Antibacterial Activity of Ag-Doped TiO<sub>2</sub> and Ag-Doped ZnO Nanoparticles

Nigussie, Gebretinsae Yeabyo; Tesfamariam, Gebrekidan Mebrahtu; Tegegne, Berhanu Menasbo; Weldemichel, Yemane Araya; Gebreab, Tesfakiros Woldu; Gebrehiwot, Desta Gebremedhin; Gebremichel, Gebru Equar

doi:https://doi.org/10.1155/2018/5927485

International Journal of Photoenergy

On this page

Abstract Introduction Experimental Results and Discussion Conclusion Conflicts of Interest Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2018 | Article ID 5927485 | https://doi.org/10.1155/2018/5927485

Antibacterial Activity of Ag-Doped TiO₂ and Ag-Doped ZnO Nanoparticles

Gebretinsae Yeabyo Nigussie,¹Gebrekidan Mebrahtu Tesfamariam,¹Berhanu Menasbo Tegegne,¹Yemane Araya Weldemichel,¹Tesfakiros Woldu Gebreab,²Desta Gebremedhin Gebrehiwot,¹and Gebru Equar Gebremichel³

Academic Editor: P. Davide Cozzoli

Received21 Dec 2017

Revised26 Feb 2018

Accepted13 Mar 2018

Published02 May 2018

Abstract

We report in this paper antibacterial activity of Ag-doped TiO₂ and Ag-doped ZnO nanoparticles (NPs) under visible light irradiation synthesized by using a sol-gel method. Structural, morphological, and basic optical properties of these samples were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDX) spectrum, and UV-Vis reflectance. Room temperature X-ray diffraction analysis revealed that Ag-doped TiO₂ has both rutile and anatase phases, but TiO₂ NPs only have the anatase phase. In both ZnO and Ag-doped ZnO NPs, the hexagonal wurtzite structure was observed. The morphologies of TiO₂ and ZnO were influenced by doping with Ag, as shown from the SEM images. EDX confirms that the samples are composed of Zn, Ti, Ag, and O elements. UV-Vis reflectance results show decreased band gap energy of Ag-doped TiO₂ and Ag-doped ZnO NPs in comparison to that of TiO₂ and ZnO. Pathogenic bacteria, such as Staphylococcus aureus, Pseudomonas aeruginosa, and Escherichia coli, were used to assess the antibacterial activity of the synthesized materials. The reduction in the viability of all the three bacteria to zero using Ag-doped ZnO occurred at 60 μg/mL of culture, while Ag-doped TiO₂ showed zero viability at 80 μg/mL. Doping of Ag on ZnO and TiO₂ plays a vital role in the increased antibacterial activity performance.

1. Introduction

Currently, nanosized materials are the most advanced type of materials, both in scientific knowledge and in commercial applications. Inorganic nanoparticles (NPs), such as silver, copper, titanium, and zinc, are the most interesting NPs due to their applications and positive impact on pathogenic microorganisms [1–4]. NPs have been studied for many years because of their size-dependent physical and chemical properties. Among NPs, great attention has been shifted to nanooxides [5–7]. NPs have attracted great interest due to their special or specific properties and selectivity, especially in pharmaceutical and biological applications [8]. In laboratory tests with NPs, different microorganisms have been eliminated within minutes of contact with the NPs [9–12]. The application of NPs on bacteria is very important since NPs have a tendency to be in the lowest level and directly enter the food chain of the ecosystem [13, 14].

Recently, special attention has been given to TiO₂ and ZnO NPs due to their unique optical, electrical, and chemical properties. TiO₂ is a tremendous photocatalyst, which is widely used for antibacterial activity due to its high photosensitivity, high efficiency, nontoxic nature, strong oxidizing power, relative cheapness, and chemical stability [15]. ZnO is also a promising photocatalyst and plays a pivotal role in antibacterial activity. In line with this, it is low cost, biocompatible, highly catalytic, and environmental friendly [16, 17].

