphorescence appropriate for the long-lasting phosphors Eu²⁺-doped SrAl₂O₄ with codopants Dy³⁺ and B³⁺,” Chemistry of Materials, vol. 17, no. 15, pp. 3904–3912, 2005.
View at: Publisher Site | Google Scholar
A. L. Linsebigler, G. Lu, and J. T. Yates Jr., “Photocatalysis on TiO₂ surfaces: principles, mechanisms, and selected results,” Chemical Reviews, vol. 95, no. 3, pp. 735–758, 1995.
View at: Publisher Site | Google Scholar
G. Federici, B. J. Shaw, and R. D. Handy, “Toxicity of titanium dioxide nanoparticles to rainbow trout (Oncorhynchus mykiss): gill injury, oxidative stress, and other physiological effects,” Aquatic Toxicology, vol. 84, no. 4, pp. 415–430, 2007.
View at: Publisher Site | Google Scholar
X. Zhu, Y. Chang, and Y. Chen, “Toxicity and bioaccumulation of TiO₂ nanoparticle aggregates in Daphnia magna,” Chemosphere, vol. 78, no. 3, pp. 209–215, 2010.
View at: Publisher Site | Google Scholar
W.-W. Yang, Y. Wang, B. Huang et al., “TiO₂ nanoparticles act as a carrier of Cd bioaccumulation in the ciliate Tetrahymena thermophila,” Environmental Science & Technology, vol. 48, no. 13, pp. 7568–7575, 2014.
View at: Publisher Site | Google Scholar
T. W. Kim and H. L. Park, “Observation of two valence states of Eu in a SrS_xO_1−x:Eu_y phosphor,” Solid State Communications, vol. 85, no. 7, pp. 635–637, 1993.
View at: Publisher Site | Google Scholar
J. Tauc, “Optical properties and electronic structure of amorphous Ge and Si,” Materials Research Bulletin, vol. 3, no. 1, pp. 37–46, 1968.
View at: Publisher Site | Google Scholar
A. Escobedo Morales, E. Sanchez Mora, and U. Pal, “Use of diffuse reflectance spectroscopy for optical characterization of un-supported nanostructures,” Revista Mexicana de Física, vol. 53, pp. 18–22, 2007.
View at: Google Scholar
X. Luo, W. Cao, and F. Sun, “The development of silicate matrix phosphors with broad excitation band for phosphor-convered white LED,” Chinese Science Bulletin, vol. 53, no. 19, pp. 2923–2930, 2008.
View at: Publisher Site | Google Scholar
G. Blasse and B. C. Grabmaier, Luminescent Materials, vol. 2, Springer, Berlin, Germany, 1994.
View at: Publisher Site
Y.-F. Xu, D.-K. Ma, M.-L. Guan, X.-A. Chen, Q.-Q. Pan, and S.-M. Huang, “Controlled synthesis of single-crystal SrAl₂O₄:Eu²⁺,Dy³⁺ nanosheets with long-lasting phosphorescence,” Journal of Alloys and Compounds, vol. 502, no. 1, pp. 38–42, 2010.
View at: Publisher Site | Google Scholar
M. A. Kale, C. P. Joshi, and S. V. Moharil, “Preparation and photoluminescence study of Eu²⁺ doped SrAl₄O₇ and Sr₃Al₃₂O₅₁,” International Journal of Chemical and Physical Sciences, vol. 1, no. 2, pp. 35–39, 2012.
View at: Google Scholar
M. Gaft, W. Strek, L. Nagli, G. Panczer, G. R. Rossman, and L. Marciniak, “Laser-induced time-resolved luminescence of natural sillimanite Al₂SiO₅ and synthetic Al₂SiO₅ activated by chromium,” Journal of Luminescence, vol. 132, no. 11, pp. 2855–2862, 2012.
View at: Publisher Site | Google Scholar
S. Deng, Z. Xue, Q. Yang et al., “Surface modification of MAl₂O₄:Eu²⁺,Dy³⁺ (M = Sr, Ca, Ba) phosphors to enhance water resistance by combustion method,” Applied Surface Science, vol. 282, pp. 315–319, 2013.
View at: Publisher Site | Google Scholar
T. Laamanen, Defects in persistent luminescence materials [Ph.D. thesis], Universidad of Turku, Graduate School of Materials Research, Turku, Finland, 2011, S. Ser and A. I. Osa.
H. Ryu and K. S. Bartwal, “Defect structure and its relevance to photoluminescence in SrAl₂O₄:Eu²⁺, Nd³⁺,” Physica B: Condensed Matter, vol. 404, no. 12-13, pp. 1714–1718, 2009.
View at: Publisher Site | Google Scholar
R. Borja-Urby, L. A. Díaz-Torres, P. Salas, E. Moctezuma, M. Vega, and C. Ángeles-Chávez, “Structural study, photoluminescence, and photocatalytic activity of semiconducting BaZrO₃:Bi nanocrystals,” Materials Science and Engineering: B, vol. 176, no. 17, pp. 1382–1387, 2011.
View at: Publisher Site | Google Scholar
A. Houas, H. Lachheb, M. Ksibi, E. Elaloui, C. Guillard, and J.-M. Herrmann, “Photocatalytic degradation pathway of methylene blue in water,” Applied Catalysis B: Environmental, vol. 31, no. 2, pp. 145–157, 2001.
View at: Publisher Site | Google Scholar
D. Wojcieszak, D. Kaczmarek, J. Domaradzki, and M. Mazur, “Correlation of photocatalysis and photoluminescence effect in relation to the surface properties of TiO₂:Tb thin films,” International Journal of Photoenergy, vol. 2013, Article ID 526140, 9 pages, 2013.
View at: Publisher Site | Google Scholar
S.-Y. Kim, T.-H. Lim, T.-S. Chang, and C.-H. Shin, “Photocatalysis of methylene blue on titanium dioxide nanoparticles synthesized by modified sol-hydrothermal process of TiCl₄,” Catalysis Letters, vol. 117, no. 3-4, pp. 112–118, 2007.
View at: Publisher Site | Google Scholar
C. R. García, L. A. Diaz-Torres, P. Salas, M. Guzman, and C. Angeles-Chavez, “Photoluminescent and photocatalytic properties of bismuth doped strontium aluminates blended with titanium dioxide,” Materials Science in Semiconductor Processing, vol. 37, pp. 105–111, 2015.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2016 C. R. García et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1425

Downloads

954

Citations