In order to enhance the photocatalytic activity, intensive interdisciplinary researches have been made on TiO₂ [18–20] and ZnO [21–24]. It is known that photocatalytic activity of NPs depends upon their crystalline structure [19], doping [25], surface area [26], and hydroxyl group [19]. Currently, different researchers are engaged in improving the efficiency of photocatalysts by using metal dopants like Ag which is the most effective due to its high stability and good electrical/thermal conductivity. Furthermore, Ag doping on the surface of metal oxides employed to enhance photocatalytic activity by preventing fast e⁻-h⁺ recombination processes [23, 24, 27, 28]; also, this mechanism could lead to the generation of good antibacterial properties. In this work, Ag-doped TiO₂ and Ag-doped ZnO were synthesized using the sol-gel method, and their antibacterial activity was carefully investigated and discussed.

2. Experimental

2.1. Materials and Methods

High-purity (AR grade) titanium tetrachloride (TiCl₄) (Merck, EtOH 99%), silver nitrate (AgNO₃), zinc nitrate (ZnNO₃), hydrochloric acid (HCl), deionized water (DI), and sodium hydroxide (NaOH) were used as precursors for the preparation of NPs and were acquired from Sigma-Aldrich.

2.2. Synthesis of Nanoparticles

TiO₂ NPs were synthesized using an acid-catalyzed sol-gel process, as described elsewhere [29]. First, 1 mL of TiCl₄ was slowly added dropwise to 10 mL EtOH (Merck, 99.8%) under vigorous stirring. A large amount of HCl gas was evolved, and a yellowish solution was formed. The gel was subjected to an oven, and it was dried at 100°C for 24 h. Finally, the white TiO₂ powder was obtained. To obtain nanocrystalline particles, TiO₂ was annealed at 450°C for 4 hours.

Ag-doped TiO₂ was synthesized using1 mL TiCl₄ (Merck, 99%) slowly added dropwise to 10 mL EtOH (Merck, 99.8%) under vigorous stirring. AgNO₃ was mixed gently with 0.5 mL deionized water (DI). After gelation, the NPs were left to dry at 100°C for 24 hours. In addition, the amorphous TiO₂ transformed to a crystalline structure using a furnace at 450°C for 4 hours.

First, 0.5 M ZnNO₃ was dissolved in ethanol, and the reaction mixture was kept under constant stirring for 1 hour until ZnNO₃ was completely dissolved. Similarly, in another reaction vessel, 0.5 M of NaOH was dissolved under constant stirring for 1 hour. Then, 0.5 M NaOH was added dropwise to the ZnNO₃ solution under vigorous stirring for 45 minutes. The reaction mixture was left for 2 hours after NaOH was completely added. Then, the solution was centrifuged for 10 minutes, the precipitate was dried in an oven at approximately 80°C, and Zn(OH)₂ was completely converted into ZnO.

Ag-doped ZnO nanopowder was synthesized using a 0.5 M concentration of AgNO₃, which was added to the zinc solution before the NaOH solution, and then, the Ag-doped ZnO NPs were obtained from the Ag(OH)₂ precipitate. The powder was calcined at a heating rate of 2°C/min in an air atmosphere for 4 hours at 450°C.

2.3. Characterizations of Ag-TiO₂ and Ag-ZnO Nanoparticles

The phase components of the powder were analyzed using PANalytical X’pert PRO with monochromatic Cu Kα radiation, and the samples were scanned over a range of 20–80°. SEM (JEOL JSM-5610 analysis station SEM) was utilized to examine the shape and cross-sectional morphology. The energy dispersive X-ray (EDX) spectrum was recorded with JEOL JSM-5610 SEM equipped with EDX. The UV-Vis diffuse reflectance spectra were measured using a PerkinElmer Lambda 35 spectrometer which was operated at a wavelength range of 200–800 nm.

2.4. Bacterial Strain and Culture Situations

In this trial, three different characteristic bacterial pathogens were nominated: Staphylococcus aureus (S. aureus, ATCC29737/NCIM-2901), Pseudomonas aeruginosa (P. aeruginosa, PA220), and Escherichia coli (E. coli, ATCC 25922). These were grown in 61748 LB Broth (Luria Bertani Broth) medium in a humidified incubator at 37°C with constant agitation overnight. The microorganisms were cultured on a nutrient agar plate for 24 hours and grown aerobically at 37°C.

2.4.1. Antibacterial Activity of Ag-TiO₂ and Ag-ZnO Nanoparticles

(1) Bacterial Cell Growth and Viability Resting. The bacterial growth rate was observed in the presence of Ag-TiO₂ and Ag-ZnO NPs, on the bacteria. S. aureus, P. aeruginosa, and E. coli cultures were gathered in the midexponential growth phase, and the cells were collected using centrifugation at 3000 rpm for 10 min. Directly, the bacterial pellet was washed three times with saline water to clean the pellet of medium constituents. Then, 10 μL of the cell suspensions was mixed with seven different concentrations of Ag-TiO₂ and Ag-ZnO NPs (0 μg/mL, 10 μg/mL, 20 μg/mL, 40 μg/mL, 60 μg/mL, 80 μg/mL, and 100 μg/mL) and incubated at 37°C for 2 h with slight shaking. The mixture was then transferred to 5 mL tubes containing 2 mL MH medium, and the tubes were incubated on a rotary shaker at 180 rpm and 37°C. The antibacterial activity was tested by using 107 CFU/mL and then incubated with concentrations of Ag-TiO₂ and Ag-ZnO for 4 h. Next, 20 μL of a successive 106-fold dilution of each bacterial suspension in sterile deionized water was spread onto agar plates to grow for 24 h at 37°C.

3. Results and Discussion

3.1. Material Characterization

3.1.1. X-Ray Diffraction

The XRD pattern of pure TiO₂ and Ag-doped TiO₂ samples is shown in Figure 1. It reveals that the unmodified TiO₂ contains only the anatase phase, and its diffraction peaks are well matching with those of the standard anatase phase of TiO₂ Joint Committee on Powder Diffraction Standard (JCPDS card number 01-071-1167), while Ag-doped TiO₂ exhibited both the anatase and rutile phases (JCPDS card number 4-783). In Figure 1(a, b), the (101) diffraction peak appeared to be attributed to both TiO₂ and Ag-doped TiO₂. Xu et al. [30] reported that a mixture of anatase and rutile phases of Ag-doped TiO₂ possesses greater photocatalytic activity than the pure anatase phase of TiO₂ under UV light. This is evidenced by the presence of Ag in the diffractogram of the Ag-doped samples with the relative intensity of the stronger Ag peaks, (111) at 2θ of 42.500° and (200) at 2θ of 48.500°. Furthermore, this result agrees with that of other reports [31], in which calcination is used to increase the crystallinity of TiO₂ by decreasing the e⁻-h⁺ pair recombination and enhance the photocatalytic activity as well.

Figure 2(a, b) represents the XRD pattern of pure and Ag-doped ZnO collected over a 2θ range of 20°–80° using Cu Kα radiation.

The XRD pattern of the ZnO NP (Figure 2) shows its characteristic peaks with a hexagonal wurtzite structure. The broadening of the graph illustrates the nanometer range of the particle. Our data is in agreement with that of JCPDS card number 36-1451 [1]. The strongest peaks observed at 2θ values of 31.791°, 34.421°, 36.252°, 47.511°, 56.602°, 62.862°, 67.961°, and 69.000° correspond to the lattice planes (100), (002), (101), (110), (103), (112), (201), and (200), respectively. The XRD pattern of Ag-doped ZnO NPs (Figure 2(b)) shows the characteristic peak of Ag at 2θ of 38.110°, 44.270°, and 64.420° (JCPDS card number 04-0783). No shift was observed for ZnO peaks, confirming the surface doping or segregation of Ag nanoclusters on the grain boundaries of ZnO NPs [32].

3.1.2. SEM Analysis

The morphologies of the samples were observed by SEM. Figures 3(a)–3(d) show the morphologies of the samples and Ag distribution in the as-synthesized samples. It can be seen that the surface of Ag in Figures 3(b) and 3(d) is smooth. The nanostructure of the sample as revealed by SEM shows a significant difference in the undoped and doped states. Large elongated grains together with a granular structure show evidence of mixed phases which is in accordance with the XRD results of the corresponding gel powder (Figure 2). These results are in accordance with the values found in the literature [33]. Furthermore, the compositions of the samples were determined with energy dispersive X-ray spectroscopy (EDX) (Figure 4(a, b)). All of the peaks on the curves are recognized to be of Zn, Ag, Ti, O, Cu, C, and Na elements, and no peaks of other elements are observed. The Cu, C, and Na signals might be from the precursors and sample holders. Therefore, it is concluded that the as-synthesized samples are composed of Zn, Ti, Ag, and O elements, which is in good agreement with the above XRD result.

(a)

(b)

(c)

(d)

(a)

(b)

3.1.3. Optical Properties

As shown in Figure 4, Ag-TiO₂ and Ag-ZnO exhibited atypical absorption characteristics due to a band gap change in the range 400–550 nm in the visible region caused by the surface plasmon band characteristics of silver; it was further confirmed that Ag was effectively deposited on the surface of TiO₂ and ZnO [34]. The shift in absorption spectra provides some evidence of the interaction between Ag and TiO₂ or ZnO, which is also in agreement with the XRD patterns.

3.2. Antibacterial Activity of the Nanoparticles

The antibacterial activities of Ag-TiO₂ and Ag-ZnO were examined against gram-positive S. aureus and gram-negative P. aeruginosa and E.coli bacteria, as shown in Figure 5. The Ag-TiO₂ and Ag-ZnO NPs at concentrations of 60 μg/mL of culture were toxic to the three different bacteria tested Figure 5. However, 40 μg/mL concentrations of Ag-ZnO NPs eliminated 100% P. aeruginosa cells, whereas 15% and 12% viabilities of S. aureus and E. coli were obtained, respectively. In Ag-doped NPs at 60 μg/mL of culture, 0% viability in the case of P. aeruginosa and S. aureus was observed, while in E. coli, viabilities were observed. Therefore, here it was determined that 60 μg/mL Ag-doped NP concentration of bacterial culture (0.2 OD at 600 nm) is the optimal concentration for eliminating the bacteria.

(a)

(b)

(c)

When we compare the antibacterial activity of Ag-ZnO NPs to that of Ag-TiO₂ NPs, it was observed that Ag-ZnO NPs are highly efficient. A significant antibacterial activity was observed on gram-negative bacteria in both doped NPs. It may be that gram-positive bacteria have a stronger molecular network in the cell wall than gram-negative bacteria and silver ions may enter the cell walls of gram-positive bacteria [29]. The percent viability of bacteria was exponentially reduced as the concentration of Ag doping increased in the TiO₂ and ZnO matrix. The observed results of this study, along with those of a previous study [35], demonstrate that doping with metal or metal oxide on the surface of TiO₂ and ZnO NPs increases the e⁻-h⁺ charge separation by reducing the band gap energy and leads to a delay in the recombination and an increase in the antibacterial activity Figure 6.

4. Conclusion

In summary, Ag-TiO₂ and Ag-ZnO were prepared via the sol-gel method. The synthesized NPs were characterized using XRD, SEM, EDX, and UV-Vis. This study may provide new insights into the design and preparation of nanomaterials and the enhancement of antibacterial activity. In comparison to other materials, the antibacterial results were more favorable for assays conducted with the same species. Moreover, the low antibacterial activities of pure TiO₂ and ZnO were significantly improved by the incorporation of silver. The synthesized Ag-TiO₂ and Ag-ZnO NPs with high thermal stability and strong antibacterial activity are expected to serve in applications in the pharmaceutical and nanocomposite fields. Our work provided a possible way to develop nanomaterials with very attractive properties to be applied in antibacterial activities.

Conflicts of Interest

In this, the authors wish to confirm that there are no conflicts of interest associated with this publication.

Acknowledgments

The authors would like to acknowledge Mekelle University for their financial support from the recurrent budget (Grant no. CRPO/CNCS/016/08). They are also grateful to Osmania University, India, and TIGP-SCST for their provision of XRD and SEM analyses.

References

S. Prabhu and E. K. Poulose, “Silver nanoparticles: mechanism of antimicrobial action, synthesis, medical applications, and toxicity effects,” International Nano Letters, vol. 2, no. 1, p. 32, 2012.
View at: Publisher Site | Google Scholar
X. Wan, T. Wang, Y. Dong, and D. He, “Development and application of TiO₂ nanoparticles coupled with silver halide,” Journal of Nanomaterials, vol. 2014, Article ID 908785, 5 pages, 2014.
View at: Publisher Site | Google Scholar
S. Chen, Y. Guo, S. Chen, Z. Ge, H. Yang, and J. Tang, “Fabrication of Cu/TiO₂ nanocomposite: toward an enhanced antibacterial performance in the absence of light,” Materials Letters, vol. 83, pp. 154–157, 2012.
View at: Publisher Site | Google Scholar
V. Mohammad, A. Umar, and Y. B. Hahn, “ZnO nanoparticles: growth, properties, and applications,” Metal Oxide Nanostructures and their Applications, American Scientific Publishers, New York, NY, USA, 2010.
View at: Google Scholar
C. B. Murray, C. R. Kagan, and M. G. Bawendi, “Synthesis and characterization of monodisperse nanocrystals and close-packed nanocrystal assemblies,” Annual Review of Materials Research, vol. 30, no. 1, pp. 545–610, 2000.
View at: Publisher Site | Google Scholar
L. Cermenati, D. Dondi, M. Fagnoni, and A. Albini, “Titanium dioxide photocatalysis of adamantane,” Tetrahedron, vol. 59, no. 34, pp. 6409–6414, 2003.
View at: Publisher Site | Google Scholar
R. Kumar, D. Rana, A. Umar, P. Sharma, S. Chauhan, and M. S. Chauhan, “Ag-doped ZnO nanoellipsoids: potential scaffold for photocatalytic and sensing applications,” Talanta, vol. 137, pp. 204–213, 2015.
View at: Publisher Site | Google Scholar
P. Li, J. Li, C. Wu, Q. Wu, and J. Li, “Synergistic antibacterial effects of β-lactam antibiotic combined with silver nanoparticles,” Nanotechnology, vol. 16, no. 9, pp. 1912–1917, 2005.
View at: Publisher Site | Google Scholar
T. Sungkaworn, W. Triampo, P. Nalakarn et al., “The effects of TiO₂ nanoparticles on tumor cell colonies: fractal dimension and morphological properties,” International Journal of Biomedical Science, vol. 2, no. 1, pp. 67–74, 2007.
View at: Google Scholar
G. Nagaraju, Udayabhanu, Shivaraj et al., “Electrochemical heavy metal detection, photocatalytic, photoluminescence, biodiesel production and antibacterial activities of Ag–ZnO nanomaterial,” Materials Research Bulletin, vol. 94, pp. 54–63, 2017.
View at: Publisher Site | Google Scholar
Y. Xiang, J. Li, X. Liu et al., “Construction of poly(lactic-co-glycolic acid)/ZnO nanorods/Ag nanoparticles hybrid coating on Ti implants for enhanced antibacterial activity and biocompatibility,” Materials Science and Engineering: C, vol. 79, pp. 629–637, 2017.
View at: Publisher Site | Google Scholar
S. M. Lam, J. A. Quek, and J. C. Sin, “Mechanistic investigation of visible light responsive Ag/ZnO micro/nanoflowers for enhanced photocatalytic performance and antibacterial activity,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 353, pp. 171–184, 2018.
View at: Publisher Site | Google Scholar
J. D. Fortner, D. Y. Lyon, C. M. Sayes et al., “C₆₀ in water: nanocrystal formation and microbial response,” Environmental Science & Technology, vol. 39, no. 11, pp. 4307–4316, 2005.
View at: Publisher Site | Google Scholar
M. Herrera, P. Carrión, P. Baca, J. Liébana, and A. Castillo, “In vitro antibacterial activity of glass-ionomer cements,” Microbios, vol. 104, no. 409, pp. 141–148, 2001.
View at: Google Scholar
A. Kösemen, Z. Alpaslan Kösemen, B. Canimkubey et al., “Fe doped TiO₂ thin film as electron selective layer for inverted solar cells,” Solar Energy, vol. 132, pp. 511–517, 2016.
View at: Publisher Site | Google Scholar
H. Morkoç and Ü. Özgür, Zinc Oxide: Fundamentals, Materials and Device Technology, Wiley-VCH, Weinheim, Germany, 2009.
View at: Publisher Site
J. Jayabharathi, C. Karunakaran, V. Kalaiarasi, and P. Ramanathan, “Nano ZnO, Cu-doped ZnO, and Ag-doped ZnO assisted generation of light from imidazole,” Journal of Photochemistry and Photobiology A: Chemistry, vol. 295, pp. 1–10, 2014.
View at: Publisher Site | Google Scholar
L. Elsellami, F. Dappozze, A. Houas, and C. Guillard, “Effect of Ag⁺ reduction on the photocatalytic activity of Ag-doped TiO₂,” Superlattices and Microstructures, vol. 109, pp. 511–518, 2017.
View at: Publisher Site | Google Scholar
S. Krejčíková, L. Matějová, K. Kočí et al., “Preparation and characterization of Ag-doped crystalline titania for photocatalysis applications,” Applied Catalysis B: Environmental, vol. 111-112, no. 112, pp. 119–125, 2012.
View at: Publisher Site | Google Scholar
K. Ubonchonlakate, L. Sikong, and F. Saito, “Photocatalytic disinfection of P.aeruginosa bacterial Ag-doped TiO2 film,” Procedia Engineering, vol. 32, pp. 656–662, 2012.
View at: Publisher Site | Google Scholar
Y. Zhang, X. Gao, L. Zhi et al., “The synergetic antibacterial activity of Ag islands on ZnO (Ag/ZnO) heterostructure nanoparticles and its mode of action,” Journal of Inorganic Biochemistry, vol. 130, pp. 74–83, 2014.
View at: Publisher Site | Google Scholar
Y. Al-Hadeethi, A. Umar, A. A. Ibrahim et al., “Synthesis, characterization and acetone gas sensing applications of Ag-doped ZnO nanoneedles,” Ceramics International, vol. 43, no. 9, pp. 6765–6770, 2017.
View at: Publisher Site | Google Scholar
O. Bechambi, M. Chalbi, W. Najjar, and S. Sayadi, “Photocatalytic activity of ZnO doped with Ag on the degradation of endocrine disrupting under UV irradiation and the investigation of its antibacterial activity,” Applied Surface Science, vol. 347, pp. 414–420, 2015.
View at: Publisher Site | Google Scholar
M. Elango, M. Deepa, R. Subramanian, and A. Mohamed Musthafa, “Synthesis, characterization of polyindole/Ag—ZnO nanocomposites and its antibacterial activity,” Journal of Alloys and Compounds, vol. 696, pp. 391–401, 2017.
View at: Publisher Site | Google Scholar
R. Kumar, J. Rashid, and M. A. Barakat, “Zero valent Ag deposited TiO₂ for the efficient photocatalysis of methylene blue under UV-C light irradiation,” Colloids and Interface Science Communications, vol. 5, pp. 1–4, 2015.
View at: Publisher Site | Google Scholar
S. Angkaew and P. Limsuwan, “Preparation of silver-titanium dioxide core-shell (Ag@TiO₂) nanoparticles: effect of Ti-Ag mole ratio,” Procedia Engineering, vol. 32, pp. 649–655, 2012.
View at: Publisher Site | Google Scholar
A. Hastir, N. Kohli, and R. C. Singh, “Ag doped ZnO nanowires as highly sensitive ethanol gas sensor,” Materials Today: Proceedings, vol. 4, no. 9, pp. 9476–9480, 2017.
View at: Publisher Site | Google Scholar
M. Jakob, H. Levanon, and P. V. Kamat, “Charge distribution between UV-irradiated TiO₂ and gold nanoparticles: determination of shift in the Fermi level,” Nano Letters, vol. 3, no. 3, pp. 353–358, 2003.
View at: Publisher Site | Google Scholar
K. Gupta, R. P. Singh, A. Pandey, and A. Pandey, “Photocatalytic antibacterial performance of TiO₂ and Ag-doped TiO₂ against S. aureus. P. aeruginosa and E. coli,” Beilstein Journal of Nanotechnology, vol. 4, pp. 345–351, 2013.
View at: Publisher Site | Google Scholar
H. Xu, H. Li, C. Wu, J. Chu, Y. Yan, and H. Shu, “Preparation, characterization and photocatalytic activity of transition metal-loaded BiVO₄,” Materials Science and Engineering: B, vol. 147, no. 1, pp. 52–56, 2008.
View at: Publisher Site | Google Scholar
X. You, F. Chen, and J. J. Zhang, “Effects of calcination on the physical and photocatalytic properties of TiO₂ powders prepared by sol–gel template method,” Journal of Sol-Gel Science and Technology, vol. 34, no. 2, pp. 181–187, 2005.
View at: Publisher Site | Google Scholar
N. Y. Jamil, S. A. Najim, A. M. Muhammed, and V. M. Rogoz, “Preparation, structural and optical characterization of ZnO/Ag thin film by CVD,” Proceedings of the International Conference Nanomaterials: Applications and Properties, vol. 3, no. 2, pp. 32–45, 2014.
View at: Google Scholar
B. Cheng, Y. Le, and J. Yu, “Preparation and enhanced photocatalytic activity of Ag@TiO₂ core–shell nanocomposite nanowires,” Journal of Hazardous Materials, vol. 177, no. 1–3, pp. 971–977, 2010.
View at: Publisher Site | Google Scholar
C. Chen, Y. Zheng, Y. Zhan, X. Lin, Q. Zheng, and K. Wei, “Enhanced Raman scattering and photocatalytic activity of Ag/ZnO heterojunction nanocrystals,” Dalton Transactions, vol. 40, no. 37, pp. 9566–9570, 2011.
View at: Publisher Site | Google Scholar
S. Banerjee, J. Gopal, P. Muraleedharan, A. K. Tyagi, and B. Raj, “Physics and chemistry of photocatalytic titanium dioxide: visualization of bactericidal activity using atomic force microscopy,” Current Science, vol. 90, no. 10, pp. 1378–1383, 2006.
View at: Google Scholar

Copyright

Copyright © 2018 Gebretinsae Yeabyo Nigussie et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

6985

Downloads

2523

Citations

International Journal of Photoenergy

Antibacterial Activity of Ag-Doped TiO2 and Ag-Doped ZnO Nanoparticles

Abstract

1. Introduction

2. Experimental

2.1. Materials and Methods

2.2. Synthesis of Nanoparticles

2.3. Characterizations of Ag-TiO2 and Ag-ZnO Nanoparticles

2.4. Bacterial Strain and Culture Situations

2.4.1. Antibacterial Activity of Ag-TiO2 and Ag-ZnO Nanoparticles

3. Results and Discussion

3.1. Material Characterization

3.1.1. X-Ray Diffraction

3.1.2. SEM Analysis

3.1.3. Optical Properties

3.2. Antibacterial Activity of the Nanoparticles

4. Conclusion

Conflicts of Interest

Acknowledgments

References

Copyright

Antibacterial Activity of Ag-Doped TiO₂ and Ag-Doped ZnO Nanoparticles

2.3. Characterizations of Ag-TiO₂ and Ag-ZnO Nanoparticles

2.4.1. Antibacterial Activity of Ag-TiO₂ and Ag-ZnO Nanoparticles